Aluminium alloy sheet material for labour protection leather shoes head and preparation method thereof

An aluminum alloy sheet, aluminum alloy technology, applied in shoe uppers, footwear, applications, etc., can solve the problems of unsatisfactory performance and thick thickness, and achieve the effects of improving work efficiency, low thickness and shortening molding time.

Active Publication Date: 2013-09-11
SOUTHWEST ALUMINUM GRP
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] General labor insurance shoes have fixed plates or protective plates embedded in their heads, and the fixed plates or protective plates use aluminum alloy plates or plastic plates, but the aluminum alloy plates used for safety protection of labor insurance leather shoes in the prior art, The thickness is thick, and the performance cannot meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminium alloy sheet material for labour protection leather shoes head and preparation method thereof
  • Aluminium alloy sheet material for labour protection leather shoes head and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0049] The invention provides a method for preparing an aluminum alloy plate used for the toe cap of labor insurance leather shoes, comprising:

[0050] a) Provide an aluminum alloy ingot; the aluminum alloy ingot includes the following elements by weight percentage:

[0051] Fe 0.50%~1%;

[0052] Mn 0.40%~1.0%;

[0053] Mg 0.4%~0.80%;

[0054] Si 0.20%~0.80%;

[0055] Zr 0.2%~0.3%;

[0056] Ti 0.10%~0.2%;

[0057] Cu 3.5%~4.5%;

[0058] The balance of Al;

[0059] b) homogenizing, planing, sawing and milling the aluminum alloy ingot;

[0060] c) hot-rolling and cold-rolling the milled aluminum alloy ingot;

[0061] d) Annealing the cold-rolled aluminum alloy prefabricated plate;

[0062] e) pre-shearing and finishing the annealed aluminum alloy prefabricated panel;

[0063] f) Cleaning and drying the finished aluminum alloy prefabricated plate to obtain an aluminum alloy plate for the toe cap of labor insurance leather shoes.

[0064] According to the present inven...

Embodiment 1

[0079] Fe 0.50%;

[0080] Mn 0.40%;

[0081] Mg 0.4%;

[0082] Si 0.20%;

[0083] Zr 0.2%;

[0084] Ti 0.10%;

[0085] Cu 3.5%;

[0086] The balance of Al;

[0087] Mix the metal powders in the above weight percentages, prepare an ingot by powder metallurgy, and mill the ingot on a milling machine. .

[0088] Then heat the aluminum alloy ingot after milling, and perform homogenization treatment. The heating temperature is 580°C,

[0089] The homogenized ingot is immediately hot-rolled, the starting temperature is preferably 580°C, the final rolling temperature is preferably 500°C, and the thickness of the plate is 1% of the thickness of the ingot.

[0090] The hot-rolled ingot is subjected to the first cold rolling. According to the present invention, the first cold rolling adopts a larger reduction, which is 1% of the thickness of the hot-rolled ingot. The rolling start temperature was 300°C. The finishing temperature is preferably 250°C. A preform is obtained aft...

Embodiment 2

[0093] Fe 1%;

[0094] Mn 1.0%;

[0095] Mg 0.80%;

[0096] Si 0.80%;

[0097] Zr 0.3%;

[0098] Ti 0.2%;

[0099] Cu 4.5%;

[0100] The balance of Al.

[0101] The ingot is milled on a milling machine, the amount of milling on one side is 8mm, to ensure that the defects on both sides are milled clean, and the side milling cutter mills the small face.

[0102] Then heat the aluminum alloy ingot after milling, and perform homogenization treatment. The heating temperature is 500°C,

[0103] The homogenized ingot is immediately hot-rolled, the starting temperature is preferably 500°C, the final rolling temperature is preferably 450°C, and the thickness of the plate is 10% of the thickness of the ingot.

[0104] The hot-rolled ingot is subjected to the first cold rolling. According to the present invention, the first cold rolling adopts a larger reduction, which is 10% of the thickness of the hot-rolled ingot. The rolling start temperature was 300°C. The finishing temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides an aluminium alloy sheet material for labour protection leather shoes head and preparation method thereof, and the aluminium alloy sheet material is 7xxx series aluminium alloy, and concretely comprises the following components by weight percent: 0.50-1% of Fe, 0.40-1.0% of Mn, 0.4-0.80% of Mg, 0.20-0.80% of Si, 0.2-0.3% of Zr, 0.10-0.2% of Ti, 3.5-4.5% of Cu and Al the rest amount. The aluminium alloy contains Zr, Ti, Si, Cu and Mg, and has a high hardness and intensity, and belongs to the superhard aluminium alloy, the invention has a good wear resistance, and after the stress is relieved by processing, the product does not deform and warp, thereby shortening the moulding time and improving the work efficiency. The aluminium alloy sheet material provided by the invention can satisfy the requirements of intensity and hardness, and ensure the thickness of the aluminium alloy sheet material is the lowest.

Description

technical field [0001] The invention relates to the field of preparation of aluminum alloys, in particular to a preparation method of an aluminum alloy plate used for labor protection leather toe caps. Background technique [0002] Labor insurance shoes are a kind of shoes that have a safety protection effect on the feet. There are many types of it, such as toe protection, anti-puncture, insulation, acid and alkali resistance, etc. The selection of labor insurance shoes should be carried out according to the nature and degree of hazards of the working environment. [0003] General labor insurance shoes have fixed plates or protective plates embedded in their heads, and the fixed plates or protective plates use aluminum alloy plates or plastic plates, but the aluminum alloy plates used for safety protection of labor insurance shoes in the prior art, The thickness is thicker, and the performance cannot meet the requirements. Contents of the invention [0004] The technica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/16C22F1/057C21D8/02A43B23/10
Inventor 赵涛王军
Owner SOUTHWEST ALUMINUM GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap