Material with excellent piezoelectric property and preparation method of material

A piezoelectric performance, excellent technology, applied in the field of piezoelectric ceramics, can solve problems such as not having piezoelectric performance, and achieve the effect of simple synthesis process

Inactive Publication Date: 2013-05-29
UNIV OF SCI & TECH BEIJING
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has broad application prospects in piezoelectric transducers, sensors and drivers, and has attracted close attention from scholars at home and abroad. However, in addition to BiScO 3 -PbTiO 3 Except for piezoelectric materials, other syste...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Material with excellent piezoelectric property and preparation method of material
  • Material with excellent piezoelectric property and preparation method of material
  • Material with excellent piezoelectric property and preparation method of material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Utilize this invention to prepare 0.38Bi(Ni 1 / 2 f 1 / 2 )O 3 -0.62PbTiO 3 . Weigh 5.0000 g PbO, 3.1986 g Bi 2 o 3 , 0.5127 g NiO, 1.7890 g TiO 2 and 1.4449 g HfO 2 . Grind the powder thoroughly in a mortar, then calcinate the powder at 850°C for 6 hours, press the sample after cooling to room temperature with the furnace, and sinter the obtained sheet at 1180°C for 2 hours to obtain a dense high-pressure powder. Electrical properties of ceramic samples, piezoelectric coefficient d 33 =446pC / N, Curie temperature T C =290°C. figure 1 and figure 2 is 0.38Bi(Ni 1 / 2 f 1 / 2 )O 3 -0.62PbTiO 3 X-ray diffraction pattern and scanning electron microscope diffraction pattern.

Embodiment 2

[0032] Using this invention to prepare 0.39Bi(Ni 1 / 2 f 1 / 2 )O 3 -0.61PbTiO 3 . Weigh 5.0000 g PbO, 3.3366 g Bi 2 o 3 , 0.5349 g NiO, 1.7890 g TiO 2 and 1.5073 g HfO 2 . Fully grind to 1800 mesh in a mortar, then calcinate the powder at 850°C for 6 hours, press the sample after cooling to room temperature with the furnace, and finally sinter the obtained tablet at 1210°C for 2 hours, you can get Ceramic sheet samples with high piezoelectric properties, piezoelectric coefficient d 33 =434pC / N, Curie temperature T C =275°C. image 3 is 0.39Bi(Ni 1 / 2 f 1 / 2 )O 3 -0.61PbTiO 3 The x-ray diffraction pattern of .

Embodiment 3

[0034] Utilize this invention to prepare 0.30Bi(Ni 1 / 2 f 1 / 2 )O 3 -0.70PbTiO 3 . Weigh 5.0000 g PbO, 2.2366 g Bi 2 o 3 , 0.3585 g NiO, 1.7890 g TiO 2 and 1.0104 g HfO 2 . Grind the powder thoroughly in a mortar, then calcinate the powder at 600°C for 10 hours, press the sample after cooling to room temperature with the furnace, and sinter the obtained sheet at 1500°C for 1 hour to obtain a dense high-pressure powder. Electrical properties of ceramic samples.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Piezoelectric coefficientaaaaaaaaaa
Curie temperatureaaaaaaaaaa
Piezoelectric coefficientaaaaaaaaaa
Login to view more

Abstract

The invention discloses a material with excellent piezoelectric property and a preparation method of the material, belonging to the field of piezoceramic materials. A chemical structure general formula of the material with excellent piezoelectric property is (1-x)BiMeO3-xPbTiO3, wherein Me=Ni1/2Hf1/2 or Ni1/2Zr1/2; and 0.5<x<1. The preparation method comprises the following steps of: based on Bi2O3, NiO, HfO2, ZrO2, PbO and TiO2 as raw materials, weighing Bi2O3, NiO, HfO2 or ZrO2, PbO and TiO2 which accord with the chemical dose ratio according to the chemical structure general formula, uniformly grinding, calcining a sample after grinding for 1-10h at the temperature of 600-1000 DEG C, then tabletting the sample, and sintering the tabletted sample for 1-15h at the temperature of 800-1500 DEG C to obtain the material with excellent piezoelectric property. The material is low in preparation cost and simple in synthetic process, thus having larger scientific research and practical values.

Description

technical field [0001] The invention relates to a piezoelectric functional material and a preparation method thereof, belonging to the field of piezoelectric ceramics, in particular to a material with excellent piezoelectric performance and a preparation method thereof. Background technique [0002] Piezoelectric ceramics are widely used in electronic science and technology, including electroacoustic transducers, underwater acoustic transducers and ultrasonic transducers, as well as other sensor and driver applications. The market is huge, and it is one of the most important electronic materials. It has become an important functional material in the defense industry, civilian industry and daily life. In 2011, Richard E. Eitel [1] proposed Bi( Me )O 3 -PbTiO 3 Material system (of which Me +3 is a cation with a relatively large radius, such as Sc, Y, Yb, In, etc.). literature Japanese Journal of Applied Physics 40, 5999 (2001) reported that BiScO 3 -PbTiO 3 The mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/49C04B35/622
Inventor 陈骏潘昭戎阳春樊龙龙邓金侠于然波邢献然
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap