Manufacturing method of aluminum alloy coated plates

A technology of aluminum alloy plate and manufacturing method, which is applied to chemical instruments and methods, building structures, covering/lining, etc., can solve problems such as non-recyclable, low bonding fastness, and falling off of lining materials, and achieve saving Energy, bright decorative effect, long service life effect

Inactive Publication Date: 2014-05-14
WUXI XINDAZHONG STEEL SHEET
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above two commonly used materials also have disadvantages: first, the adhesion fastness is not high, and the lining material on the surface will fall off to a certain extent after about half a year of use; Liner base material, not recyclable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A method for manufacturing an aluminum alloy film-coated plate of the present invention comprises the following steps:

[0025] (1) Material selection: the material is aluminum alloy plate with a thickness of 0.16mm and a width of 1280mm;

[0026] (2) Surface pretreatment: put the aluminum alloy plate with a clean surface and a thickness of 0.16mm and a width of 1280mm into the surface treatment machine for coating the surface treatment agent. The coated board surface treatment agent is GR934 passivator produced by Nippon Paint Co., Ltd. The single-side coating speed of the board surface treatment agent is 25m / min, and the single-side coating amount of the board surface treatment agent is 0.7g / m 2 , the temperature of the surface treatment agent is 20°C when coating;

[0027] (3) Drying treatment: the aluminum alloy plate coated with the surface treatment agent enters the oven for drying treatment. The temperature of the oven is 50°C, and the drying time is 15 seconds;...

Embodiment 2

[0035] A method for manufacturing an aluminum alloy film-coated plate of the present invention comprises the following steps:

[0036] (1) Material selection: the material is aluminum alloy plate with a thickness of 1.3mm and a width of 850mm;

[0037] (2), board surface pretreatment: the aluminum alloy plate with a thickness of 1.3 mm and a width of 850 mm, which is clean and unoiled, is put into the surface treatment machine for pretreatment of the board surface coating agent. The coated board surface treatment agent is GR934 passivator produced by Nippon Paint Co., Ltd. The single-side coating speed of the board surface treatment agent is: 10m / min, and the single-side coating amount of the board surface treatment agent is: 1.3g / m 2 , the temperature of the surface treatment agent is 40°C when coating;

[0038] (3) Drying treatment: the aluminum alloy plate coated with the surface treatment agent enters the oven for drying treatment, the temperature of the oven is 66°C, and...

Embodiment 3

[0046] A method for manufacturing an aluminum alloy film-coated plate of the present invention comprises the following steps:

[0047] (1) Material selection: the material is aluminum alloy plate with a thickness of 0.8mm and a width of 1100mm;

[0048] (2) Surface pretreatment: put the aluminum alloy plate with a clean surface and an unoiled thickness of 0.8mm and a width of 1100mm into the surface treatment machine for surface pretreatment of coating the surface treatment agent. The coated board surface treatment agent is GR934 passivation agent produced by Nippon Paint Co., Ltd. The single-side coating speed of the board surface treatment agent is: 15m / min, and the single-side coating amount of the board surface treatment agent is: 1.0g / m 2 , the temperature of the surface treatment agent is 30°C when coating;

[0049] (3) Drying treatment: the aluminum alloy plate coated with the surface treatment agent enters the oven for drying treatment. The temperature of the oven is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a manufacturing method of building plates, in particular to a manufacturing method of aluminum alloy coated plates. The building plates are resistant to corrosion and weather proof, prevent dew dropping, and have certain insulation performance. The manufacturing method includes the steps of selecting materials, preprocessing surfaces of plates, drying, coating with glue, laminating, drying, hot-pressing, and checking for storage. The product manufactured by the method has good fire resistance; detections show that the product is approved by the level B-1 of fire rating for national building materials, is fully environment friendly and pollution free, also passes environmental certification, and has the advantages of long service life, environment friendliness, fire proofing, dew prevention, corrosion resistance, acoustic absorption, light absorption, thermal insulation, high transparency, high glossiness, low haze, excellent UV barrier property, laser security, and bright decoration.

Description

technical field [0001] The invention relates to a manufacturing method of a building plate with corrosion resistance, weather resistance, dew condensation prevention, and certain thermal insulation performance, especially a manufacturing method of an aluminum alloy film-coated plate. Background technique [0002] In modern architecture and decoration, in many cases, some metal layers pasted with lining materials are used, such as metal plates pasted with glass fiber or foamed plastics. The advantages of such materials are beautiful, waterproof, and easy to use. Now It has been widely used in large-area construction and decoration such as factories and office buildings. However, the above two commonly used materials also have disadvantages: first, the adhesion fastness is not high, and the lining material on the surface will fall off to a certain extent after about half a year of use; The base material of the lining layer cannot be recycled. Contents of the invention [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/077B32B15/09B32B37/12B32B37/06B32B38/16
Inventor 周明华
Owner WUXI XINDAZHONG STEEL SHEET
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap