Calcium carbonate nano ink

A calcium carbonate, nano technology, applied in the field of ink, can solve the problem of rare practical application, achieve the effect of good dispersion and cost reduction

Inactive Publication Date: 2014-03-19
SUZHOU YIHENG PRINTING
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the printing industry, the application of nanotechnology is mainly manifested in the fields of printing ink, printing equipment and packaging printing, etc. However, the research on nano-ink is mostly in the theoretical stage, and there are not many practical applications.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The present invention has prepared a calcium carbonate nano-ink, which is composed of the following raw materials in parts by weight: 37 parts of titanium white, CaCO with an average particle diameter of 100nm 3 13 parts, maleic anhydride rosin 10 parts, epoxy resin 21 parts, acrylic resin 7 parts, isopropanol 3 parts, calcium stearate 1 part.

Embodiment 2

[0014] The present invention has prepared a calcium carbonate nano-ink, which is composed of the following raw materials in parts by weight: 40 parts of ultramarine, CaCO with an average particle diameter of 100nm 3 19 parts, maleic anhydride rosin 15 parts, epoxy resin 26 parts, acrylic resin 8 parts, isopropanol 5 parts, calcium stearate 2 parts.

Embodiment 3

[0016] The present invention has prepared a calcium carbonate nano-ink, which is composed of the following raw materials in parts by weight: 45 parts of Hansa yellow, CaCO with an average particle diameter of 100nm 3 26 parts, maleic anhydride rosin 20 parts, epoxy resin 29 parts, acrylic resin 10 parts, isopropanol 7 parts, calcium stearate 2 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a calcium carbonate nano ink which is prepared from the following raw materials in parts by weight: 37-45 parts of pigment, 13-26 parts of CaCO3 with the average particle size of 100nm, 10-20 parts of maleic anhydride rosin, 21-29 parts of epoxy resin, 7-10 parts of acrylic resin, 3-7 parts of isopropanol and 1-2 parts of calcium stearate. The ink has the advantages of favorable stability, low pigment consumption, high covering power, full color, clear printed image and long service life, and is suitable for industrial production.

Description

technical field [0001] The invention relates to the technical field of ink, in particular to a nanometer ink. Background technique [0002] Ordinary ink is a uniform mixture composed of pigments (including colored pigments and fillers), linking materials, mineral oil, additives, etc. It can be printed and dried on the printed object. It has a color and a certain fluidity. Siamese. The composition of nano-ink is basically the same as that of ordinary ink. The biggest difference between them is the size of the pigment particles. The pigment particle size of ordinary ink is micron level, while the pigment particle size of nano ink is nano level, the size difference between the two is about 1000 times, and the fineness of the ink made in this way has been greatly improved. The fineness and purity of ink have a great influence on the quality of printed matter. The smaller the pigment particles, the higher the fineness of the ink, and the clearer, fuller and more powerful the d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/10C09D11/102C09D11/08C09D11/107
Inventor 陈明
Owner SUZHOU YIHENG PRINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products