Pre-cold pressing quenching correction technology for die steel

A die steel and pre-cooling technology, applied in quenching devices, manufacturing tools, furnaces, etc., can solve the problems of increased difficulty, deformed metal workpiece performance, time-consuming and labor-intensive, etc., and achieves the effects of small deformation, low quenching stress, and easy correction.

Inactive Publication Date: 2013-05-15
昆山鑫昌泰模具科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above two correction methods are all carried out after the workpiece is quenched and cooled, and the correction should be carried out according to the specific deformation of the metal after quenching. Since the strength and hardness of the metal workpiece after quenching are significantly improved, the difficulty of correction is greatly increased and it is time-consuming and labor-intensive. New deformations may appear after corrections or have a certain impact on the performance of metal workpieces
The above situation is especially serious for thin plates or strip workpieces with a thickness of less than 20mm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pre-cold pressing quenching correction technology for die steel
  • Pre-cold pressing quenching correction technology for die steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] combine figure 1 The present invention is described in further detail.

[0016] The size specification of the steel sheet selected in this embodiment is 500×100×20 mm; the material of the selected steel sheet is one of hypereutectoid steel.

[0017] A pre-cooling and press-quenching correction process for die steel: comprising the following steps:

[0018] Step (1): Place the steel sheet to be quenched in a quenching furnace and heat to the Ac1+(50-80)°C of the steel sheet material;

[0019] Step (2): precooling the steel sheet heated in step (1) at room temperature for 30 to 60 seconds;

[0020] Step (3): Place the pre-cooled steel sheet in step (2) quickly on two press-quenched plates, start the hydraulic device, and the hydraulic device applies a pressure of 1 to 2 tons to the press-quenched plate, while the steel sheet is Natural cooling is carried out in the ambient temperature environment of the atmosphere, and the internal structure of the steel sheet material...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a pre-cold pressing quenching correction technology for a die steel. The technology, which quits the manner of the traditional thermal treatment process that the die steel needs to be insulated for a while after heating, comprises the steps of pre-cooling the die steel part after being heated to Ac1+(50-80)DEG C of the material, and carrying out pressing quenching cooling correction on the die steel directly without heat preservation. According to the technology, the plasticity and toughness of an austenite material are fully utilized, the quenching stress of the die steel being thermally treated is lowered to the minimum, the die steel deforms slightest, and then the die steel workpiece is simple and easy to correct.

Description

technical field [0001] The invention relates to a metal quenching correction process, in particular to a pre-cooling press quenching correction process for die steel. Background technique [0002] Due to the rapid cooling of the metal workpiece during the quenching process, internal stress will be generated inside the workpiece. When the internal stress is large enough to a certain extent, the workpiece will be distorted and deformed. Therefore, the deformation must be corrected before the next step of the workpiece. At present, the commonly used correction methods include mechanical correction and heat treatment correction. Mechanical correction is to use mechanical methods to cause local micro-deformation of deformed workpieces, and at the same time release residual internal stress to achieve the purpose of correcting deformation. Heat treatment correction generally uses appropriate heat treatment methods to correct the deformation. Its thermal deformation is corrected. H...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C21D9/00C21D9/46C21D1/673
Inventor 沈君
Owner 昆山鑫昌泰模具科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap