Method for preparing aluminum-titanium intermediate alloy by recycling titanium scrap or titanium leftover material

A technology for master alloys and scraps is applied in the field of preparing aluminum-titanium master alloys, which can solve the problems of low utilization rate of titanium scraps or titanium scraps, and achieve the effects of saving cost and energy consumption, simple production process and reducing production costs.
CN103773979AInactive Publication Date: 2014-05-07HARBIN UNIV OF SCI & TECH
2 Cites 7 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
HARBIN UNIV OF SCI & TECH
Publication Date
2014-05-07
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention relates to a method for preparing an aluminum-titanium intermediate alloy by recycling titanium scrap and titanium leftover material, relates to a method for preparing an aluminum-titanium intermediate alloy, and aims at solving the problem of low recycling rate of the titanium scrap or titanium leftover material generated in the production process of existing titanium products. The preparation method comprises the following steps: (I) grinding the titanium scrap or titanium leftover material on a grinder, removing oil and drying, and packaging with aluminum foil into bags to obtain titanium blocks in bags; (II) melting pure aluminum in a smelting furnace to obtain molten aluminum; (III) increasing the temperature of the molten aluminum, adding part of the titanium blocks in bags by a bell jar press-in way, stirring for a period of time, adding the rest titanium blocks in bags, and continuously stirring to obtain the molten aluminum; (IV) removing gas by use of a rotary degasser, and performing slagging-off and casting and ingot formation to obtain the aluminum-titanium intermediate alloy. According to the method provided by the invention, the waste titanium scrap and titanium leftover material generated in the machining process of the titanium product are recycled, and then, the recycling rate of the titanium element reaches 85-90%.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a method for preparing an aluminum-titanium master alloy, in particular to a method for preparing an aluminum-titanium master alloy by using titanium shavings or titanium scraps. Background technique

[0002] With the increasingly wide application of titanium metal, titanium shavings and titanium scraps generated during the production and processing of titanium products are increasing. The data shows that the waste titanium generated in the production process of titanium materials and titanium parts accounts for about 60% to 70% of the weight of the smelted metal, and the waste titanium scrap generated reaches 1 / 3. The commonly used recycling method is recycling in front of the furnace, crushing titanium shavings, titanium scraps and defective castings that meet the requirements of direct remelting, and putting them back into electric arc melting furnaces, electrolytic refining furnaces or induction melting furnaces for remelti...

Claims