Gunning mix for repairing RH refractory brick

A technology of gunning material and refractory brick, which is applied in the field of gunning material for repairing refractory materials, can solve the problem of low service life and achieve the effect of shortening the maintenance cycle

Active Publication Date: 2013-11-27
宝武环科南京资源利用有限公司
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the technical problem that the current RH refractory bricks fall off and cause low service life, the present invention creatively discloses a gunning material for repairing RH refractory bricks. The wei

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0025] The periclase and sintered magnesia are respectively crushed according to the weight percentage of the raw material components in the table, and the particles with a particle size of less than or equal to 1cm are screened out as aggregates, and then the superfine silica powder, pure calcium aluminate cement, and trioxide The di-aluminum fine powder is weighed according to the weight percentage of the raw material components in the table, and the raw materials are mixed for 15-20 minutes to obtain the gunning material for RH refractory brick repair disclosed by the present invention.

[0026] The above mixing process is completed in the mixer.

[0027] Raw material composition (weight percent) Periclase (%) Sintered magnesia (%) Pure calcium aluminate cement (%) Silica superfine powder (%) Al 2 0 3 Micropowder (%) Example 1 35 32 24 6 3 Example 2 37 33 19 7 4 Example 3 40 35 13 8 4 Example 4 43 27 18 8 4 E...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to gunning mix for repairing refractory materials, in particular to gunning mix for repairing an RH refractory brick. In order to solve the technical problem of short service life of the RH refractory brick due to falling off in the prior art, the invention creatively discloses the gunning mix for repairing the RH refractory brick, the gunning mix comprises the following raw materials by weight: 35 to 45 % of periclase, 25 to 35 % of magnesite clinker, 13 to 24 % of pure calcium aluminate cement, 6 to 8 % of monox ultrafine powder and 3 to 4 % of aluminium oxide micro powder. The gunning mix disclosed by the invention has the advantages that after the repair of a magnesia-alumina spinel brick of the RH stove, the maintenance period is reduced from the original about 5 times per month to about 2 times per month caused by the cracking or the falling off of the magnesia-alumina spinel brick, and the maintenance cost is reduced; the average service life of the magnesia-alumina spinel brick is prolonged from the original 65 stove times on average to 98 stove times on average after the repairing of the magnesia-alumina spinel brick by the conventional spray-repairing method.

Description

technical field [0001] The invention relates to a gunning material for repairing refractory materials, in particular to a gunning material for repairing RH refractory bricks. [0002] Background technique [0003] The RH vacuum degassing refining method was jointly developed by Ruhrstahl and Heraeus, a subsidiary of Tyssen in Germany, and the vacuum molten steel circulation degassing method was successfully developed. The two companies used their company names This molten steel refining method is named RH vacuum degassing refining method. This method can further reduce [O] and [N] in molten steel, and is used for smelting steel with high cleanliness in molten steel composition. [0004] There are three main working conditions for the RH furnace insertion tube, one is to withstand the erosion and erosion of high-speed flow of air flow and molten steel; the other is the erosion and penetration of molten slag; the third is thermal spalling and structural spalling caused by int...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66
Inventor 王士青洪建国
Owner 宝武环科南京资源利用有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap