Self-cleaning nano-coating protective film and preparation method thereof

A nano-coating and self-cleaning technology, used in coatings, film/flake adhesives, adhesives, etc., can solve the problems of static electricity accumulation, insufficient adhesion, poor anti-pollution performance, etc. Excellent, good anti-sand dust effect, low production cost effect

Inactive Publication Date: 2014-04-23
NALI OPTICAL MATERIAL DONGGUAN
View PDF4 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing technology for manufacturing optical films mostly uses PET substrates, and then coats a layer of hardened coating on its surface. This coating is mostly acrylic resin materials, and acrylic resin materials need ultraviolet light to be cured. The prepared optical films have The disadvantages are: 1. The adhesion between the PET substrate and the acrylic resin material is often not strong enough, and it has a lot to do with the surface treatment of the PET substrate.
2. UV curing requires the support of ultraviolet light equipment, and the commonly used high-pressure mercury lamp not only has a low utilization rate, but also emits only 30% of the output power of ultraviolet light, and is easy to cause UV pollution. Protective equipment must be used when using
4. The prepared protective film is easy to accumulate static electricity and has poor anti-pollution performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-cleaning nano-coating protective film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A method for preparing a self-cleaning nano-coating protective film, comprising the following processing steps:

[0047] The first step, preparing a nano-coating with self-cleaning function;

[0048] In the second step, the above-mentioned nano-coating is coated on the PET substrate by using a micro-groove anilox roller. The angle is 30 degrees; the coating line speed of the micro concave anilox roller is 10m / min;

[0049] The third step is to adopt the thermal curing method of oven heating, the heating temperature is 50 ℃, and the heating time is 3 minutes, so that a layer of nano film is formed on the PET substrate;

[0050] The fourth step is to coat the adhesive on the other surface of the PET base material, and heat and cure in an oven. The baking temperature of the oven is 130°C, and the baking time is 3 minutes, and then the PET release layer is pasted on the adhesive layer. . The adhesive is a silicone adhesive. The coating thickness of the adhesive is 10 μm...

Embodiment 2

[0062] A method for preparing a self-cleaning nano-coating protective film, comprising the following processing steps:

[0063] The first step, preparing a nano-coating with self-cleaning function;

[0064] The second step is to apply the above-mentioned nano-coating on the PET substrate with a micro-grained anilox roller. The angle is 30 degrees; the coating line speed of the micro concave anilox roller is 10m / min;

[0065] The third step is to use the thermal curing method of oven heating, the heating temperature is 55 ° C, and the heating time is 2.5 minutes, so that a layer of nano film is formed on the PET substrate;

[0066] The fourth step is to coat the adhesive on the other surface of the PET base material, heat and cure in an oven, the baking temperature of the oven is 150°C, and the baking time is 2.5 minutes, and then paste the PET release layer on the adhesive layer superior. The adhesive is a silicone adhesive. The coating thickness of the adhesive is 15 μm, ...

Embodiment 3

[0078] A method for preparing a self-cleaning nano-coating protective film, comprising the following processing steps:

[0079] The first step, preparing a nano-coating with self-cleaning function;

[0080] In the second step, the above-mentioned nano-coating is coated on the PET substrate by using a micro-groove anilox roller. The angle is 30 degrees; the coating line speed of the micro concave anilox roller is 15m / min;

[0081] The third step is to adopt the thermal curing method of oven heating, the heating temperature is 60 ℃, and the heating time is 2 minutes, so that a layer of nano film is formed on the PET substrate;

[0082] The fourth step is to coat the adhesive on the other surface of the PET base material, and heat and cure in an oven. The baking temperature of the oven is 160°C, and the baking time is 2 minutes, and then the PET release layer is pasted on the adhesive layer. . The adhesive is a silicone adhesive. The coating thickness of the adhesive is 20 μm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of optical protective films, and in particular relates to a self-cleaning nano-coating protective film and a preparation method thereof. The preparation method comprises the following processing steps: I, preparing a nano-paint having a self-cleaning function; II, coating a PET (Polyethylene Terephthalate) substrate with the nano-paint by using a micro-concave anilox roller; III, forming a layer of nanofilm on the PET substrate by adopting a heat curing way; and IV, coating silica gel and sticking a stripping layer. The PET substrate is coated with the nano-paint having the self-cleaning function by using the micro-concave anilox roller, and the PET substrate is dried and cured in a drying oven, so that the nano-coating having a self-cleaning function is formed on the surface of the PET substrate. The self-cleaning nano-coating protective film can be used by peeling the PET stripping layer off and sticking an adhesive layer to a screen. The self-cleaning nano-coating protective film is convenient to use and easy to operate.

Description

technical field [0001] The invention relates to the technical field of optical protective films, in particular to a self-cleaning nano coating protective film and a preparation method thereof. Background technique [0002] With the rapid development of electronic product technology, more people have electronic products. Protective films can not only beautify electronic products, but also prolong the life of electronic products. Therefore, more consumers are willing to use protective films. [0003] With the development of smart mobile devices, optical film manufacturing technology has also been greatly improved. The existing technology for manufacturing optical films mostly uses PET substrates, and then coats a layer of hardened coating on its surface. This coating is mostly acrylic resin materials, and acrylic resin materials need ultraviolet light to be cured. The prepared optical films have The disadvantages are: 1. The adhesion between the PET substrate and the acrylic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/02C08J7/06C09D1/00C09D7/12
Inventor 陈克勇朱文峰杨忠芝齐东东虞礼森
Owner NALI OPTICAL MATERIAL DONGGUAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com