Zinc-carrying nano organic montmorillonite antimicrobial agent and preparation method thereof

A nano-organic and montmorillonite technology, applied in botany equipment and methods, biocides, disinfectants, etc., can solve the problems of silver-loaded inorganic antibacterial agents that are easy to change color and limit their wide application

Inactive Publication Date: 2014-07-02
LONGYAN UNIV
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, silver-loaded inorganic antibacterial agents are easy to change color, which limits its wide application in composite materials; copper-loaded montmorillonite has certain inhibitory effects on Staphylococcus aureus and Escherichia coli, and because of its own color, it also limits its application in composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Prepare 22g of montmorillonite and deionized water into a 10% suspension, add 1g of zinc chloride, stir at 60°C for 3 hours, add 2g of octadecyltrimethylammonium chloride, heat up and stir, and stir at 70°C After stirring continuously for 3 hours, filter with suction, wash repeatedly with distilled water, then vacuum-dry at 65°C for 48 h, grind, and pass through a 300-mesh sieve to obtain sample 1.

[0018] The glass culture dish and prepared nutrient agar were cultured in a high-temperature sterilization pot, and sterilized at 0.15 MPa for 20 minutes. Nutrient agar cultures were then incubated in a 52°C water bath. Take 4, 2, 1, 0.5, 0.25, 0.125 and 0.0625mg of sample 1, add appropriate amount of water to dissolve into a slurry and place it in a 10mL centrifuge tube, take about 0.2mL of the prepared bacterial solution in the centrifuge tube, and then add an appropriate amount of Pour the nutrient agar medium into the centrifuge tube to the full scale, shake well and p...

Embodiment 2

[0020] Prepare 20g of montmorillonite and deionized water into a 10% suspension, add 2g of zinc chloride, stir at 60°C for 3 hours, add 3g of octadecyltrimethylammonium chloride, heat up and stir, and stir at 70°C After stirring continuously for 3 hours, filter with suction, wash repeatedly with distilled water, then vacuum-dry at 65°C for 48 h, grind, and pass through a 300-mesh sieve to obtain sample 1.

[0021] The glass culture dish and prepared nutrient agar were cultured in a high-temperature sterilization pot, and sterilized at 0.15 MPa for 20 minutes. Nutrient agar cultures were then incubated in a 52°C water bath. Take 4, 2, 1, 0.5, 0.25, 0.125 and 0.0625mg of sample 2, add appropriate amount of water to dissolve into a slurry and place it in a 10mL centrifuge tube, take about 0.2mL of the prepared bacterial solution in the centrifuge tube, and then add an appropriate amount of Pour the nutrient agar medium into the centrifuge tube to the full scale, shake well and p...

Embodiment 3

[0023] Prepare 15g of montmorillonite and deionized water into a 10% suspension, add 2g of zinc chloride, stir at 60°C for 4 hours, add 3g of octadecyltrimethylammonium chloride, heat up and stir, After stirring continuously for 4 hours, filter with suction, wash repeatedly with distilled water, then vacuum-dry at 65°C for 48 h, grind, and pass through a 300-mesh sieve to obtain sample 3.

[0024] The glass culture dish and prepared nutrient agar were cultured in a high-temperature sterilization pot, and sterilized at 0.15 MPa for 20 minutes. Nutrient agar cultures were then incubated in a 52°C water bath. Take 4, 2, 1, 0.5, 0.25, 0.125 and 0.0625mg of sample 3, add appropriate amount of water to dissolve into a slurry and place it in a 10mL centrifuge tube. Pour the nutrient agar medium into the centrifuge tube to the full scale, shake well and pour the plate to solidify. After completion, place the petri dish in an incubator for observation and determine the minimum inhibi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a zinc-carrying nano organic montmorillonite antimicrobial agent which is prepared from the following components in percentage by weight: 8-15% of zinc chloride, 13-16% of organized intercalation treating agent and 69-79% of montmorillonite. The preparation method comprises the following steps: preparing 69-79% of montmorillonite and deionized water into a 10% suspension, adding 8-15 wt% of zinc chloride, stirring at 60-70 DEG C for 3-4 hours, adding 13-16% of organized intercalation treating agent, heating while stirring, continuing stirring at 70-80 DEG C for 4-5 hours, carrying out vacuum filtration, repeatedly washing with distilled water, carrying out vacuum drying at 65 DEG C for 48 hours, grinding, and passing through a 300-mesh screen to obtain the zinc-carrying nano organic montmorillonite antimicrobial agent. The antimicrobial agent has the advantages of high efficiency and broad antibacterial spectrum.

Description

technical field [0001] The invention relates to an antibacterial agent and a preparation method thereof, in particular to a zinc-loaded nanometer organic montmorillonite antibacterial agent and a preparation method thereof. Background technique [0002] With the development of economy and society, people's requirements for living environment and their own health are constantly improving. Harmful bacteria are widely distributed in nature and there are many kinds, which threaten human health. Especially in recent years, global microbial disasters caused by microorganisms and their variants have occurred frequently. Materials with antibacterial and bactericidal functions have attracted more and more attention. The development of antibacterial agents with good antibacterial properties is the key to the development of antibacterial materials. [0003] The antimicrobial agents currently used are mainly divided into two categories: organic and inorganic. Organic antibacterial age...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A01N59/16A01N25/08A01P1/00A01N33/12
Inventor 温德才唐治炜谢桂香林标声
Owner LONGYAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap