Vegetable seedling breeding matrix material made of hickory cattail husk and preparation method for vegetable seedling breeding matrix material
The technology of vegetable seedling substrate and pecan catfish shell is applied in the preparation and application of fertilizers made of biological waste and organic fertilizers, which can solve the problems of high cost, small amount, unsuitable for large-scale production and the like, and achieves protection of peat resources. , the effect of solving the pollution problem
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1: Fermentation temperature test
[0023] 1). Material: Pecan husks were collected from Changhua Town, Lin'an City, Zhejiang Province, and collected during the local harvest.
[0024] 2). Test method: The test has 4 formula treatments, and the specific composition is:
[0025] (A) 80% hickory husk + 0% soybean meal + 20% carbonized rice husk
[0026] (B) 80% hickory husk + 5% soybean meal + 15% carbonized rice husk
[0027] (C) 80% hickory husk + 10% soybean meal + 10% carbonized rice husk
[0028] (D) 80% hickory husk + 15% soybean meal + 5% carbonized rice husk
[0029] 3). Test results and analysis: see figure 1 .
[0030] The heating process and fermentation process of different material ratio fermentation reactors are obviously different, which is manifested in the obvious difference in the maintenance time of the reactor temperature. The maintenance time of treatment B is the longest, the time above 55℃ is 31 days, the treatment C is 15 days, and the treatment D is 5 ...
Example Embodiment
[0032] Example 2: Germination test of water extract of fermented product in different time period
[0033] 1). Materials: Fermented products were randomly collected from treatment B in Example 1, and the test variety was green cauliflower seeds.
[0034] 2). Test method: 10 days, 20 days, 30 days, 40 days, 50 days, and 60 days respectively before and after the start of fermentation, randomly collect 5 500 ml samples, mix them evenly, and then press the screw to achieve For solid-liquid separation, add 1000 ml of deionized water to the solid, stir for 5 minutes and filter. Take 100 ml of the filtrate in a petri dish, put 100 green cauliflower seeds in the incubator at 25°C for 5 days and determine the germination rate of the seeds. The germination test is set to 4 repetitions.
[0035] 3). Test results and analysis: see Table 1.
[0036] Table 1 The effect of water extract of fermented product in different time period on seed germination
[0037]
[0038] It can be seen from T...
Example Embodiment
[0040] Example 3: Germination test of water extracts of fermented products with different proportions
[0041] 1). Materials: From each treatment in Example 1, samples were collected according to the method in Example 2. The test vegetable seeds were the same as in Example 2.
[0042] 2). Test method: After 60 days of fermentation test, 5 samples of 1000 ml were randomly collected from each treatment in Example 1, and they were evenly mixed and divided into 2 samples, one of which was extruded by screw to achieve solid-liquid separation. Add 1000 ml of deionized water to the solid, stir for 5 minutes, and filter. The other sample was directly added with the same amount of deionized water and stirred and filtered. Take 100 ml of the filtrate in a petri dish, put 100 green cauliflower seeds in the incubator at 25°C for 5 days and determine the germination rate of the seeds. The germination test is set to 4 repetitions.
[0043] 3). Test results and analysis: see Table 2.
[0044] Fro...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap