Active basic magnesium sulfate whisker modified polypropylene composite material and preparation method thereof
A magnesium sulfate whisker and composite material technology, which is applied in the field of active basic magnesium sulfate whisker modified polypropylene composite material and its preparation, can solve the problem that the strength, stiffness and heat resistance cannot meet the requirements of parts, limit polypropylene Application and development, poor impact performance of polypropylene, etc., to achieve the effect of improving the scope and depth of use, improving service life, and enhancing compatibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0051] Copolymerized polypropylene: 48 parts
[0052] Homopolypropylene: 40 parts
[0053] Toughener POE: 10 parts
[0054] Processing aid TAF: 0.7 parts
[0055] Processing aid CaSt 2 : 0.4 parts
[0056] Silane coupling agent KH550: 0.3 parts
[0057] Hydrochloric acid solution: 0.5 parts
[0058] Heat stabilizer 1010: 0.2 parts
[0059] Heat stabilizer 168: 0.2 parts
[0060] Basic magnesium sulfate whiskers: 10 parts
[0061] This embodiment adopts a twin-screw extruder with a length-to-diameter ratio of 35:1. Polypropylene, a toughening agent and a heat stabilizer are melted, mixed, and dispersed in the extruder, and then the active basic magnesium sulfate whisker The premix is fed from its side, plasticized at a temperature of 190-220°C, extruded and granulated to obtain the product.
Embodiment 2
[0063] Copolymerized polypropylene: 42 parts
[0064] Homopolypropylene: 28 parts
[0065] Toughener PE: 8 parts
[0066] Processing aid TAF: 0.3 parts
[0067] Processing aid EBS: 0.4 parts
[0068] Silane coupling agent KH560: 0.4 parts
[0069] Sulfuric acid solution: 0.4 parts
[0070] Heat stabilizer 1010: 0.3 parts
[0071] 2,6-tertiary butyl-4-methylphenol: 0.3 parts
[0072] Basic magnesium sulfate whiskers: 20 parts
[0073] This embodiment adopts a twin-screw extruder with a length-to-diameter ratio of 40:1. Polypropylene, a toughening agent and a heat stabilizer are melted, mixed, and dispersed in the extruder, and then the active basic magnesium sulfate whisker The premix is fed from its side, plasticized at a temperature of 190-220°C, extruded and granulated to obtain the product.
Embodiment 3
[0075] Copolymerized polypropylene: 36 parts
[0076] Homopolypropylene: 24 parts
[0077] Toughener POE: 5 parts
[0078] Processing aid TAF: 0.1 parts
[0079] Processing aid CaSt 2 : 0.2 parts
[0080] Silane coupling agent KH570: 0.5 parts
[0081] Phosphoric acid solution: 0.3 parts
[0082] Bis(3,5-tertiary butyl-4-hydroxyphenyl)sulfide: 0.5 parts
[0083] Heat stabilizer 168: 0.5 parts
[0084] Basic magnesium sulfate whiskers: 30 parts
[0085] This embodiment adopts a twin-screw extruder with a length-to-diameter ratio of 50:1. Polypropylene, toughening agent and heat stabilizer are melted, mixed and dispersed in this extruder, and then the active basic magnesium sulfate whisker The premix is fed from its side, plasticized at a temperature of 190-220°C, extruded and granulated to obtain the product.
PUM
Property | Measurement | Unit |
---|---|---|
melt flow index | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com