A heavy metal polluted soil stabilization agent and its preparation method and application

A technology of polluted soil and heavy metals, applied in the restoration of polluted soil, chemical instruments and methods, applications, etc., can solve the problems of high cost and unsustainable stabilization effect, and achieve low cost, long-term effective stabilization effect, and use simple effect

Active Publication Date: 2016-03-09
ENVIRONMENTAL SCI RES & DESIGN INST OF ZHEJIANG PROVINCE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The invention provides a heavy metal-contaminated soil stabilizing agent and its preparation method and application, which solves the problems of high cost of the heavy metal-contaminated soil stabilizing agent and unsustainable stabilization effect at present.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A heavy metal polluted soil stabilization agent and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] according to figure 1The process flow shown is to obtain a certain farmland soil, which is polluted by lead. The lead content in the surface soil is 381-1129mg / kg, and the lead concentration leached by the TCLP method is 5.98mg / L. After analysis, the pollutants in the soil are relatively simple and easy to stabilize. The ratio of the stabilizer agent used is 60% bone meal, 30% shell meal, and 10% biochar, and the amount of stabilizer agent added to the soil is 5%. The stabilizing agent is evenly distributed to the soil twice by hand, and after each distribution, the contaminated soil is loosened several times with a rotary tiller to achieve stabilization. Also compared with 5% phosphate stabilized and 5% lime stabilized samples.

[0047] Table 1 Concentration of Pb in TCLP leach solution before and after stabilization

[0048]

Embodiment 2

[0050] according to figure 1 The process shown in the figure shows that the polluted soil in a lead-zinc mining area is obtained. The pollutants in the surface soil are mainly lead, cadmium and zinc, and their concentrations are 637-3128mg / kg, 3.6-17.5mg / kg and 684-2873mg / kg respectively. . After analysis, the types of pollutants in the soil are relatively complex, and the pollution degree is relatively high. The ratio of the stabilizer agent used is 50% bone meal, 40% shell meal, and 10% biochar. The amount of stabilizer agent added to the soil is 8 %. Using the method of ex-situ stabilization, dry the soil and mix it with the stabilizer in a mixer, adjust the moisture content to 10-20%, and maintain it at room temperature for 7-14 days to achieve the best stabilization effect. At the same time, it was compared with the sample stabilized with 5% phosphate. Table 1 Concentration of heavy metals in TCLP leachate before and after stabilization

[0051]

[0052] Acc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses a stabilizing agent for heavy metal contaminated soil and a preparation method and application thereof, and the stabilizing agent comprises the following raw materials: by weight, 20-60% of bone meal; 10-30% of biochar and 20-70% of calcined shell powder. The preparation method is as follows: (1) drying biomass in air and grinding into particles smaller than 60 meshes, cracking in a cracking furnace at 400-800 DEG C for 6-8 hours to obtain the biocar; calcining shell powder with the particle size below 20 meshes in a high temperature furnace at 800-1000 DEG C for 2 to 4 hours, naturally cooling to room temperature to obtain the calcined shell powder; and (2) proportionally mixing the biocar, the calcined shell powder and the bone meal evenly to obtain the stabilizing agent. The stabilizing agent compounding the three components in accordance with a specific proportion solves the problem of high cost, undurable stabilization effect and the like of stabilizing agents for the heavy metal contaminated soil in the prior art.

Description

technical field [0001] The invention relates to a method for harmless treatment of heavy metal polluted soil, in particular to a heavy metal polluted soil stabilizing agent and its preparation method and application. Background technique [0002] Due to its long-term latency, concealment, and irreversibility, soil heavy metal pollution has become one of the major environmental problems to be solved in my country. The discharge of "three wastes" from mining, smelting, electroplating, chemical, electronics, leather and other industries, as well as the unreasonable application of pesticides and fertilizers will lead to heavy metal pollution in the soil. Heavy metals in the soil will not only affect the yield and quality of crops, but also accumulate and amplify along with water and air circulation and food chains, endangering human health. [0003] Heavy metal stabilization technology is a disposal technology applied to heavy metal hazardous waste. Through the addition of stab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09K17/06B09C1/08C09K101/00
Inventor 张弛顾震宇裘知韦彦斐钟重王睿
Owner ENVIRONMENTAL SCI RES & DESIGN INST OF ZHEJIANG PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap