A technology of insulating coatings and high-voltage wires, applied in anti-corrosion coatings, coatings, etc., can solve the problems of poor cold resistance, heat resistance and corrosion resistance, and weather resistance needs to be further improved to achieve excellent corrosion resistance and good wear resistance sexual effect

Inactive Publication Date: 2014-05-07
NANTONG TIANMING PHOTOELECTRIC TECH
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, ordinary coatings for high-voltage wires have good insulation performance, but their cold resistance, heat resistance and corrosion resistance are not good, and the weather resistance needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Insulating paint for high-voltage wires, including the following raw materials in parts by mass: 55 parts of polytetrafluoroethylene emulsion, 20 parts of silicon micropowder, 10 parts of titanium dioxide, 0.5 parts of polyethylene wax, 0.6 parts of polyoxyethylene polyoxypropylene pentaerythritol ether, 15 parts of glycerol, 16 parts of butyl acetate, and 80 parts of water.

[0015] According to the mass ratio, the components are mixed and stirred evenly to obtain the finished product, and the performance of the finished product is tested, and the test results are shown in Table 1.

Embodiment 2

[0017] Insulating paint for high-voltage wires, including the following raw materials in parts by mass: 60 parts of polytetrafluoroethylene emulsion, 25 parts of silicon micropowder, 13 parts of titanium dioxide, 1 part of polyethylene wax, 0.8 parts of emulsified silicone oil, 20 parts of glycerol, 18 parts of butyl acetate, 90 parts of water.

[0018] The preparation method of this embodiment is the same as that of Example 1, and the performance of the finished product is tested, and the test results are shown in Table 1.

Embodiment 3

[0020] Insulating paint for high-voltage wires, including the following raw materials in parts by mass: 56 parts of polytetrafluoroethylene emulsion, 22 parts of silicon micropowder, 12 parts of titanium dioxide, 0.6 part of polyethylene wax, 0.7 part of polyoxyethylene polyoxypropylene pentaerythritol ether, 18 parts of glycerol, 17 parts of butyl acetate, and 88 parts of water.

[0021] The preparation method of this embodiment is the same as that of Example 1, and the performance of the finished product is tested, and the test results are shown in Table 1.

[0022]

[0023] The coating obtained in Examples 1-3 is subjected to a performance test, and the coating is a dry film with a thickness of 25 μm. The results are shown in Table 1:

[0024] Table 1 Performance test data

[0025] performance Example 1 Example 2 Example 3 Adhesion 5B 5B 5B Alkali resistance, 60% NaOH solution 500h no change 500h no change 500h no change Acid resista...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an insulating coating special for high-voltage lines. The insulating coating is prepared from the following raw materials in parts by weight: 55-60 parts of polytetrafluoroethylene emulsion, 20-25 parts of silica powder, 10-13 parts of titanium dioxide, 0.5-1 part of polyethylene wax, 0.6-0.8 part of defoamer, 15-20 parts of glycerol, 16-18 parts of n-butyl acetate and 80-90 parts of water. The insulating coating has excellent non-corrosibility and high and low temperature resistance in addition to excellent insulation property, and the coating has excellent wear resistance.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a special insulating coating for high-voltage electric wires. Background technique [0002] Special coatings for high-voltage wires play an important role in the field of coatings, effectively protecting the safety of high-voltage lines, prolonging the life of lines, and providing security for people's lives. At present, the common coatings for high-voltage wires have good insulation performance, but their cold resistance, heat resistance and corrosion resistance are not good, and the weather resistance needs to be further improved. [0003] To sum up, how to overcome the deficiencies of the prior art has become an urgent problem to be solved in the field of coatings. Contents of the invention [0004] The purpose of the present invention is to overcome the deficiencies of the prior art and propose a special insulating coating for high-voltage electric wires. The coating of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D127/18C09D7/12C09D5/25C09D5/08
Inventor 严晖
Owner NANTONG TIANMING PHOTOELECTRIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap