Monocomponent PRTV anti-pollution-flashover paint and preparation method thereof

An antifouling flashover coating, a single-component technology, applied in the direction of fireproof coatings, coatings, etc., to achieve the effects of cost reduction, good flame retardant effect, and strong adhesion

Inactive Publication Date: 2014-07-16
滕州市智星电力电子工程有限公司
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing RTV anti-fouling flashover coating is a new material that has emerged in recent years to improve the insulation level of electrical equipment. The service life of the RTV coating was five yea

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of one-component PRTV antifouling flashover coating is made up of the following materials of weight part:

[0029] Polydimethylsiloxane: 28;

[0030] Hydroxyl-terminated fluoropolysiloxane: 10;

[0031] Nano silica: 3;

[0032] Crosslinker: 1;

[0033] Catalyst: 0.5;

[0034] Decabromodiphenyl ether: 2;

[0035] Pigments: 1;

[0036] Solvent: 40;

[0037] The polydimethylsiloxane is silicone rubber;

[0038] The hydroxyl-terminated fluorine-containing polysiloxane is fluorosilicone rubber with a viscosity of 1200cp;

[0039] The catalyst is stannous octoate;

[0040] The pigment is iron oxide red or titanium dioxide;

[0041] The solvent is mc-318 composite solvent, which does not contain ozone-depleting substances (ODS).

Embodiment 2

[0043] A kind of one-component PRTV antifouling flashover coating is made up of the following materials of weight part:

[0044] Polydimethylsiloxane: 38;

[0045] Hydroxyl-terminated fluoropolysiloxane: 19;

[0046] Nano silica: 5;

[0047] Crosslinker: 3;

[0048] Catalyst: 1;

[0049] Decabromodiphenyl ether: 3;

[0050] pigments: 2;

[0051] Solvent: 50;

[0052] The polydimethylsiloxane is silicone rubber;

[0053] The hydroxyl-terminated fluorine-containing polysiloxane is fluorosilicone rubber with a viscosity of 2000cp;

[0054] The catalyst is stannous octoate;

[0055] The pigment is iron oxide red or titanium dioxide;

[0056] The solvent is mc-318 composite solvent, which does not contain ozone-depleting substances (ODS).

Embodiment 3

[0058] A kind of one-component PRTV antifouling flashover coating is made up of the following materials of weight part:

[0059] Polydimethylsiloxane: 33;

[0060] Hydroxy-terminated fluoropolysiloxane: 15;

[0061] Nano silica: 4;

[0062] Crosslinker: 2;

[0063] Catalyst: 0.8;

[0064] Decabromodiphenyl ether: 2.5;

[0065] Pigment: 1.5;

[0066] Solvent: 45;

[0067] The polydimethylsiloxane is silicone rubber;

[0068] The hydroxyl-terminated fluorine-containing polysiloxane is fluorosilicone rubber with a viscosity of 1600cp;

[0069] The catalyst is stannous octoate;

[0070] The pigment is iron oxide red or titanium dioxide;

[0071] The solvent is mc-318 composite solvent, which does not contain ozone-depleting substances (ODS).

[0072] The preparation method of the single-component PRTV antifouling flashover paint described in the above three embodiments is:

[0073] (1) Send polydimethylsiloxane, hydroxyl-terminated fluorine-containing polysiloxane, nano...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses monocomponent PRTV anti-pollution-flashover paint and a preparation method thereof. The monocomponent PRTV anti-pollution-flashover paint is composed of the following materials in parts by weight: 28-38 parts of polydimethylsiloxane, 10-19 parts of hydroxyl-terminated fluorine-containing polysiloxane, 3-5 parts of nanometer silica, 1-3 parts of a coupling agent, 0.5-1 part of a catalyst, 2-3 parts of decabromodiphenyl ether, 1-2 parts of a pigment and 40-50 parts of a solvent. The monocomponent PRTV anti-pollution-flashover paint has the beneficial effects that a fluorine material and a nanometer material are organically combined and blended with silicone rubber, silicone rubber is taken as main base rubber and fluorosilicone rubber is taken as auxiliary base rubber; and the monocomponent PRTV anti-pollution-flashover paint has the main technical advantages of being good in flame retardant effect, substantially reduced in cost.

Description

technical field [0001] The invention relates to the technical field of insulating material production, in particular to a single-component PRTV antifouling flashover coating and a preparation method thereof. Background technique [0002] Electrical equipment arranged outdoors is easily affected by the environment, and its insulation level is likely to decrease in extreme cases, leading to electrical insulation failure. Therefore, how to improve the adaptability of outdoor electrical equipment insulation to the environment has become one of the concerns of electrical equipment maintenance personnel. Of course, the first consideration is to consider the atmospheric environment of electrical equipment at the design stage and to select the equipment in a targeted manner. However, as the equipment is put into operation, the insulation level of the equipment will age and decrease, and the environment in which the equipment is located Changes, as well as the quest for increased eff...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D183/04C09D183/08C09D7/12C09D5/25C09D5/18
Inventor 马涛
Owner 滕州市智星电力电子工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap