A technology of regenerated resin and production method, which is applied in chemical instruments and methods, synthetic resin layered products, and final product manufacturing, etc. Low cost, uniform and bright colors

Active Publication Date: 2013-04-10
KUNSHAN XIEFU NEW MATERIALS LTD BY SHARE LTD
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ordinary synthetic leather feels hard, has poor elasticity, is prone to peeling and other phenomena, and i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0027] Embodiment: a kind of method for making synthetic leather of hydrolysis-resistant regenerated resin, concrete steps are as follows:

[0028] Step 1: Wet Mixing Ingredients:

[0029] Coating Mixture Ingredients:

[0030] a: Stir 5-10kg of dimethylformamide and 4-13kg of wet-process hydrolysis-resistant color paste at high speed for 5-15 minutes, filter and set aside;

[0031] b: Stir 20-55kg dimethylformamide, 0.5-3kg wet process hydrolysis resistance additive and 0.5-2kg surfactant for 15-20 minutes, set aside;

[0032] c: Add the mixed slurry in step a to the mixture formed in step b and continue to stir for 5-15 minutes, then add 100kg of wet-process high hydrolysis-resistant regenerated polyurethane resin and stir for 1.5- After 2.5 hours, filter still, defoam and set aside;

[0033] Impregnation mixture ingredients:

[0034] d: Stir 10-15kg of dimethylformamide and 4-13kg of wet-process hydrolysis-resistant color paste at high speed for 15-20 minutes, filter and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a production method of hydrolysis resistance regenerating resin synthetic leather, including: stirring uniformly and filtering dimethylformamide and wet hydrolysis resistance paste; adding a mixture of dimethylformamide, a wet hydrolysis resistance additive and a surfactant and stirring uniformly, adding wet high hydrolysis resistance regeneration polyurethane resin to mix uniformly, filtering and defoaming to get a coating; stirring the dimethylformamide and the high hydrolysis resistance regeneration polyurethane resin uniformly and then adding the mixture of the surfactant, dimethylformamide and the wet hydrolysis resistance paste to stir uniformly to get an immersion liquid, feeding non-woven fabrics in the immersion liquid and then feeding into a quantitative roll, scraping the coating, solidifying to be film, extruding and washing, drying and fixing the shape, processing the color to get the wet base, uniformly scraping the high hydrolysis resistance dry polyurethane resin, dimethylformamide, toluene, butanone, dry hydrolysis resistance paste and the surfactant on release paper, and adhering the wet base to get the product. The synthetic leather of the present invention is soft in hand feel, good in flexibility, good in touch sense, and high in peel strength.

Description

technical field [0001] The invention relates to a manufacturing method of artificial leather, in particular to a manufacturing method of hydrolysis-resistant regenerated resin synthetic leather. Background technique [0002] Ordinary synthetic leather feels hard, has poor elasticity, is prone to peeling and other phenomena, and is difficult to decompose after damage, which is likely to cause environmental pollution and high production costs. Contents of the invention [0003] In order to overcome the above-mentioned defects, the present invention provides a method for producing hydrolysis-resistant regenerated resin synthetic leather. The method for producing hydrolysis-resistant regenerated resin synthetic leather has a simple process, and the produced product has soft hand feeling, excellent elasticity, high peel strength, and good touch. Low cost, high physical properties, and environmental protection. [0004] The technical scheme that the present invention adopts in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/14B32B27/12B32B27/18B32B27/40
CPCY02P70/62
Inventor 吴月红张凤吴玉华唐卫平皇甫觉明魏芬
Owner KUNSHAN XIEFU NEW MATERIALS LTD BY SHARE LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap