Water-based golden ink produced by using ordinary bronze powder and preparation method thereof

A copper-gold powder and water-based technology, applied in the field of water-based gold ink and preparation, can solve the problems of high production material cost and unstable material source, and achieve the effects of good printing stability, strong metal effect and stable material source.

Active Publication Date: 2014-05-14
深圳市深赛尔股份有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There are also a few ink manufacturers in China that produce water-based gold inks, but they are all produced with imported wate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] ①Preparation of pre-prepared resin liquid: In a certain volume of agitable open tank, first add 1 part of water, 30 parts of ethanol solvent, 5 parts of PH regulator (AMP-95), and disperse at a medium speed with a disc stirring paddle for 2- 5 minutes; then put in 65 parts of alkali-soluble colloidal acrylic resin (NeoCryl BT-20) while stirring, and disperse at 300-1500rpm / min for 8-30 minutes to obtain a pre-prepared resin solution for later use.

[0033] ②Preparation of pre-mixed gold powder slurry: In a certain volume of agitable open tank, first add 30 parts of ethanol solvent, 0.2 parts of water-based leveling wetting agent (silok100), 1 part of water-based passivator (Nacorr1151), and stir with a disc Disperse at a medium speed for 2-5 minutes; then add 68.8 parts of copper and gold powder, disperse at 300-1500rpm / min for 5-10 minutes, soak for more than 5 hours, and obtain a pre-mixed gold powder slurry for later use.

[0034] ③ Mixing, dispersing and tempering: ...

Embodiment 2

[0036] ①Preparation of pre-prepared resin liquid: In a certain volume of agitable open tank, first add 5 parts of water, 40 parts of ethanol solvent, 2 parts of pH regulator (AMP-95), and disperse 2- 5 minutes; then add 25 parts of alkali-soluble colloidal acrylic resin (NeoCryl BT-20) while stirring, and disperse at 300-1500rpm / min for 8-30 minutes to obtain a pre-prepared resin solution; set aside.

[0037] ②Preparation of pre-mixed gold powder slurry: In a certain volume of agitable open tank, first add 50 parts of ethanol solvent, 1 part of water-based leveling wetting agent (silok100), 2 parts of water-based passivator (Nacorr1151), and stir with a disc Disperse at a medium speed for 2-5 minutes; then put in 45 parts of copper gold powder, disperse at 300-1500rpm / min for 5-10 minutes, soak for more than 12 hours, and obtain a pre-mixed gold powder slurry for later use.

[0038] ③ Mixing, dispersing and tempering: Put 50 parts of pre-prepared resin liquid into the open cyl...

Embodiment 3

[0040] ①Preparation of pre-prepared resin liquid: In a certain volume of agitable open tank, first add 5 parts of water, 30 parts of ethanol solvent, 3 parts of PH regulator (AMP-95), and use a disc stirring paddle to disperse at a medium speed 2- 5 minutes; then add 49.5 parts of alkali-soluble colloidal acrylic resin (BT-20) while stirring, and disperse at 300-1500rpm / min for 8-30 minutes to obtain a pre-prepared resin solution; set aside.

[0041] ②Preparation of pre-mixed gold powder slurry: In a certain volume of agitable open tank, first add 40 parts of ethanol solvent, 2 parts of water-based leveling wetting agent (silok100), 1 part of water-based passivator (Dowcorning84), and stir with a disc Disperse with a paddle at a medium speed for 2-5 minutes; then put in 57 parts of copper gold powder, disperse at 300-1500rpm / min for 5-10 minutes, soak for more than 24 hours, and obtain a pre-mixed gold powder slurry for later use.

[0042]③ Mixing, dispersing and tempering: pu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses water-based golden ink produced by using ordinary bronze powder. The ink is prepared from the following raw materials in parts by weight: 30-55 parts of pre-prepared resin liquid, 0-10 parts of water-based color paste, 10-60 parts of pre-prepared gold paste, 0-5 parts of anti-scraping agent, 0.1-1 part of water-based defoaming agent, 0.2-2 parts of water-based lubricant, 1-10 parts of water and 1-30 parts of alcohol solvent. The preparation method comprises steps of preparing the pre-prepared resin liquid, preparing the pre-prepared gold paste, mixing, dispersing and tempering. The effects of imported water-based golden ink can be achieved by using ordinary bronze powder produced in China, and the ink is low in price, stable in material resource, good in metal effect and good in storage stability.

Description

technical field [0001] The invention relates to a printing ink and a preparation method thereof, in particular to a water-based gold ink produced from common copper and gold powder and a preparation method thereof. Background technique [0002] For a long time, gravure gold ink has used acrylic resin to make solvent-based ink; because the solvent content in the ink exceeds 30-60%, a large amount of solvent volatilizes during the printing process, which is likely to cause environmental pollution and damage human health, and there are potential fire hazards. For environmental protection, we are all working hard. In the printing industry, many traditional toxic and highly polluting products have been banned. Water-based inks instead of solvent inks have become an inevitable trend in the development of inks. Water-based gold inks are environmentally friendly, non-toxic, non-polluting, and have no harmful gas emissions, which caters to today's direction of development. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/107C09D11/106C09D11/037
Inventor 梁素静刘国民
Owner 深圳市深赛尔股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap