Metal polishing agent

A polishing agent and metal technology, which is applied in the field of metal surface treatment, can solve the problems of incomplete cleaning, high labor intensity, low unit output, etc., and achieve stable polishing effect, good polishing effect and improved brightness

Inactive Publication Date: 2014-04-02
黔东南州九黎苗妹工艺品有限公司
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing polishing agents have problems such as quick rust return, narrow applicable metal types, and incomplete cleaning. Many polishing agents contain fluorine compounds or phosphorus-containing compounds, which pollute the environment.
Moreover, the commonly used polishing agents on the market are mainly solid, that is, polishing paste. This product is often operated intermittently in use, with high labor intensity, low unit output, and insufficient surface treatment for fine structures.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Diethylene glycol butyl ether: 4 parts, benzyl alcohol: 6 parts, disodium aminotriacetate: 2 parts, sodium nitrite: 3 parts, sodium tallow fatty acid: 1 part, surfactant: 1 part by weight percentage , Corrosion inhibitor: 0.3 parts, antirust agent: 0.2 parts and the balance is water, put it into the reaction kettle, and stir it at 45°C for 2 hours.

Embodiment 2

[0021] Diethylene glycol butyl ether: 5 parts, benzyl alcohol: 5 parts, disodium aminotriacetate: 3 parts, sodium nitrite: 2 parts, sodium tallow fatty acid: 2 parts, surfactant: 1.5 parts by weight percentage , Corrosion inhibitor: 0.4 parts, antirust agent: 0.3 parts and the balance is water, put into the reaction kettle, and stir at 45°C for 2 hours.

Embodiment 3

[0023] Weigh Diethylene Glycol Butyl Ether: 6 parts, Benzyl Alcohol: 4 parts, Disodium Aminotriacetate: 4 parts, Sodium Nitrite: 1 part, Sodium Tallow Fatty Acid: 3 parts, Surfactant: 2 parts , Corrosion inhibitor: 0.5 part, antirust agent: 0.4 part and the balance is water, put it into the reaction kettle, and stir it at a constant temperature of 45 ℃ for 2 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a metal polishing agent which is characterized by comprising the following components in percentage by weight: 4%-8% of diethylene glycol butyl ether, 3%-6% of benzyl methanol, 2%-5% of disodium aminotriacetate, 1%-3% of sodium nitrite, 1%-3% of tallow fatty acid sodium, 1%-2.5% of a surfactant, 0.3%-0.8% of a corrosion inhibitor, 0.2%-0.5% of an anti-rust agent and the balance amount of water. The metal polishing agent has the characteristics of wide application range, stable polishing effect, convenience in use, high efficiency and the like.

Description

technical field [0001] The invention relates to the field of metal surface treatment, in particular to a metal polishing agent. Background technique [0002] After metal parts are processed, there is usually a layer of oil or other chemical agents attached to the surface. After a period of use, the metal parts will be corroded by the use environment, and rust will appear on the surface. Therefore, many metal parts need a certain brightness. Polishing treatment is an important part of parts processing. Polishing agents are often added during the polishing process to improve the brightness of metal parts and clean the metal surface. However, the existing polishing agents have problems such as quick rust return, narrow applicable metal types, and incomplete cleaning. Many polishing agents contain fluorine compounds or phosphorus-containing compounds, which pollute the environment. Moreover, the commonly used polishing agents on the market are mainly solid, that is, polishing p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F3/00
Inventor 张聪聪
Owner 黔东南州九黎苗妹工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products