Method for preparing high-reflectance working mould of microprism reflecting films by utilizing ultrasonic electroforming

A technology of reflectivity and micro-prism, applied in the field of micro-prism, can solve the problem of difficulty in controlling the reflectivity of the working mode of the reflective film, and achieve the effect of convenient adjustment

Active Publication Date: 2013-12-11
福建跃发光新材料股份有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a method for preparing a high-reflective microprism reflective film working mold by ultrasonic electroforming for the existing microprisms, which are difficult to control the reflective degree of the reflective film working mold.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing high-reflectance working mould of microprism reflecting films by utilizing ultrasonic electroforming
  • Method for preparing high-reflectance working mould of microprism reflecting films by utilizing ultrasonic electroforming

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Preparation of electroforming solution: According to the total volume of the electroforming tank, weigh 450g of nickel sulfate, 50g of nickel chloride, 50g of boric acid, 0.07g of sodium lauryl sulfate, 0.5g of saccharin and 0.35g of 1,4-butynediol. g. Add deionized water to the electroforming tank, heat to 50°C, add weighed nickel sulfate and nickel chloride in turn, stir and keep warm for 4 hours. Take another beaker and rinse it with deionized water, dry it, add deionized water, stir and heat to boiling, add weighed boric acid and boil for 0.5h, then add sodium lauryl sulfate, wait until sodium lauryl sulfate is fully dissolved Finally, slowly pour it into the electroforming tank, and add saccharin and butynediol to the casting tank, then add deionized water until the electroforming tank is full, stir well, keep warm at 45°C for 12 hours, and measure with pH test paper Its pH value is adjusted to pH=4.2 with 30% sulfuric acid solution. Guaranteed quality-volume con...

Embodiment 2

[0028] Preparation of nickel sulfate electroforming solution: according to the total volume of the electroforming tank, first weigh 300g of nickel sulfate, 30g of nickel chloride, 30g of boric acid, 0.05g of sodium lauryl sulfate, 0.1g of saccharin and 1,4-butynedi Alcohol 0.2g. Add deionized water to the electroforming tank, heat to 55°C, add weighed nickel sulfate and nickel chloride in turn, stir and keep warm for 3.5h. Take another beaker and rinse it with deionized water, dry it, add deionized water, stir and heat to boiling, add weighed boric acid and boil for 40min, then add sodium lauryl sulfate, after sodium lauryl sulfate is fully dissolved , slowly pour it into the electroforming tank, and add saccharin and butynediol into the casting tank, then add deionized water until the electroforming tank is full, stir well, keep warm at 50°C for 10 hours, and measure the pH value with pH test paper pH value, adjusted to pH=4.2 with 30% sulfuric acid solution. Guaranteed qua...

Embodiment 3

[0034]Preparation of nickel sulfate electroforming solution: According to the total volume of the electroforming tank, first weigh 600g of nickel sulfate, 70g of nickel chloride, 75g of boric acid, 1g of sodium lauryl sulfate, 1g of saccharin and 0.5 g of 1,4-butynediol g. Add 1 / 2 volume of deionized water to the electroforming tank, heat to 60°C, add weighed nickel sulfate and nickel chloride in turn, stir and keep warm for 3 hours. Take another beaker and rinse it with deionized water, dry it, add deionized water, stir and heat to boiling, add weighed boric acid and boil for 50 minutes, then add sodium lauryl sulfate, after sodium lauryl sulfate is fully dissolved , slowly pour it into the electroforming tank, and add saccharin and butynediol to the casting tank, then add deionized water until the electroforming tank is full, stir well, keep it warm at 55°C for 8 hours, and measure it with pH test paper pH value, adjusted to pH=4.2 with 30% sulfuric acid solution. Guarante...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for preparing a high-reflectance working mould of microprism reflecting films by utilizing ultrasonic electroforming, and relates to microprisms. The method comprises the following steps of preparing electroforming solution, namely adding hot water into an electroforming tank, then adding nickel sulfate hexahydrate and nickel chloride in sequence, adding hot water into a container, then adding boric acid, then boiling the mixture, then adding lauryl sodium sulfate, pouring the solution into the electroforming tank after lauryl sodium sulfate is dissolved, adding saccharin and 2-butyne-1,4-diol into the electroforming tank, then injecting water to fully fill the electroforming tank and regulating the pH value to be 4.2; putting an anode nickel sheet into an anode basket, connecting the anode nickel sheet to an anode and connecting a nickel master mould to a cathode to carry out electroforming, and carrying out cathode demoulding to obtain the high-reflectance working mould of the microprism reflecting films. The method has the advantages that the ultrasonic parameters can be conveniently regulated by utilizing an ultrasonic washing machine during production; the coefficient of retroreflection of the microsized working mould of the microprism reflecting films can be controlled by regulating the ultrasonic parameters and the electroforming solution formula.

Description

technical field [0001] The invention relates to a microprism, in particular to a method for preparing a high-reflection microprism reflective film working mold by ultrasonic electroforming. Background technique [0002] Under the general mechanical stirring electroforming process conditions, electroforming nickel can only get a rough surface, and its retroreflective performance is not high. The micro-prism reflective film is made of dozens of micron-scale pyramid arrays, which cannot be mechanically polished after processing. The reflective film requires the working mold to have a high coefficient of retroreflection, that is, high reflectivity must be obtained after electroforming. [0003] Nickel is a common electroforming and electroplating material. It is widely used due to its good performance. Most of the research is on the formulation of plating solution, electroplating equipment, DC electroforming and coating appearance. There are few researches on ultrasonic electro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D1/06
Inventor 杨光皮钧
Owner 福建跃发光新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap