Degradable vegetable fiber daily utensils and manufacturing method thereof

A plant fiber and manufacturing method technology, applied in the direction of coating, etc., can solve the problems of papermaking waste water, large food consumption, and destruction of green resources, and achieve the effects of reducing production costs, increasing water resistance, and low total migration

Inactive Publication Date: 2016-07-06
ANHUI YIKE ENVIRONMENTAL PROTECTION TECH
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The degradable daily utensils currently on the market have: grain tableware with the shortest decomposition period, which has the disadvantage of high production cost, consumes a large amount of grain, and is prone to mold; paper tableware with a long decomposition period has the disadvantage that the paper tableware is degraded during the degradation process. Harmful gases will be produced, which will pollute the atmosphere, and all cardboard must be wood pulp paper made by cutting down trees, and other papers cannot be used. Cutting down trees will destroy green resources, and papermaking will produce waste water, polluting the environment, Therefore, in essence, this is not a fundamental method to solve the problem; the most difficult to decompose is the degradable plastic tableware. Due to the limitations of the plastic material itself, whether it is biodegradation or photosensitive degradation, it is only a large piece of plastic. The point where it is broken into small pieces does not significantly improve the elimination of white pollution and the deterioration of the soil

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Degradable vegetable fiber daily utensils and manufacturing method thereof
  • Degradable vegetable fiber daily utensils and manufacturing method thereof
  • Degradable vegetable fiber daily utensils and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 1) Take 55 grams of 80-mesh plant fiber powder composed of bamboo powder, straw powder and tea powder and mix with 45 grams of polylactic acid resin, stir at 4500 rpm for 3 minutes at high speed, then put the above mixture into a high-temperature and high-pressure mold for molding, Obtain a plant fiber shell with a temperature of 120°C and a pressure of 39209.8kPa;

[0024] 2) grinding the surface of the plant fiber shell obtained in step 1);

[0025] 3) spray water-based polyurethane on the surface of the plant fiber shell in step 2);

[0026] 4) After spraying, the product is baked in an oven at 120°C for 20-30 minutes, and the degradable plant fiber daily utensils are obtained.

Embodiment 2

[0028] 1) Take 50 grams of 120-mesh plant fiber powder composed of bamboo powder, rice bran powder and tea powder, 44.5 grams of polylactic acid resin, 5 grams of water, 0.03 g of zinc stearate and 0.47 g of coloring agent, mix at a high speed of 5000 rpm Stir for 5 minutes, then put the above mixture into a high-temperature and high-pressure mold for molding to obtain a plant fiber shell at a temperature of 160°C and a pressure of 50176kPa;

[0029] All the other steps are the same as in Example 1.

Embodiment 3

[0031] 1) Mix 70 grams of 160-mesh plant fiber powder composed of bamboo powder and tea powder, 25 grams of polylactic acid resin, 4.5 grams of water, 0.05 g of zinc stearate and 0.45 g of coloring agent, and stir at a high speed of 5000 rpm for 5 minutes , and then put the above mixture into a high-temperature and high-pressure mold for molding to obtain a plant fiber shell at a temperature of 180°C and a pressure of 73725.4kPa;

[0032] All the other steps are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention proposes degradable plant fiber daily utensils and a manufacturing method thereof, which consists of 50-70% plant fiber powder, 25-45% polylactic acid resin, 0-8% water, and 0-0.05% release agent and 0-0.5% colorant, and the plant fiber powder is one or more mixtures of bamboo powder, straw powder, rice bran powder or tea powder. The degradable plant fiber daily utensil of the invention has the advantages of complete degradability, no environmental pollution, low cost and the like.

Description

technical field [0001] The invention relates to a degradable plant fiber daily vessel and a manufacturing method thereof. Background technique [0002] Daily utensils such as tableware and flower pots are the necessities of people's life. In recent years, with the rapid development of the economy, the pace of people's life is also accelerating, and the fast food industry has been able to develop sequentially, which has also caused the market's increasing demand for fast food tableware. [0003] The degradable daily utensils currently on the market have: grain tableware with the shortest decomposition period, which has the disadvantage of high production cost, consumes a large amount of grain, and is prone to mold; paper tableware with a long decomposition period has the disadvantage that the paper tableware is degraded during the degradation process. Harmful gases will be produced, which will pollute the atmosphere, and all cardboard must be wood pulp paper made by cutting ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L97/02C08L67/04C08K3/34C08K5/098C08J7/04
Inventor 谢大兵
Owner ANHUI YIKE ENVIRONMENTAL PROTECTION TECH