Production method for double-zero aluminum foil

A double-zero aluminum foil and production method technology, applied in metal rolling and other directions, can solve the problems of unstable product quality, high coloring and printing costs, and achieve high strength, less pinholes, and stable quality

Active Publication Date: 2014-05-14
LUOYANG WANJI ALUMINUM PROCESSING CO LTD
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process improves the surface of the double-zero aluminum foil, but there are still obvious stripes a...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of production method of double-zero aluminum foil, thickness is 0.006mm, and its specific operation steps are as follows:

[0021] A production method of double-zero aluminum foil. After degassing and deslagging the AA1235 aluminum alloy melt, it is cast-rolled into a cast-rolled coil with a thickness of 6.5-8.0 mm, and then the cast-rolled coil is rolled into a thickness of 6.5-8.0 mm by the first cold rolling. The aluminum coil is 2.0-3.0mm, and then the aluminum coil after the first cold rolling is subjected to the first heat treatment at a temperature of 450-550°C for 15-20 hours, and then the aluminum coil after the first heat treatment is subjected to The second cold rolling is rolled into an aluminum coil with a thickness of 0.6-0.8mm, and the aluminum coil after the second cold rolling is subjected to a second heat treatment at a temperature of 300-380° C. for 6-12 hours; The aluminum coil after the second heat treatment is rolled into an aluminum coil wi...

Embodiment 2

[0023] A production method of double-zero aluminum foil, the thickness of which is 0.007mm, and its specific operation steps are as follows:

[0024] A production method of double-zero aluminum foil. After degassing and deslagging the molten aluminum alloy, it is cast-rolled into a cast-rolled coil with a thickness of 6.5-8.0 mm, and then the cast-rolled coil is rolled into a thickness of 6.5-8.0 mm by the first cold rolling. 2.0mm aluminum coil, then the aluminum coil after the first cold rolling is subjected to the first heat treatment at a temperature of 450°C for 15 hours, and then the aluminum coil after the first heat treatment is subjected to the second cold rolling into an aluminum coil with a thickness of 0.6mm, and conduct a second heat treatment on the aluminum coil after the second cold rolling at a temperature of 300° C. for 6 hours; Rolling into an aluminum coil with a thickness of 0.05mm, then place the aluminum coil in a heat treatment device, and heat it to th...

Embodiment 3

[0026] A production method of double-zero aluminum foil, the thickness of which is 0.009mm, and its specific operation steps are as follows:

[0027] A production method of double-zero aluminum foil. After degassing and deslagging the molten aluminum alloy, it is cast-rolled into a cast-rolled coil with a thickness of 6.5-8.0 mm, and then the cast-rolled coil is rolled into a thickness of 6.5-8.0 mm by the first cold rolling. 2.5mm aluminum coil, then the aluminum coil after the first cold rolling is subjected to the first heat treatment at a temperature of 500°C for 18 hours, and then the aluminum coil after the first heat treatment is subjected to the second cold rolling into an aluminum coil with a thickness of 0.7mm, and conduct a second heat treatment on the aluminum coil after the second cold rolling at a temperature of 360° C. for 10 hours; Roll the aluminum coil to a thickness of 0.08mm, then place the aluminum coil in a heat treatment device, and heat it to the critic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production method for a double-zero aluminum foil. The production method includes subjecting an aluminum-alloy molten mass to cast rolling to produce a cast rolling coil with the thickness of 6.5-8.0mm after degassing and deslagging, subjecting the cast rolling coil to first cold rolling to produce an aluminum coil with the thickness of 2.0-3.0mm, performing first heat treatment on the aluminum coil subjected to the first cold rolling at the temperature of 450-550 DEG C for 15-20 hours, subjecting the aluminum coil subjected to the first heat treatment to second cold rolling to produce an aluminum coil with the thickness of 0.6-0.8mm, and performing second heat treatment on the aluminum coil subjected to the second cold rolling at the temperature of 300-380 DEG C for 6-12 hours; subjecting the aluminum coil subjected to the second heat treatment to third cold rolling to produce an aluminum coil with the thickness of 0.05-0.1mm, heating the aluminum coil to the aluminum-foil recrystallization critical temperature of 250-310 DEG C, keeping the aluminum coil at the temperature for 5-10 hours, and subjecting an aluminum foil to fourth cold rolling to produce the double-zero aluminum foil with the thickness of 0.006-0.009mm. The double-zero aluminum foil produced by the production method has tensile strength of more than 95Mpa, ductility of more than 3.1%, small blank grain size, few surface stripes, few needle holes and stable quality.

Description

Technical field [0001] The present invention involves aluminum foil processing technology, which is specifically a production method of double zero aluminum foil. Background technique [0002] At present, dual -zero aluminum foil is mainly used in the field of packaging, such as soft packaging aluminum foil, cigarette aluminum foil, and cardboard aluminum foil.However, in addition to the softening bag on the surface of the aluminum foil, the cigarette card paper, aluminum foil and gold card paper need to be printed on the surface of the aluminum foil.With less, the color pulp you need to apply is less, and the effect after printing is good, and vice versa.If the surface of the aluminum foil is more and large, it is necessary to apply thicker color pulp to obtain a good printing effect, increasing the production cost of the enterprise. [0003] There are generally two types of billets in the current two -zero aluminum foil blank in the current industry, one is casting rolling bill...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22D11/06C22F1/04B21B1/40
Inventor 郭峰张广斌钱志恒吴俊刘全贵
Owner LUOYANG WANJI ALUMINUM PROCESSING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka