Ternary tobacco fiber paper filter rod made from composite aroma-enhancing plants and preparation method of filter rod

A technology of tobacco fiber and aroma plants, which is applied in the fields of tobacco, e-liquid filter, food science, etc., can solve the problem of not finding paper filter material, etc., and achieve excellent coke reduction and harm reduction functions, high adsorption and relative absorption. , the effect of improving wettability

Active Publication Date: 2013-12-18
CHINA TOBACCO GUANGDONG IND
View PDF9 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] At present, there is no new paper filter material that can comp...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ternary tobacco fiber paper filter rod made from composite aroma-enhancing plants and preparation method of filter rod
  • Ternary tobacco fiber paper filter rod made from composite aroma-enhancing plants and preparation method of filter rod
  • Ternary tobacco fiber paper filter rod made from composite aroma-enhancing plants and preparation method of filter rod

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] S1 prepares tobacco fiber filter element with tobacco leaves, tobacco stems and licorice

[0048] (1) Extracting tobacco leaves and tobacco stems

[0049] S11. extracting the tobacco raw material to obtain an extract of the tobacco raw material and a solid slag of the tobacco raw material;

[0050] In this example, tobacco stems and water were extracted at a mass ratio of 1:7 at a temperature of 60°C and an extraction time of 100 minutes, and the extraction was repeated three times. Tobacco stem extract and tobacco stem solid slag obtained after treatment.

[0051] Tobacco leaves and water were extracted at a mass ratio of 1:10, the extraction temperature was 80°C, and the extraction time was 60 minutes, and the extraction was repeated three times. Tobacco leaf extract and tobacco leaf solid slag obtained after treatment.

[0052] S12. Refining the solid slag of tobacco raw materials to obtain tobacco fiber pulp; commercially available lignocellulosic pulp. The r...

Embodiment 2

[0060] S1. Preparation of grooved tobacco fiber filter rods from tobacco powder, tobacco fragments and tobacco stalks

[0061] S11. extracting the raw material to obtain the extract of the raw material and the solid slag of the raw material;

[0062] In this example, tobacco stems and water were extracted at a mass ratio of 1:7 at a temperature of 60°C and an extraction time of 100 minutes, and the extraction was repeated three times. Tobacco stem extract and tobacco stem solid slag obtained after treatment.

[0063] Tobacco leaves and water were extracted at a mass ratio of 1:10, the extraction temperature was 80°C, and the extraction time was 60 minutes, and the extraction was repeated three times. Tobacco leaf extract and tobacco leaf solid slag obtained after treatment.

[0064] According to the mass ratio of solid to liquid of 1:10, the smoke fragments and water were separated, the extraction temperature was 75°C, and the extraction time was 60 minutes. The smoke chip ...

Embodiment 3

[0072] S1. Preparation of grooved tobacco fiber filter rods from tobacco dust, tobacco fragments and tobacco stems

[0073] S11. extracting the raw material to obtain the extract of the raw material and the solid slag of the raw material;

[0074] In this example, tobacco stems and water were extracted at a mass ratio of 1:7 at a temperature of 60°C and an extraction time of 100 minutes, and the extraction was repeated three times. Tobacco stem extract and tobacco stem solid slag obtained after treatment.

[0075] Tobacco leaves and water were extracted at a mass ratio of 1:10, the extraction temperature was 80°C, and the extraction time was 60 minutes, and the extraction was repeated three times. Tobacco leaf extract and tobacco leaf solid slag obtained after treatment.

[0076] According to the mass ratio of solid to liquid of 1:10, the smoke fragments and water were separated, the extraction temperature was 75°C, and the extraction time was 60 minutes. The smoke chip ext...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of tobacco filter rods, and discloses a ternary tobacco fiber paper filter rod made from composite aroma-enhancing plants. The filter rod is composed of filter elements and forming paper wrapping the filter elements, the filter elements include two sections of tobacco fiber paper filter elements and a natural aromatic plant filter between the two sections of tobacco fiber paper filter elements, and the tobacco fiber paper filter elements are formed by rolling of paper fibers. The paper filter element has higher capabilities of removing tar and nicotine than an acetate fiber filter rod, raw materials are from tobacco or other natural plants, color, seen by consumers, of the filter rod is identical to that of cigarette tobacco shreds, strong natural tobacco material quality is provided, reasonable addition of the aroma-enhancing plants adds rich flavors to tar and harm reduced cigarette smoke, and a new research direction is guided to the technical field of the filter rods.

Description

technical field [0001] The invention relates to the technical field of cigarette filter sticks, in particular to a three-element tobacco fiber paper filter stick compounded with flavoring plants and a preparation method thereof. Background technique [0002] Cigarette smoke contains particles, commonly known as tar. Tar contains a large number of chemical components, 4000 to 5000 kinds, all of which are products of incomplete combustion of tobacco. In addition to tar, cigarette smoke contains other substances, such as the "steam" or "gas" phase, which also includes volatile tobacco combustion substances such as acetaldehyde and other low molecular weight components. Other phases in cigarette smoke, such as the "semi-volatile" phase, which includes many combustion substances, are equivalent to particulate and vapor phases. [0003] Cigarette filter rods can filter smoke components. Cigarette filter rods are composed of filter elements and molding paper. The filter ele...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A24D3/02A24D3/04A24D3/10A24D3/14
CPCA24D3/10
Inventor 邵干辉黄春晖赵瑞峰夏国聪黄宪忠何艳明陶红胡静
Owner CHINA TOBACCO GUANGDONG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap