A preparation method of high-emissivity far-infrared health-care purple sand tiles

A far-infrared health care, high emissivity technology, applied in clay products, other household appliances, household appliances, etc., can solve the problems of low technical content, single function, few varieties, etc., to increase blood flow, accelerate blood circulation, Anti-aging effect

Active Publication Date: 2015-09-02
LIAONING SILICATE RES INST
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although purple sand products have the above advantages, traditional products have few varieties, single functions, and low technical content, which cannot meet more needs of people.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Weigh 400g of purple sand raw materials, 40g of medical stone, 1.8ml of water glass and 240ml of water, put them into a quick mill (the mass of the balls in the grinding tank is 1.5 times the mass of the dry material) and grind for 2 minutes to obtain a slurry. The slurry is granulated in the spray drying tower, and pressed into the required shape (such as circle, rhombus, hexagon, etc.) by a pressure molding machine. The samples were dried at 40°C for 2 hours and thoroughly dried at 100°C for 5 hours. Then put in the rapid heating resistance furnace (SX 3 -10-14) were sintered at 1160°C, and the holding time was 30 minutes to prepare purple sand tiles.

[0024] Dry the prepared purple sand tiles at 120°C for 2 hours, weigh the mass, boil in boiling water for 2 hours and 30 minutes, wait for the water to cool naturally, remove the tiles, and wipe off the excess on the soaked deerskin. Moisture (until there is no water on the surface), weigh its mass, and calculate the...

Embodiment 2

[0026] Weigh 400g of purple sand raw materials, 40g of medical stone, 1.8ml of water glass and 240ml of water, put them into a quick mill (the mass of the balls in the grinding tank is 1.5 times the mass of the dry material) and grind for 2 minutes to obtain a slurry. The slurry is granulated in the spray drying tower, and pressed into the required shape (such as circle, rhombus, hexagon, etc.) by a pressure molding machine. The samples were dried at 40°C for 2 hours and thoroughly dried at 100°C for 5 hours. Then put in the rapid heating resistance furnace (SX 3 -10-14) were sintered at 1120°C, and the holding time was 30 minutes to prepare purple sand tiles.

[0027] Dry the prepared purple sand tiles at 120°C for 2 hours, weigh the mass, boil in boiling water for 2 hours and 30 minutes, wait for the water to cool naturally, remove the tiles, and wipe off the excess on the soaked deerskin. Moisture (until there is no water on the surface), weigh its mass, and calculate the...

Embodiment 3

[0029] Weigh 400g of purple sand raw materials, 80g of medical stone, 3ml of water glass and 180ml of water, put them into a quick mill (the mass of the balls in the grinding tank is 1.5 times the mass of the dry material) and grind for 2 minutes to obtain a slurry. The slurry is granulated in the spray drying tower, and pressed into the required shape (such as circle, rhombus, hexagon, etc.) by a press molding machine. The samples were dried at 40°C for 2 hours and thoroughly dried at 100°C for 5 hours. Then put in the rapid heating resistance furnace (SX 3 -10-14) were sintered at 1100°C, and the holding time was 30 minutes to prepare purple sand tiles.

[0030] Dry the prepared purple sand tiles at 120°C for 2 hours, weigh the mass, boil in boiling water for 2 hours and 30 minutes, wait for the water to cool naturally, remove the tiles, and wipe off the excess on the soaked deerskin. Moisture (until there is no water on the surface), weigh its mass, and calculate the wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A preparation method for a high-emissivity far-infrared health-care purple-sand porcelain slice is disclosed, and mainly solves the problems that conventional purple-sand products are excessively traditional and monotonous, and functional products are less. The preparation method comprises the following steps: material preparing, grinding, granulating, compaction molding, drying and sintering. The raw materials comprises in parts by weight: 100 parts of a purple-sand raw material, 10-20 parts of Chinese medical stone, 45-60 parts of a disperse medium water and 0.45-0.75 part of a dispersant water glass. The preparation method comprises the advantages that by utilizing the far-infrared emission function of purple sand and adding a proper amount of Chinese medical stone, the prepared purple-sand porcelain is applied to summer sleeping mats or heating blankets, and gives play to effects of improving sleep quality, promoting and improving blood circulation, enhancing metabolism, improving immunity and adjusting body metabolism, and delaying organ failure process, thereby reaching the health-care effects of delaying aging, prolonging life span and the like.

Description

technical field [0001] The invention belongs to the field of functional ceramic materials, and in particular relates to a preparation method of high-emissivity far-infrared health-care purple sand tiles. Background technique [0002] Due to the special structure of purple sand, its products have high appreciation value and use value. Zisha teapots can maintain the color, aroma and taste of tea, and are not easy to deteriorate and go rancid; purple sand potted flowers are not easy to rot, and are good for plant growth. Although purple sand products have the above-mentioned advantages, traditional products have few varieties, single functions, and low technical content, which cannot meet people's more needs. Contents of the invention [0003] The purpose of the present invention is to make up for the lack of traditional monotonous and few functional products of existing purple sand products, and to provide a preparation method of high emissivity far-infrared health care pur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/24
Inventor 高琳琳韩绍娟许壮志薛健张全河
Owner LIAONING SILICATE RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap