Special composite emulsifier for wax emulsion, and preparation method thereof

A compound emulsifier and wax emulsion technology, which is applied in the field of wax emulsion special compound emulsifier and its preparation, can solve the problems of not being able to emulsify well

Inactive Publication Date: 2014-04-02
山东力厚轻工新材料有限公司
View PDF8 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this emulsifier can only be used for the emulsification of paraffin wax, and cannot emulsify other types of wax, such as palm wax, beeswax, rice bran, candelilla wax, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Add 37.5kg of Pingpingjia O-10, 10kg of Pingpingjia O-25, 24kg of stearic acid and 28.5kg of AEO-9 into the reaction kettle in turn, heat up to 60-70°C until the materials are completely melted, and then stir until uniform Discharging obtains the special compound emulsifier of 100kg wax emulsion.

[0013] Add 8.2 kg of the composite emulsifier to 100 kg of paraffin, heat to 85° C., and slowly add 108 kg of 90° C. hot water after stirring to obtain a white translucent emulsion with a solid content of 50%.

[0014] Add this composite emulsifier 9kg in 100kg palm wax, be heated to 95 ℃, slowly add 95 ℃ hot water 255kg after stirring, obtain the light gray transparent emulsion that solid content is 30%.

Embodiment 2

[0016] Add 40kg of Pingpingjia O-10, 10kg of Pingpingjia O-25, 21kg of stearic acid and 29kg of AEO-7 into the reaction kettle in turn, heat up to 60-70°C until the materials are completely melted, then stir until uniform and then discharge Obtain the compound emulsifier special for 100kg wax emulsion.

[0017] Add 8.5 kg of the composite emulsifier to 100 kg of beeswax, heat to 85° C., and slowly add 108 kg of 90° C. hot water after stirring to obtain a slightly yellow translucent emulsion with a solid content of 50%.

[0018] Add 8 kg of this composite emulsifier in 100 kg montan wax, heat to 95 ° C, and slowly add 108 kg of 95 ° C hot water after stirring to obtain a brown transparent emulsion with a solid content of 50%.

Embodiment 3

[0020] Add 35kg of Pingpingjia O-10, 10kg of Pingpingjia O-25, 25kg of stearic acid, 18kg of AEO-9 and 12kg of AEO-7 into the reaction kettle in turn, heat up to 60-70°C until the materials are completely melted, and then stir until uniform Can discharge and obtain 100kg wax emulsion special composite emulsifier.

[0021] Add 10 kg of the composite emulsifier to 100 kg of polyethylene wax, heat to 115° C., and slowly add 220 kg of 100° C. hot water after stirring to obtain a white emulsion with a solid content of 33%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides a special composite emulsifier for a wax emulsion. The special composite emulsifier is characterized by comprising, by weight, 45-50 parts of peregal, 20-25 parts of stearic acid, and 25-30 parts of fatty alcohol polyoxyethylene ether. The process comprises: sequentially adding peregal, stearic acid and fatty alcohol polyoxyethylene ether to a reaction kettle, heating to achieve a temperature of 60-70 DEG C until completely melting the material, and stirring to achieve a uniform state so as to discharge the material. According to the present invention, during preparation of various wax emulsions, the emulsifier having the amount of 8-10% of the mass of wax and the wax are co-melted and then uniformly stirred, and hot water with a temperature of 90-95 DEG C is added until the solid content is 50% so as to obtain the corresponding wax emulsion, or deionized water can be added according to requirements so as to adjust the wax emulsion content to 5-50% and the like. The special composite emulsifier can be provided for emulsifying paraffin wax, polyethylene wax, palm wax, montan wax, beeswax, rice bran wax, candelilla wax, shellac wax, and other types of waxes, such that material preparation of wax emulsion manufacturers is simply, and the prepared emulsion is translucent, has blue light , and has characteristics of good stability and small particle size; and the emulsifying system is consistent, such that various wax emulsions can be compounded according to any ratios without generation of phenomena such as precipitation, flocculation, layering and the like, and the special composite emulsifier can be conveniently used in various fields.

Description

technical field [0001] The invention relates to a special composite emulsifier for wax emulsion and a preparation method thereof, belonging to the technical field of chemical industry related to the preparation of wax emulsion. Background technique [0002] Wax emulsion is a water-containing uniform fluid formed by wax under the action of emulsifier and mechanical force. It is easy to compound with other emulsions or diluted with water. It has the advantages of safety, high efficiency, economy and environmental protection. It is a widely used Chemical Products. For example, low-content wax emulsions can generally be used in latex products in the pharmaceutical industry and agricultural fruit preservation, etc., while high-concentration wax emulsions can generally be used in papermaking sizing agent coating agents, concrete curing agents, ink dispersants, leather finishing agents , automotive and floor brighteners and wood-based panel waterproofing agents and other fields. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L91/06C08L23/06C08L71/02C08J3/03C08J3/05C08K5/09
Inventor 冯练享白清泉
Owner 山东力厚轻工新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com