Environmentally-friendly polyurethane composition for making carpet backing material, and its preparation method

A carpet backing and polyurethane technology, which is applied in the field of foam foaming, can solve the problems of easy static electricity, easy pollution and non-conformity in drying, and achieve the effects of ensuring excellent performance, improving noise absorption performance, and increasing areal density

Active Publication Date: 2015-06-24
SHANDONG INOV POLYURETHANE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Nowadays, the commonly used carpets are mostly wool or chemical fiber carpets, and these carpets have the disadvantages of being easy to pollute, not easy to clean, easy to generate static electricity when dry, and easy to be moth-eaten when wet.
However, the existing composite carpets often use adhesives to bond the surface layer and the bottom material, which is prone to produce harmful substances to the human body, and does not conform to the current trend of green environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmentally-friendly polyurethane composition for making carpet backing material, and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A component material:

[0032] Polyether polyol A: 70 (with glycerin as the initiator, primary hydroxyl content ≥ 70%, number average molecular weight 4000)

[0033] Polyether polyol B: 30 (ethylene glycol as the initiator, primary hydroxyl content ≥ 80%, number average molecular weight 3000)

[0034] AK7703: 0.8

[0035] DC-829: 0.3

[0036] Kaolin: 40

[0037] B component material:

[0038] Polyether polyol C: 50 (using ethylene glycol as the initiator, primary hydroxyl content ≥ 80%, number average molecular weight 2000)

[0039] 1,6 hexanediol: 3

[0040] Pure MDI: 15

[0041] Aggregated MDI: 10

[0042] Phosphoric acid: 10ppm

[0043] Preparation of component A materials: Put the measured polyether polyol A, polyether polyol B, AK7703, DC-829, and solid fillers into the reactor in sequence, set the speed at 60 rpm, and stir for 1 hour. Sampling is carried out for free bubble detection experiment. If milk white, gel, daily limit time and free bubble density...

Embodiment 2

[0047] A component material:

[0048] Polyether polyol A: 40 (with glycerin as the initiator, primary hydroxyl content ≥ 70%, number average molecular weight 5000)

[0049] Polyether polyol B: 40 (ethylene glycol as the initiator, primary hydroxyl content ≥ 80%, number average molecular weight 4000)

[0050] AK7703: 0.3

[0051] DC-829: 0.9

[0052] Talc powder: 10

[0053] B component material:

[0054] Polyether polyol C: 10 (using ethylene glycol as the initiator, primary hydroxyl content ≥ 80%, number average molecular weight 3000)

[0055] 1,4-Butanediol: 5

[0056] Pure MDI: 45

[0057] Phosphoric acid: 10ppm

[0058] Preparation of component A materials: Put the measured polyether polyol A, polyether polyol B, AK7703, DC-829, and solid fillers into the reaction kettle in sequence, set the speed at 100 rpm, and stir for 1 hour. Sampling is carried out for free bubble detection experiment. If milk white, gel, daily limit time and free bubble density meet the desig...

Embodiment 3

[0062] A component material:

[0063] Polyether polyol A: 80 (with glycerin as the initiator, primary hydroxyl content ≥ 70%, number average molecular weight 7000)

[0064] Polyether polyol B: 0 (ethylene glycol as the initiator, primary hydroxyl content ≥ 80%, number average molecular weight 2000)

[0065] AK7703: 2.0

[0066] DC-829:1

[0067] Steel slag powder: 50

[0068] B component material:

[0069] Polyether polyol C: 70 (using ethylene glycol as the initiator, primary hydroxyl content ≥ 80%, number average molecular weight 4000)

[0070] Ethylene glycol: 10

[0071] Carbodiimide modified MDI: 85

[0072] Phosphoric acid: 10ppm

[0073] Preparation of component A materials: Put the measured polyether polyol A, polyether polyol B, AK7703, DC-829, and solid fillers into the reactor in sequence, set the speed at 60 rpm, and stir for 2 hours. Sampling is carried out for free bubble detection experiment. If milk white, gel, daily limit time and free bubble density mee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention relates to an environmentally-friendly polyurethane composition for making a carpet backing material, and its preparation method, and belongs to the technical field of foam foaming. The composition is prepared through using a component A and a component B, wherein the component A is composed of 40-80wt% of polyether polyol A, 0-40wt% of polyether polyol B, 0.2-2.0wt% of a foam stabilizing agent, 0.2-2.0wt% of a catalyst and 10-50wt% of a solid filler. The blow-in of air through a bubbling machine substitutes a physical or chemical foaming agent in the preparation method of the composition, and belongs to an environmentally-friendly material. The temperature-sensitive catalyst used in the component A has small influences on the early-stage system reaction rate and the fluidity, is benefit for the continuous lying production in the product preparation, and guarantees the excellent performances of the composition; and the composition is a polyurethane carpet backing material having the advantages of high bonding property, no smell, and environmental protection, and the bonding strength of the solidified composition is very good.

Description

technical field [0001] The invention relates to an environment-friendly polyurethane composition for making carpet backing material and a preparation method thereof, belonging to the technical field of foaming. Background technique [0002] Nowadays, the commonly used carpets are mostly wool or chemical fiber carpets, and these carpets have the disadvantages of being easy to pollute, not easy to clean, easy to generate static electricity when dry, and easy to be eaten by insects when wet. However, the existing composite carpets mostly use adhesives to bond the surface layer and the bottom material, which is easy to produce harmful substances to the human body, and does not meet the current general trend of green environmental protection. Contents of the invention [0003] According to the deficiencies of the prior art, the technical problem to be solved by the present invention is: provide an environment-friendly polyurethane composition for making carpet backing material,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/66C08G18/48C08G18/32C08J9/30C09J175/08
Inventor 李健孙清峰牛富刚罗杰
Owner SHANDONG INOV POLYURETHANE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap