A kind of rare earth sulfide rubber additive and preparation method thereof

A rare earth sulfide and rubber technology, which is applied in the field of rare earth sulfide rubber additives and its preparation, can solve the problems of unfavorable environmental protection, etc., and achieve the effects of easy operation, low production cost and energy consumption, and prevention of aging and degradation

Active Publication Date: 2016-08-17
内蒙古中科宏特高新科技有限责任公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the rubber additives currently used contain organic substances and other substances that are harmful to the environment, which is not conducive to the requirements of environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of rare earth sulfide rubber additive and preparation method thereof
  • A kind of rare earth sulfide rubber additive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1 Preparation of rubber composites

[0025] Mix 0.5wt% rare earth samarium sulfide with 99.5wt% natural rubber, and masticate at 50-60°C for 24 hours, then knead for 30min at the temperature of the front roll at 55-60°C and at the temperature of the rear roll at 50-55°C, and then in At 140-150°C, vulcanize for 2 hours to obtain rubber composite materials.

Embodiment 2

[0026] Example 2 Preparation of rubber composites

[0027] Mix 0.5wt% rare earth samarium sulfide with 99.5wt% styrene-butadiene rubber, masticate at 30-45°C for 3 hours, then knead for 45min at the temperature of the front roll at 45-55°C and at the temperature of the rear roll at 50-60°C, and then At 150-160°C, vulcanize and mold for 2 hours to obtain rubber composite materials.

Embodiment 3

[0028] Example 3 Preparation of rubber composites

[0029] Mix 1wt% rare earth samarium sulfide with 99wt% natural rubber, and masticate at 50-60°C for 24 hours, then knead at the temperature of the front roll at 55-60°C and the temperature of the rear roll at 50-55°C for 30 minutes, and then at 140-60°C At 150°C, vulcanize for 2 hours to obtain a rubber composite material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a rubber composite material, which comprises 0.5-5 wt% of tombarthite sulfide, and further provides a preparation method for the rubber composite material. The preparation method comprises the following steps: mixing the tombarthite sulfide and rubber; conducting plastication, mixing and sulfidation forming to obtain the rubber composite material. The prepared rubber composite material is provided with relatively excellent stretching property, simple and safe in manufacturing technology, easy to operate, and relatively low in preparing cost and energy consumption, so as to facilitate industrialized production; besides, the tombarthite sulfide is adopted as a green rubber ingredient, so as to be free from contamination to environment, and environmental-friendly.

Description

technical field [0001] The invention belongs to the technical field of polymer material modification, and in particular relates to a rare earth sulfide rubber additive and a preparation method thereof. Background technique [0002] Rubber is a high-molecular compound with high elasticity. It has become an important material due to its special properties such as excellent fatigue resistance, high wear resistance, electrical insulation, compactness, corrosion resistance, high temperature resistance and low temperature resistance. industrial materials. With the continuous growth of the global automobile industry, high-speed railway and aerospace and other industrial fields, the demand for rubber products will continue to be strong, and the rubber industry will maintain a continuous development trend. [0003] Rubber additives are important raw materials in the rubber industry. Rubber additives play a pivotal role in improving the processing and application performance of rubbe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L9/06C08K3/30
Inventor 刘建钢姜银举翟纪敏张成边瑞峰刘明月
Owner 内蒙古中科宏特高新科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap