Thiophene adsorbents and application thereof
A technology of adsorbent and thiophene, which is applied to the purification treatment agent for removing thiophene in aqueous solution and its treatment field, can solve the problems of unsatisfactory treatment effect, complicated process and high treatment cost, and achieves significant practical value, strong adsorption effect, and solution Effects of pollution problems
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0016] Example 1
[0017] Accurately weigh 23.800g of Zn(NO 3 ) 2 .6H 2 O, 15.005g of Al (NO 3 ) 3 .9H 2 O, and 23.070g of sodium dodecyl sulfate (SDS) were placed in a beaker, 400mL of distilled water was added, stirred to dissolve completely, and then transferred to a 1000mL three-necked flask. 2M NaOH solution was added dropwise to maintain the pH at 7, the temperature was controlled at 30°C, and the crystallization time was 12h. Finally, centrifugal filtration and vacuum drying can obtain the desired product, which is denoted as SDS-ZnAl-LDH.
[0018] In a 1000mL reaction vessel, measure 500mL of a solution with a thiophene concentration of 800mg / L, a water bath at a constant temperature of 25°C, PH=6.33, and add 1.2g of SDS-Zn 2 Al 1 -LDH, stirring for 6 hours, extracting a certain amount of reaction solution, filtering to obtain the supernatant, measuring the remaining content of thiophene, and calculating the adsorption rate of 74.74%.
Example Embodiment
[0019] Example 2
[0020] Accurately weigh 23.800g Zn(NO 3 ) 2 .6H 2 O and 15.005g Al (NO 3 ) 3 .9H 2 Put O in a beaker, add 200 mL of deionized water, stir to dissolve it completely, record it as solution A; accurately weigh 8.479 g of Na 2 CO 3 Put 7.680g NaOH in a beaker, add 200mL deionized water, stir to dissolve it completely, and record it as solution B. The A and B solutions were quickly mixed in the rotating liquid film nucleation reactor, vigorously circulated and stirred for 2 min, then the slurry was crystallized at 80 °C for 24 h, and finally centrifuged and dried to obtain the desired product, denoted as ZnAL-CO 3 -LDH.
[0021] In a 1000mL reaction vessel, measure 500mL of a solution with a thiophene concentration of 800mg / L, a water bath at a constant temperature of 25°C, pH=6.33, add 1.2g Zn 2 AL 1 -CO 3 -LDH, stir for 5h, extract a certain amount of reaction solution, filter to obtain the supernatant, measure the remaining content of thiophene, and...
Example Embodiment
[0022] Example 3
[0023] In a 100mL conical flask, measure 100mL of a solution with a thiophene concentration of 800mg / L, control the temperature at 25°C, pH=6.33, add 0.4g of SDS-ZnAl-LDH prepared in Example 1, stir for 5h, and filter to obtain the upper layer In the clear night, the residual content of thiophene was measured, and the adsorption rate was calculated to be 82.84%.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap