Large-thickness high-performance SA302GrC steel plate and production method thereof

A production method and large-thickness technology, applied in the field of iron and steel smelting technology, can solve problems such as production difficulties, and achieve the effects of simple production and manufacturing procedures, increased supercooling, and improved strength

Active Publication Date: 2013-09-18
WUYANG IRON & STEEL +1
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because of the very strict requirements on the material itself, production is very difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The actual composition (by weight percentage) of the SA302GrC steel of the present invention is: C 0.16%, Si 0.24%, Mn 1.33%, P 0.012%, S 0.002%, Al 0.028%, V 0.006%, Ni 0.46%, Cr 0.04% , Mo 0.52%, Cu 0.07%, Ti 0.002%, Ceq 0.53%, rolled into 135mm steel plate. Its mechanical properties: yield strength: 452MPa, tensile strength: 595MPa, yield strength ratio: 0.76, A%: 28%, -10°C impact energy AKV (transverse direction): 131, 143, 151J, Z direction: 45%.

Embodiment 2

[0023] The actual composition (by weight percentage) of the SA302GrC steel of the present invention is: C 0.11%, Si 0.20%, Mn 1.30%, P 0.010%, S 0.002%, Al 0.025%, V 0.004%, Ni 0.42%, Cr 0.05% , Mo 0.50%, Cu 0.07%, Ti 0.002%, Ceq 0.47%, rolled into 135mm steel plate. Its mechanical properties: yield strength: 435MPa, tensile strength: 575MPa, yield strength ratio: 0.76, A%: 28%, -10°C impact energy AKV (transverse direction): 135, 142, 155J, Z direction: 50%.

Embodiment 3

[0025] The actual composition (by weight percentage) of the SA302GrC steel of the present invention is: C 0.17%, Si 0.35%, Mn 1.40%, P 0.011%, S 0.002%, Al 0.028%, V 0.006%, Ni 0.50%, Cr 0.04% , Mo 0.57%, Cu 0.07%, Ti 0.002%, Ceq 0.56%, rolled into 135mm steel plate. Its mechanical properties: yield strength: 445MPa, tensile strength: 582MPa, yield strength ratio: 0.76, A%: 29%, -10°C impact energy AKV (transverse direction): 125, 128, 118J, Z direction: 45%.

[0026] The processing steps of each embodiment are as follows:

[0027] ① Smelting process: The mass percentages of the chemical components of molten steel are as follows: C 0.10-0.18%, Si 0.15-0.40%, Mn 1.20-1.45%, P ≤0.015%, S ≤0.010%, Ni 0.40-0.55%, Mo 0.45-0.60 %, the rest is Fe and unavoidable impurities. The molten steel is first smelted in an electric furnace. When P≤0.012%, the ladle temperature is ≥1570℃, the steel is tapped, and the LF furnace is refined. The white slag retention time is ≥25 minutes, and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Impact energyaaaaaaaaaa
Login to View More

Abstract

The invention relates to a large-thickness high-performance SA302GrC steel plate and a production method thereof, belonging to the technical field of steel smelting processes. According to the technical scheme, the production method comprises procedures of smelting, casting, heating, rolling, cooling after rolling, normalizing, accelerated cooling and tempering; and the steel plate is prepared from the following chemical ingredients in percentage by mass: 0.10-0.18% of C, 0.15-0.40% of Si, 1.20-1.45% of Mn, less than or equal to 0.015% of P, less than or equal to 0.010% of S, 0.40-0.55% of Ni, 0.45-0.60% of Mo, and the balance of Fe and inevitable impurities. The steel plate has the following advantages that the obdurability matching is good, the yield strength Re is greater than or equal to 345Mpa, the transverse Charpy impact in the position which is 1 / 4 of the plate thickness at minus 10 DEG C is less than 41J, the steel quality is purer, the lamellar tearing resisting property is good, the through thickness direction Z is greater than or equal to 35%, the welding property is good, and the thickness of the steel plate is 135mm. The steel plate which is produced by using the production method provided by the invention has the characteristics of high purity, uniformity in component and internal compactness, and has good obdurability matching.

Description

technical field [0001] The invention relates to a large-thickness high-performance SA302GrC steel plate and a production method thereof, in particular to a large-thickness high-performance SA302GrC steel plate of 135mm, belonging to the technical field of iron and steel smelting technology. Background technique [0002] In recent years, the development of the petrochemical industry is mainly centered on the secondary deep processing of the coal chemical industry and the large-scale installation, marked by the application of high temperature and high pressure technology. The service conditions of the steel plate are harsh, and the material has been exposed to high temperature, high pressure and hydrogen for a long time. In addition to meeting the basic mechanical properties at room temperature, the material also needs to meet the requirements of strength at high temperature, resistance to temper embrittlement and hydrogen corrosion. Because of the very strict requirements on ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/12C22C33/04C21D8/02
Inventor 袁锦程韦明刘生张萌吴艳阳牛红星高雅尹卫江王全胜秦红新
Owner WUYANG IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com