Hard metal used for drilling bit

A hard metal and drill bit technology, applied in the field of hard metal, can solve the problems of uneven carbonization reaction, segregation and restriction of structural defects, and achieve the effect of improving the uniformity of the structure, uniform structure and reducing sintering defects

Active Publication Date: 2013-09-11
JIANGMEN JIANTAO HI TECH
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current invention patent discloses a hard alloy, but the hard alloy is prepared by mixing traditional metal powder and carbon powder. Due to the large particle size of the raw material, it is difficult for the carbon powder to effectively form a wrapping structure outside the metal powder, and the uneven carbonization reaction leads to structural defects. Serious segregation greatly restricts the implementation of this method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A hard metal used for drill bits is prepared from the following components by weight:

[0020] Fe: 150 parts; Graphene: 0.05 parts, carbon powder: 0.1 parts, SiO 2 : 0.01 parts, Ti : 5 parts, TiO 2 : 0.2 parts; P: 0.01 parts, Cr: 2 parts, Ni: 5 parts, Mo: 0.5 parts.

[0021] A method for preparing a hard metal for a drill bit, comprising the following steps:

[0022] Graphene is uniformly dispersed in an organic solvent to form a dispersion liquid, and then mixed with other raw material powders to form a cemented carbide raw material, the mixture is melted, cooled into an ingot, ground into a fine powder, dried, granulated, and melted again , to get the desired product.

Embodiment 2

[0024] A hard metal for a drill bit, characterized in that it is prepared from the following components by weight:

[0025] Fe: 240 parts; graphene: 0.1 parts, carbon powder: 0.5 parts, SiO 2 : 0.03 parts, Ti : 10 parts, TiO 2 : 0.8 parts; P: 0.05 parts, Cr: 4 parts, Ni: 10 parts, Mo: 1 part.

[0026] A method for preparing a hard metal for a drill bit, comprising the following steps:

[0027] Graphene is uniformly dispersed in an organic solvent to form a dispersion liquid, and then mixed with other raw material powders to form a cemented carbide raw material, the mixture is melted, cooled into an ingot, ground into a fine powder, dried, granulated, and melted again , to get the desired product.

Embodiment 3

[0029] A hard metal used for drill bits is prepared from the following components by weight:

[0030] Fe: 200 parts; graphene: 0.08 parts, carbon powder: 0.3 parts, SiO 2 : 0.02 parts, Ti : 6 parts, TiO 2 : 0.5 parts; P: 0.03 parts, Cr: 3 parts, Ni: 7 parts, Mo: 0.7 parts.

[0031] A method for preparing a hard metal for a drill bit, comprising the following steps:

[0032] Graphene is uniformly dispersed in an organic solvent to form a dispersion liquid, and then mixed with other raw material powders to form a cemented carbide raw material, the mixture is melted, cooled into an ingot, ground into a fine powder, dried, granulated, and melted again , to get the desired product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses hard metal used for a drilling bit. The hard metal is prepared by following components, by weight, 150-240 parts of Fe; 0.05-0.1 part of graphite alkene, 0.1-0.5 part of carbon dust; 0.01-0.03 part of SiO2, 5-10 parts of Ti, 0.2-0.8 part of TiO2; and 0.01-0.05 part of P, 2-4 parts of Cr, 5-10 parts of Ni, 0.5-1 part of Mo. Hardness of the hard metal used for the drilling bit is much larger than that of common alloy or metal, and a preparation method of the hard metal is quite simple and particularly suitable for industrial production.

Description

technical field [0001] The present invention relates to an alloy material, in particular to a hard metal used for a drill bit. Background technique [0002] Drills are generally made of cemented carbide, because the epoxy glass cloth clad copper foil plate wears the tool very quickly. The so-called cemented carbide is formed by pressing and sintering tungsten carbide powder as the matrix and cobalt powder as the binder. It usually contains 94% tungsten carbide and 6% cobalt. Due to its high hardness, it is very wear-resistant and has a certain strength, which is suitable for high-speed cutting. However, the toughness is poor and very brittle. In order to improve the performance of the cemented carbide, some use a chemical vapor deposition layer of 5-7 microns of extra-hard titanium carbide (TIC) or titanium nitride (TIN) on the carbide substrate to make it Has higher hardness. Some use ion implantation technology to inject titanium, nitrogen, and carbon into the matrix t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F1/00C22C38/50
Inventor 蒋伟锋
Owner JIANGMEN JIANTAO HI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com