Manufacturing method of hot-dip galvanized coated plates

A manufacturing method, hot-dip galvanizing technology, applied to chemical instruments and methods, building structures, covering/lining, etc., can solve problems such as non-recyclable, low adhesion fastness, and falling off of lining materials, and achieve the goal of using Extended life, bright decorative effect, long service life effect

Inactive Publication Date: 2014-05-14
WUXI XINDAZHONG STEEL SHEET
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above two commonly used materials also have disadvantages: first, the adhesion fastness is not high, and the lining material on the surface will fall off to a certain extent after about half a year of use; Liner base material, not recyclable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of manufacturing method of hot-dip galvanized coated sheet material of the present invention comprises the following steps:

[0025] (1) Material selection: The material selection is a hot-dip galvanized sheet with a thickness of 0.28mm and a width of 1300mm;

[0026] (2) Surface pretreatment: put the hot-dip galvanized sheet with a thickness of 0.28mm and a width of 1300mm that is clean and unoiled into the surface treatment machine for surface pretreatment of coating the surface treatment agent , the coated board surface treatment agent is HAS656 passivator produced by Nippon, the single-side coating speed of the board surface treatment agent is: 5m / min, and the single-side coating amount of the board surface treatment agent is: 1.2g / m 2 , the temperature of the surface treatment agent is 15°C when coating;

[0027] (3) Drying treatment: the hot-dip galvanized sheet coated with the surface treatment agent enters the oven for drying treatment. The temperature...

Embodiment 2

[0035] A kind of manufacturing method of hot-dip galvanized coated sheet material of the present invention comprises the following steps:

[0036] (1) Material selection; the material selection is a hot-dip galvanized sheet with a thickness of 1.1mm and a width of 900mm;

[0037] (2) Surface pretreatment: put the hot-dip galvanized sheet with a thickness of 1.1mm and a width of 900mm that is clean and unoiled into the surface treatment machine for surface pretreatment of coating the surface treatment agent , the coated board surface treatment agent is HAS656 passivator produced by Nippon, the single-side coating speed of the board surface treatment agent is: 15m / min, and the single-side coating amount of the board surface treatment agent is: 0.4g / m 2 , the temperature of the surface treatment agent is 27°C when coating;

[0038] (3) Drying treatment: the hot-dip galvanized sheet coated with the surface treatment agent enters the oven for drying treatment. The temperature of...

Embodiment 3

[0046] A kind of manufacturing method of hot-dip galvanized coated sheet material of the present invention comprises the following steps:

[0047] (1) Material selection: The material selection is a hot-dip galvanized sheet with a thickness of 0.5mm and a width of 1000mm;

[0048] (2) Surface pretreatment: put the hot-dip galvanized sheet with a thickness of 0.5mm and a width of 1000mm that is clean and unoiled into the surface treatment machine for surface pretreatment of coating the surface treatment agent , the coated board surface treatment agent is HAS656 passivator produced by Nippon, the single-side coating speed of the board surface treatment agent is: 10m / min, and the single-side coating amount of the board surface treatment agent is: 1.1g / m 2 , the temperature of the surface treatment agent is 20°C when coating;

[0049] (3) Drying treatment: the hot-dip galvanized sheet coated with the surface treatment agent enters the oven for drying treatment. The temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a manufacturing method of building plates, in particular to a manufacturing method of hot-dip galvanized coated plates. The building plates are resistant to corrosion and weather, prevent dropping of dews, and have certain thermal insulating property. The manufacturing method includes the steps of selecting materials, preprocessing the surfaces, drying, coating with glue, laminating, drying, hot-pressing, and checking for storage. Products manufactured by method are well fireproof; detections show that the products are approved by the level B-1 of national building materials fire rating, are fully environment friendly and free of pollution, also pass environmental certification, and have the effects of long service life, environment friendliness, fire proofing, dew prevention, corrosion resistance, acoustic absorption, light absorption, thermal insulation, high transparency, high glossiness, low haze, excellent UV barrier property, laser security, and bright decoration.

Description

technical field [0001] The invention relates to a manufacturing method of a building plate with corrosion resistance, weather resistance, dew condensation prevention, and certain thermal insulation performance, especially a manufacturing method of a hot-dip galvanized film-coated plate. Background technique [0002] In modern architecture and decoration, in many cases, some metal layers pasted with lining materials are used, such as metal plates pasted with glass fiber or foamed plastics. The advantages of such materials are beautiful, waterproof, and easy to use. Now It has been widely used in large-area construction and decoration such as factories and office buildings. However, the above two commonly used materials also have disadvantages: first, the adhesion fastness is not high, and the lining material on the surface will fall off to a certain extent after about half a year of use; The base material of the lining layer cannot be recycled. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/075B32B15/082B32B37/12B32B37/10B32B37/06B32B38/16
Inventor 周明华
Owner WUXI XINDAZHONG STEEL SHEET
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com