Pre-hardening plastic die steel

A plastic mold and mold steel technology, applied in the field of metal materials, can solve problems that hinder the application and development of 4Cr2NiMnMo, affect mold corrosion resistance, corrosion resistance, affect mold performance, etc., achieve significant corporate benefits, improve corrosion resistance, Energy Saving Effect

Active Publication Date: 2014-05-07
胡财基
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During thermal processing and heat treatment, Fe 3 C, Cr 23 C 6 、Cr 7 C 3 The solid solution of carbides into the matrix does not have a pinning effect, so the pre-hardened mold steel is prone to coarse flaky ferrite, sorbite and grain coarsening, which not only affects the corrosion resistance and corrosion resistance of the mold , and affect the performance of the mold
These factors hinder the application and development of 4Cr2NiMnMo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pre-hardening plastic die steel
  • Pre-hardening plastic die steel
  • Pre-hardening plastic die steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The mass percentage of the plastic mold steel 4Cr2NiMnMo after the alloy phase improvement includes the following composition:

[0052] C: 0.43%

[0053] Si: 0.35%

[0054] Mn: 1.32%

[0055] P: 0.021%

[0056] S: 0.005%

[0057] Ni: 1.01%

[0058] Cr: 1.98%

[0059] Cu: 0.12%

[0060] Mo: 0.31%

[0061] V: 0.12%

[0062] Fe: margin

[0063] The mechanical test result of embodiment 1 die steel 4Cr2NiMnMo is as table 1

[0064] Table 1

[0065]

[0066] The tensile property test result of embodiment 1 die steel 4Cr2NiMnMo is as table 2

[0067] Table 2

[0068]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to pre-hardening plastic die steel. The preparation method comprises the following steps: adding 0.05-0.15%V of microalloying elements into 4Cr2NiMnMo; after pleiotropic deformation, carrying out fine treatment and pre-hardening treatment, wherein the pleiotropic deformation comprises radial and axial forging deformation of the die steel and transverse and vertical pleiotropic deformation with the forging ratio greater than or equal to 8; the fine treatment comprises the following step: by taking the temperature of the forged die steel with the product thickness as a starting point, heating to 880+ / -10 DEG C; and after insulating at a speed of 3min / mm, discharging and air-cooling to 70 DEG C for spheroidizing annealing, wherein the specific process comprises the following steps: quickly heating to 780+ / -10 DEG C*3min / mm; and then cooling to 550 DEG C for discharging and air cooling at a speed less than or equal to 30 DEG C / h; the pre-hardening treatment comprises the following steps: heating the die steel with the product thickness from 70 DEG C to 350+ / -10 DEG C; insulating at the speed of 3min / mm; then heating to 880+ / -10 DEG C; then, insulating at the speed of 3min / mm; and then air-cooling to 70 DEG C and tempering.

Description

technical field [0001] The invention relates to a pre-hardened plastic mold steel, which belongs to the field of metal materials. Background technique [0002] The as-cast structure of the existing 4Cr2NiMnMo plastic mold steel is mostly coarse flaky F, P and a little M structure. According to the X-ray diffractometer test, F accounts for 85%, Fe 3 C accounts for 12%, and the rest is Cr 7 C 3 、Cr 23 C 6 Accounted for 3%. During thermal processing and heat treatment, Fe 3 C, Cr 23 C 6 、Cr 7 C 3 The solid solution of carbides into the matrix does not have a pinning effect, so the pre-hardened mold steel is prone to coarse flaky ferrite, sorbite and grain coarsening, which not only affects the corrosion resistance and corrosion resistance of the mold , and affect the performance of the mold. These factors hinder the application and development of 4Cr2NiMnMo. Contents of the invention [0003] The purpose of the present invention is to overcome the shortcoming of p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/58C22C38/46C21D8/00
Inventor 胡财基
Owner 胡财基
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com