Preparation method and application of China hemp fiber

A technology of hemp fiber and hemp, which is applied in the field of hemp fiber preparation, to achieve the effects of preventing diaper rash, environmental protection and resource saving

Active Publication Date: 2013-06-05
河南舒莱卫生用品有限公司
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, there is no report of using hemp as raw material to manufacture sanitary products such as diapers; the market needs a hemp fiber using hemp as raw material, and products such as diapers and sanitary napkins made of it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of China hemp fiber
  • Preparation method and application of China hemp fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A preparation method of hemp fiber, comprising the following steps:

[0039] 1) Peeling and soaking: peel the hemp to obtain peeled hemp, then soak the peeled hemp in a caustic soda solution with a weight ratio of 1:0.2 for 12 hours to obtain a soaking solution;

[0040] 2) Degumming: adding a hydrochloric acid solution with a volume ratio of 1:0.05 and a concentration of 40% to the soaking liquid, cooking at 95-100°C for 8 hours, and repeated cooking for 5 times to obtain finer hemp fibers;

[0041] 3) Drying: Ventilate and dry the finer hemp fibers at 60°C for 2 to 4 hours to obtain dried hemp fibers;

[0042] 4) Screening: Screen the dried hemp fibers, and collect and utilize those whose fineness reaches the requirement of 2.0D; degumming the thicker fibers until they meet the required fineness;

[0043] Promptly obtain described hemp fiber.

[0044] The unit of weight used in this embodiment is kilogram, and may also be gram.

[0045] All raw materials described ...

Embodiment 2

[0048] This embodiment is an application of the hemp fiber described in Example 1, the hemp fiber can be used to manufacture diapers, and the preparation method of the hemp fiber diapers comprises the following steps:

[0049] A. Preparation of hemp fiber:

[0050] 1) Peeling and soaking: peel the hemp to obtain peeled hemp, then soak the peeled hemp in a caustic soda solution with a weight ratio of 1:0.2 for 12 hours to obtain a soaking solution;

[0051] 2) Degumming: adding a hydrochloric acid solution with a volume ratio of 1:0.05 and a concentration of 40% to the soaking liquid, cooking at 95-100°C for 8 hours, and repeated cooking for 5 times to obtain finer hemp fibers;

[0052] 3) Drying: Ventilate and dry the finer hemp fibers at 60°C for 2 to 4 hours to obtain dried hemp fibers;

[0053] 4) Screening: Screen the dried hemp fibers, and collect and utilize those whose fineness reaches the requirement of 2.0D; degumming the thicker fibers until they meet the required f...

Embodiment 3

[0067] This embodiment is an improvement made on the basis of Embodiment 1. For the same part as Embodiment 1 in this embodiment, please refer to the content disclosed in Embodiment 1 for understanding, and the content disclosed in Embodiment 1 should also be used as this embodiment. The content of the example will not be repeated here.

[0068] The preparation method of the hemp fiber of the present embodiment comprises the following steps:

[0069] 1) Peeling and soaking: peel the hemp to obtain peeled hemp, then soak the peeled hemp in a caustic soda solution with a weight ratio of 1:0.2 for 12 hours to obtain a soaking solution;

[0070] 2) Degumming: adding a hydrochloric acid solution with a volume ratio of 1:0.05 and a concentration of 40% to the soaking liquid, cooking at 95-100°C for 8 hours, and repeated cooking for 5 times to obtain finer hemp fibers;

[0071] 3) Drying: Ventilate and dry the finer hemp fibers at 60°C for 2 to 4 hours to obtain dried hemp fibers; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing a China hemp fiber, as well as an application of the China hemp fiber on paper diapers. The method for preparing the China hemp fiber comprises the following steps: removing the peel, soaking, degumming, drying and screening. The preparation process is simple, and the cost is saved. The paper diapers are prepared by using the China hemp fiber and have the originally ecological special antibacterial, mould-proof, ventilating, comfortable, radiating and anti-radiation effect; and therefore, compared with the organic and inorganic antibiosis in the prior art, the China hemp fiber is good in antibacterial effect, washing-resistant and easily degradable and can be sustainably utilized; and moreover, the China hemp fiber is good in antibacterial effect, prevents diaper rash and bedsore, is washing-resistant, easily degradable and environment-friendly and can be sustainably utilized, and the resources are saved.

Description

technical field [0001] The invention relates to the field of daily necessities, in particular to a preparation method of hemp fiber and its application in diapers and sanitary napkins. Background technique [0002] In the field of diapers, the antibacterial technologies currently used are inorganic and organic. However, organic antibacterial is mainly chemical antibacterial, which has a great impact on the environment and human body, and is not washable; inorganic antibacterial mainly uses metal ion antibacterial technology, such as nano-silver, zinc, copper ions, etc., but cannot be degraded. consumes resources and pollutes the environment. Therefore, there is an urgent need to develop an antibacterial material that has strong antibacterial ability, has no toxic effect on the human body, and has no pollution in the production process, so as to solve the antibacterial problem in the field of hygiene products. [0003] Hemp, also known as hemp, originated in China. It is kn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01C1/02D04H1/425D04H1/4382A61F13/15
Inventor 赵华伟闫秀珍
Owner 河南舒莱卫生用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com