Ink

A technology of ink and epoxy resin, applied in ink, household utensils, applications, etc., can solve the problems of ordinary inks such as difficulty in coating, poor adhesion, and high rate of defective products, and achieve improved adhesion, fine paint, and convenient preparation Effect

Active Publication Date: 2014-04-23
威海凯虹精密化工有限公司
View PDF2 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]Thermoplastic elastomers such as TPU have good appearance texture and mild touch, and have been widely used in the casings of a large number of electronic products such as mobile phones and computers. Difficult to paint on material, poor adhesion
The traditional method is to print the ink on the primer first, then spray a layer of elastomer after drying, so the rate of defective products is high
On the other hand, people have higher and higher requirements for products such as abrasion resistance and solvent resistance. While ensuring excellent adhesion of the product, they must also have good abrasion resistance and solvent resistance. inks that do not yet meet these requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment provides an ink, based on the total weight of the ink, the ink is prepared from the following percentages of components: polyurethane modified epoxy resin, 5%; polyester resin, 40%; polyether modified Silicone defoamer, 1%; nano aluminum oxide emulsion, 5%; cyclohexanone, 49%.

Embodiment 2

[0029] This embodiment provides an ink, based on the total weight of the ink, the ink is formulated from the following percentage components: phenolic modified epoxy resin, 30%; polyester resin, 10%; polyether modified Silicone defoamer, 1%; nano-aluminum oxide emulsion, 12%; butyl acetate, 47%.

Embodiment 3

[0031] This embodiment provides an ink, based on the total weight of the ink, the ink is formulated with the following percentages: polyurethane modified epoxy resin, 15%; polyester resin, 25%; pigment, 8% ; Dispersant, 1%; Polyether modified silicone defoamer, 1%; Nano aluminum oxide emulsion, 8%; Ethylene glycol monobutyl ether, 42%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides ink. Based on the total weight of the ink, the ink is mainly prepared from the following ingredients in percentage by weight: 5-30% of epoxy resin, 10-40% of polyester resin, 0.5-2% of defoamer, 5-20% of wear-resistant emulsion and 40-60% of solvent. According to actual needs, the ink provided by the invention can also contain the following ingredients in percentage by weight: 0.5-2% of pigment and 0.5-2% of dispersant. The ink provided by the invention has relatively strong adhesion and wear resistance and good chemical resistance, and the resins and the solvent are relatively environmental-friendly, so that the ink is particularly applicable to an elastomer surface and has a good application prospect.

Description

technical field [0001] The invention relates to an ink, in particular to an ink suitable for the surface of an elastic body. Background technique [0002] Thermoplastic elastomers such as TPU have good appearance texture and mild touch, and have been widely used in the casings of a large number of electronic products such as mobile phones and computers. However, ordinary inks are difficult to coat on such materials and have poor adhesion. The traditional method is to print the ink first on the primer, and then spray a layer of elastomer after drying, so the rate of defective products is high. On the other hand, people have higher and higher requirements for products such as abrasion resistance and solvent resistance. While ensuring excellent adhesion of the product, they must also have good abrasion resistance and solvent resistance. The ink can not meet these requirements. Contents of the invention [0003] In order to overcome the above-mentioned problems in the prior ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/104C09D11/102
Inventor 邵晓光沈朝阳李其勇周彦伯
Owner 威海凯虹精密化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap