Anti-friction coating for glass lampshade, and preparation method thereof

A glass lampshade and friction-resistant technology, applied in the field of coatings, can solve the problems of poor wear resistance and no luminous performance, and achieve the effects of good wear resistance, not easy to crust, and good protection and decoration.

Inactive Publication Date: 2014-05-07
南通钰成光电科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Technical problem to be solved: Aiming at the disadvantages of poor abrasion resistance and no luminous performance of existing coatings for glass lampshades, the present invention provides a friction-resistant coating for glass lampshades and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] This embodiment provides a friction-resistant coating for glass lampshades, which contains the following components in parts by mass: 9 parts of phenoxyethyl acrylate, 3.5 parts of calcium halophosphate phosphor, 2 parts of sodium fluorosilicate, and 5 parts of alkyd resin , 0.2 parts of aminopropyltriethoxysilane, 0.1 part of epoxypropyltrimethoxysilane, 0.13 parts of cellulose acetate butyrate, 0.08 parts of benzoyl peroxide, 0.15 parts of o-methoxyphenol, polyethylene wax 0.05 parts.

[0010] The preparation steps of a friction-resistant coating for a glass lampshade are as follows: phenoxyethyl acrylate, calcium halophosphate fluorescent powder, sodium fluorosilicate, alkyd resin, aminopropyltriethoxysilane, epoxypropyl trimethyl Oxysilane, cellulose acetate butyrate, benzoyl peroxide, o-methoxyphenol and polyethylene wax are mixed evenly, then added to the ball mill, fully dissolved, stirred evenly, and then filtered with a 240-mesh screen, and the product is ready...

Embodiment 2

[0012] This embodiment provides a friction-resistant coating for glass lampshades, which contains the following components in parts by mass: 21 parts of phenoxyethyl acrylate, 8.5 parts of calcium halophosphate phosphor, 7 parts of sodium fluorosilicate, and 15 parts of alkyd resin , 0.6 parts of aminopropyltriethoxysilane, 0.3 parts of epoxypropyltrimethoxysilane, 0.32 parts of cellulose acetate butyrate, 0.16 parts of benzoyl peroxide, 0.35 parts of o-methoxyphenol, polyethylene wax 0.13 parts.

[0013] The preparation steps of a friction-resistant coating for a glass lampshade are as follows: phenoxyethyl acrylate, calcium halophosphate fluorescent powder, sodium fluorosilicate, alkyd resin, aminopropyltriethoxysilane, epoxypropyl trimethyl Oxysilane, cellulose acetate butyrate, benzoyl peroxide, o-methoxyphenol and polyethylene wax are mixed evenly, then added to the ball mill, fully dissolved, stirred evenly, and then filtered with a 260-mesh screen, and the product is re...

Embodiment 3

[0015] This embodiment provides a friction-resistant coating for glass lampshades, which contains the following components in parts by mass: 15 parts of phenoxyethyl acrylate, 6 parts of calcium halophosphate phosphor, 4.5 parts of sodium fluorosilicate, and 10 parts of alkyd resin , 0.4 parts of aminopropyltriethoxysilane, 0.2 parts of epoxypropyltrimethoxysilane, 0.22 parts of cellulose acetate butyrate, 0.12 parts of benzoyl peroxide, 0.25 parts of o-methoxyphenol, polyethylene wax 0.09 parts.

[0016] The preparation steps of a friction-resistant coating for a glass lampshade are as follows: phenoxyethyl acrylate, calcium halophosphate fluorescent powder, sodium fluorosilicate, alkyd resin, aminopropyltriethoxysilane, epoxypropyl trimethyl Oxysilane, cellulose acetate butyrate, benzoyl peroxide, o-methoxyphenol and polyethylene wax are mixed evenly, then added to the ball mill, fully dissolved, stirred evenly, and then filtered with a 250-mesh screen, and the product is re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an anti-friction coating for a glass lampshade, and a preparation method thereof. The coating comprises the following components in parts by weight: 9-21 parts of phenoxy ethyl acrylate, 3.5-8.5 parts of calcium halophosphate fluorescent powder, 2-7 parts of sodium fluosilicate, 5-15 parts of alkyd resin, 0.2-0.6 part of aminopropyltriethoxysilane, 0.1-0.3 part of epoxy propyl trimethoxy silane, 0.13-0.32 part of cellulose acetate butyrate, 0.08-0.16 part of benzoyl peroxide, 0.15-0.35 part of o-methoxyphenol, and 0.05-0.13 part of polyethylene wax. The coating provided by the invention is good in wear-resisting property, and not easy to crust, has a luminous function at night, plays good protecting and decorating roles on the glass lampshade, and can be used as a night-light in sleeping at home.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a friction-resistant coating for glass lampshades and a preparation method thereof. Background technique [0002] The glass lampshade has the advantages of good light transmission, high temperature, no gas emission, and no yellowing. It can be used for interior and exterior coating, frosting, vacuum coating, frosted aluminum plating, electrostatic spraying, color spraying and other coloring processes. It is suitable for interior decoration and lighting. . Regardless of whether the glass lampshade is used for home or outdoor use, it is easily rubbed by external objects and loses its original luster. Therefore, it is necessary to coat the outer surface of the glass lampshade with paint to protect the glass lampshade. However, the coatings available on the market for glass lampshades have poor abrasion resistance and do not have luminous properties. Contents of the invention [0003] Te...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D7/12
Inventor 刘杰
Owner 南通钰成光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com