Spraying process for laser-direct-structuring (LDS) antenna on outside surface of mobile phone plastic shell

A technology for outer surfaces and mobile phones, which is applied to the device for coating liquid on the surface, pretreatment surface, coating, etc. It can solve the problems of affecting the use of the antenna, the wear of the antenna body, and the complicated process, and achieves low cost and low labor intensity. , The effect of simple process

Active Publication Date: 2013-10-23
GUANGDONG GREEN PRECISION COMPONENTS CO LTD
View PDF5 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The authorized announcement number is: CN202084635U's utility model patent discloses a laser-formed multi-layer GPS antenna. Although the antenna body can be set on the mobile phone shell, the antenna body is set on the mobile phone shell, which is easy to use The main body of the antenna is worn out, which affects the use of the antenna
[0005] The application publication number is: CN102610899A, a laser forming antenna, which attaches a film-coated film to the surface of the laser-produced antenna, and th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spraying process for laser-direct-structuring (LDS) antenna on outside surface of mobile phone plastic shell
  • Spraying process for laser-direct-structuring (LDS) antenna on outside surface of mobile phone plastic shell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] see figure 1 , a flow chart of the LDS antenna spraying process on the outer surface of the mobile phone plastic case provided by the present invention, comprising the following steps:

[0039] S1. Provide an injection-molded mobile phone case;

[0040] S2. Irradiate the specified position on the outer surface of the plastic case of the mobile phone with a focused laser beam to activate the designated graphic part on the outer surface of the plastic case of the mobile phone and roughen the surface of the graphic part;

[0041] S3. Electroplating the metal film on the graphic part activated by the laser to realize the function of the antenna on the outer surface of the plastic case of the mobile phone;

[0042] S4. Spraying a primer on the outer surface of the mobile phone plastic case to cover the electroplated metal film on the outer surface of the mobile phone plastic case;

[0043] S5. Spraying a topcoat on the outer surface of the plastic case of the mobile phone ...

Embodiment 2

[0053] S1. Provide an injection-molded mobile phone case;

[0054] S2. Irradiate the specified position on the outer surface of the plastic case of the mobile phone with a focused laser beam to activate the designated graphic part on the outer surface of the plastic case of the mobile phone and roughen the surface of the graphic part;

[0055] S3. Electroplating the metal film on the graphic part activated by the laser to realize the function of the antenna on the outer surface of the plastic case of the mobile phone;

[0056] S4. Spraying a primer on the outer surface of the mobile phone plastic case to cover the electroplated metal film on the outer surface of the mobile phone plastic case;

[0057] S6, polishing step, after the primer is sprayed for the first time, the outer surface of the plastic case of the mobile phone is polished, and steps S4 and S6 are repeated until the outer surface of the plastic case of the mobile phone is polished after the primer is sprayed. Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a spraying process for a laser-direct-structuring (LDS) antenna on an outside surface of a mobile phone plastic shell. The spraying process comprises the following steps of providing the mobile phone plastic shell of injection molding; irradiating the specified position of the outside surface of the mobile phone plastic shell by using a focused laser beam to activate the specified graph part of the outside surface of the mobile phone plastic shell, and roughing the surface of the graph part; electroplating the graph part activated by laser with a metal film; spraying undercoat to be used for covering the electroplated metal film on the outside surface of the mobile phone plastic shell; and spraying finishing coat to be used for forming a formed part of the mobile phone plastic shell. The primary spraying thickness of the undercoat is 40-60mum, the spraying thickness of the finishing coat is 10-20mum, the undercoat is acrylic coating, and the finishing coat is ultraviolet (UV) coating. According to the spraying process for the LDS antenna on the outside surface of the mobile phone plastic shell disclosed by the invention, the height difference between the LDS antenna and the mobile phone plastic shell is effectively handled during the manufacturing process of a normal mobile phone plastic shell, and therefore, not only is the using function of the LDS antenna satisfied but also the appearance surface of the mobile phone plastic shell is not influenced. Meanwhile, a manufacturing process is simple and is good in effect.

Description

technical field [0001] The invention relates to the technical field of LDS antenna manufacturing and molding, in particular to the LDS antenna spraying process on the outer surface of a mobile phone plastic case. Background technique [0002] LPKF invented the laser structuring technology, LDS (Laser-Direct-structuring) laser direct structuring technology, the basic principle of this process is to selectively activate the surface of the injection molded part with laser before metallization, that is, to carry out the surface of the part Treatment to facilitate the process of metal deposition during electroplating. The plastic used for laser activation is a modified plastic. On the one hand, laser irradiation causes the organic metal compound to release metal particles, which is beneficial to metal deposition; on the other hand, it causes the breakage of the polymer molecular chain to roughen the surface. In this way, the surface of the modified plastic after laser activation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B05D1/36B05D1/38B05D3/00B05D3/06
Inventor 吴宝玉
Owner GUANGDONG GREEN PRECISION COMPONENTS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap