Caulking filling material easy for construction and preparation method thereof

A filling material, styrene block technology, applied in building thermal insulation materials, building components, buildings, etc., can solve the problems of increasing energy consumption of joint filling construction, emission of smoke and harmful gases, high construction temperature of joint filling, unfavorable environmental protection and other problems , to achieve the effect of good elasticity, lowering the construction temperature of the filling joint, and easy construction

Active Publication Date: 2013-04-17
CHINA PETROLEUM & CHEM CORP +1
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high addition of styrene-butadiene-styrene block copolymer, the product viscosity is relatively high, and the construction of joint filling is difficult, requiring a higher construction temperature for joint filling, which in turn increases the energy consumption of joint filling construction. and smog and other harmful gas emissions, which is not conducive to environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Heat 100 parts (by weight, the same below) of petroleum asphalt to 150°C, add 6 parts of Fufang extract oil (furfural refined extract oil, the same below), 9 parts of SBS YH-791 and 4 parts of EBS, and keep the temperature at 165 ~170°C, shear and mix for 20 minutes, add 0.11 parts of cross-linking agent, continue shearing reaction for 40 minutes, keep the temperature at 160°C, continue to develop for 60 minutes, test the performance of bridge deck caulking filling materials, see Table 1.

Embodiment 2

[0029] Heat 100 parts of petroleum asphalt to 150°C, add 8 parts of Fufang extract oil, 10 parts of SBS YH-791 and 3 parts of EBS, keep the temperature at 165-170°C, shear and mix for 20 minutes, add 0.15 parts of crosslinking agent , continue the shear reaction for 40 minutes, keep the temperature at 160°C, and continue to develop for 60 minutes to test the performance of the bridge deck caulking filling material, see Table 1.

Embodiment 3

[0031] Heat 100 parts by weight of petroleum pitch to 150°C, add 10 parts of Fufang extract oil, 12 parts of SBS YH-791, 2 parts of EBS, keep the temperature at 165-170°C, shear and mix for 20 minutes, add 0.13 parts of Cross-linking agent, continue to shear reaction for 40 minutes, keep the temperature at 160°C, and continue to develop for 60 minutes to test the performance of bridge deck caulking filling materials, see Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
penetrationaaaaaaaaaa
Login to View More

Abstract

The invention provides a caulking filling material easy for construction and a preparation method thereof. The caulking filling material is composed of 100 parts of petroleum asphalt, 5-20 parts of extract oil containing rich aromatic hydrocarbon, 3-20 parts of styrene-butadiene-styrene block polymer (SBS), 1-8 parts of ethylene bis stearamide (EBS) and 0.1-0.3 part of crosslinking agent. The preparation method comprises the following steps: heating to melt asphalt, adding the extract oil, SBS and EBS, carrying out shear mixing, adding the crosslinking agent, and evenly mixing to obtain the caulking filling material easy for construction. The caulking filling material provided by the invention has favorable high and low temperature properties; by adding the EBS, the caulking filling material has favorable flow resistance at service temperature, and the crack pouring construction temperature of the caulking filling material is obviously lowered; and the caulking filling material is easy for construction, lowers the energy consumption, decreases the emissions of smoke and other harmful gases, reduces the environmental pollution, and can be used for pavement and repair of expansion joints and cracks in bridge roads.

Description

technical field [0001] The invention relates to a caulking filling material which is easy to construct and a preparation method thereof. The caulking filling material can be used for paving and repairing expansion joints and cracks on bridge pavement. Background technique [0002] The bridge expansion joint is an important part of the bridge structure, and the performance of the bridge expansion joint directly affects the service life of the bridge and the driving comfort. Filled bridge expansion joints are a new type of bridge expansion joints. Its main working mechanism is to rely on the elasticity of the mixture of high-elastic special asphalt binder and stone to adapt to the displacement of the bridge end due to temperature and traffic loads. At the same time, it is favored by bridge builders because it has many advantages such as simple construction, low cost, comfortable driving, long service life, and half-width construction without interrupting traffic. [0003] CN1...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L53/02C08K13/02C08K5/01C08K5/20E01D19/06
Inventor 陈杰徐青柏范思远万淼
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products