Alloy material for false tooth

An alloy material, denture technology, applied in the fields of medical science, dentistry, dental preparations, etc., can solve the problems of high price and harm, and achieve the effects of low price, strong corrosion resistance and high tensile strength

Inactive Publication Date: 2013-05-22
AI JIA DENTAL LAB
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Based on this, it is necessary to provide a low-cost, safe and excellent denture alloy material for the problems that precious metal materials are expensive and non-precious metal alloy materials are harmful to the human body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alloy material for false tooth
  • Alloy material for false tooth
  • Alloy material for false tooth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1 cobalt chromium alloy

[0021] The denture alloy material of this embodiment includes the following components in terms of mass percentage: Co58.00%, Cr26.00%, W9.50%, Mo2.50%, Nb1.10%, Mn1.10%, Si0. 80%, Fe1.00%.

Embodiment 2

[0022] Embodiment 2 cobalt chromium alloy

[0023] The denture alloy material of this embodiment includes the following components in terms of mass percentage: Co62.00%, Cr23.00%, W8.50%, Mo2.70%, Nb0.95%, Mn0.90%, Si1. 05%, Fe0.90%.

Embodiment 3

[0024] Embodiment 3 cobalt chromium alloy

[0025] The denture alloy material of this embodiment includes the following components in terms of mass percentage: Co61.00%, Cr24.00%, W8.50%, Mo2.50%, Nb1.00%, Mn1.00%, Si1. 00%, Fe1.00%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an alloy material for a false tooth. The alloy material comprises the following components in percentage by weight: 58.00-63.00% of Co, 22.00-26% of Cr, 6.00-10.00% of W, 2.30-2.80% of Mo, 0.80-1.10% of Nb, 0.80-1.10% of Mn, 0.80-1.10% of Si and 0.80-1.10% of Fe. According to the alloy material for the false tooth, cobalt-chromium alloy is used, noble material which is high in using price is not used, Be element which is harmful to a human body is abandoned, and the cobalt-chromium alloy prepared from Co, Cr, W, Mo, Nb, Mn, Si and Fe low in price and safe and nontoxic is low in cost, safe and nontoxic, strong in corrosion resistance, high in strength of extension, low in coefficient of linear expansion, large in hardness and yield strength. The alloy material for the false tooth provided by the invention is an excellent material for making ceramic teeth.

Description

technical field [0001] The invention relates to the field of dental restoration, in particular to denture alloy materials. Background technique [0002] Dental disease is a common disease with a high incidence. Tooth defects and missing dentition are very common in dental diseases, and dentures are usually used to restore them. [0003] Porcelain teeth are a kind of commonly used dentures. Generally, alloy materials are used to make porcelain teeth. The alloy for making porcelain teeth must meet the following conditions: (1) good biocompatibility, non-toxic and harmless to the human body; (2) chemical Stable performance, must have excellent oxidation resistance and corrosion resistance; (3) stable physical properties, must have high strength. [0004] General porcelain teeth are divided into precious metal porcelain teeth and non-precious metal porcelain teeth. Precious metal porcelain teeth are the best performance porcelain teeth. Taking gold porcelain teeth as an exampl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C19/07A61K6/04
Inventor 刘嘉
Owner AI JIA DENTAL LAB
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com