Cold rolled coil strapping steel having tensile strength of 940MPa or more, and production method thereof
A technology with a tensile strength of 940mpa, applied in the field of strapping steel for cold-rolled coils and its production, can solve the problems of rising raw material costs, complicated operations, and easy damage to machines, and achieves low cost, simple operation, energy consumption and pollution. small effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0037] Example 1
[0038] The chemical composition of the hot-rolled sheet raw material is as follows: C: 0.11%, Mn: 1.35%, Si: 0.019%, P: 0.015%, S: 0.004%, Als: 0.04%, and the rest are Fe and residual elements.
[0039] The dimensions of the hot-rolled steel plate are as follows: thickness is 3.0 mm, width is 1295 mm; mechanical properties are as follows: tensile strength is 590 MPa, elongation is 27%; It is divided into two parts with widths of 844 mm and 451 mm, of which the 844 mm part is used as the raw material plate of the painted strip, and is produced by 9-pass rolling; the distribution of rolling passes from 1 to 9 is as follows: 3.0→2.64 →2.35→1.97→1.76→1.53→1.24→1.10→0.95→0.8 mm, the total reduction rate is 73.3%, the tensile strength of the cold-rolled raw material is 1000 MPa, the elongation is 6%, and the number of repeated bending is 4 ( R=2.5 mm), there is no brittle fracture and delamination, the bending degree is ≤25.4 mm / 2.4 m, the camber bending is ≤2.0 ...
Example Embodiment
[0041] Example 2
[0042] The chemical composition of the hot-rolled sheet raw material is as follows: C: 0.12%, Mn: 1.25%, Si: 0.013%, P: 0.015%, S: 0.004%, Als: 0.043%, and the rest are Fe and residual elements.
[0043] The dimensions of the hot-rolled steel sheet are as follows: thickness is 2.9 mm, width is 1295 mm; mechanical properties are as follows: tensile strength is 590 MPa, elongation is 27%; It is divided into two parts with widths of 844 mm and 451 mm, of which the 451 mm part is used as the raw material plate for the blue ribbon, and is produced by 9-pass rolling. The distribution of rolling passes from 1 to 9 is as follows: 2.9→ 2.64→2.35→1.97→1.76→1.53→1.24→1.10→0.95→0.8 mm, the total reduction rate is 72.4%; the tensile strength of the cold-rolled raw material is 1000 MPa, and the elongation is 6%. The number of repeated bending is 4 times (R=2.5 mm), there is no brittle fracture and delamination, the bending degree is less than or equal to 25.4 mm / 2.4 m, t...
Example Embodiment
[0045] Example 3
[0046] The chemical composition of the hot-rolled sheet raw material is as follows: C: 0.17%, Mn: 1.48%, Si: 0.024%, P: 0.018%, S: 0.003%, Als: 0.037%, and the rest are Fe and residual elements.
[0047] The dimensions of the hot-rolled steel sheet are as follows: thickness of 3.1 mm and width of 1295 mm. The mechanical properties are as follows: the tensile strength is 600 MPa, and the elongation is 26%; according to the equipment characteristics of the 1050 mm rolling mill, set as required, the hot-rolled sheets are cut before cold rolling, and the widths are 844 mm and 451 mm respectively. mm two parts, of which the 844 mm part is used as the raw material plate of the painted strip, and is produced by rolling in 9 passes; the distribution of rolling passes from 1 to 9 is as follows: 3.1→2.64→2.35→1.97→1.76→1.53→1.24→ 1.10→0.95→0.79 mm, the total reduction rate is 74.5%; the tensile strength of the cold-rolled raw material is 990 MPa, the elongation is 6%...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Width | aaaaa | aaaaa |
Tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap