Preparing method for mineral lick block for cattle and sheep

A mineral element, cattle and sheep technology, applied in the directions of additional food elements, animal feed molding or processing, animal feed, etc., can solve the problems of high price, high maintenance and repair costs, and increase the production cost of mineral element licking bricks.

Inactive Publication Date: 2014-09-03
高强
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high-strength mechanical pressing machine is expensive, and the maintenance and repair costs of the machine are high, which increases the production cost of mineral element licking bricks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparing method for mineral lick block for cattle and sheep

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] 1) Taking 100 kg as an example, the licking brick includes the following raw materials in weight percentage: 4 kg of magnesium chloride, 8 kg of magnesium oxide, 6 kg of calcium carbonate, 3 kg of calcium hydrogen phosphate, and 79 kg of sodium chloride. First, dissolve 4 kg of magnesium chloride in 8 kg of water, then mix the magnesium oxide, calcium carbonate, calcium hydrogen phosphate and sodium chloride evenly, and finally pour the magnesium chloride solution into it and stir evenly;

[0013] 2) Pour the stirred and mixed raw materials into the licking brick mold, using 11kg / cm 2 It is molded with micro-pressure, and then dried naturally for 20 days at 15-35°C to complete the production of the product, which is suitable for cattle and sheep to eat ad libitum.

Embodiment 2

[0015] 1) Taking 100 kilograms as an example, the licking brick includes the following raw materials in weight percentage: 6.5 kilograms of magnesium chloride, 23.5 kilograms of magnesium oxide, 10 kilograms of calcium carbonate, 8 kilograms of calcium hydrogen phosphate, 48 kilograms of sodium chloride, 2.4 kilograms of iron sulfate, sulfuric acid 0.006 kg of cobalt, 0.75 kg of zinc oxide, 0.8 kg of manganese oxide, 0.04 kg of calcium iodate, and 0.004 kg of sodium selenite. First, dissolve 6.5 kg of magnesium chloride in 10 kg of water, then mix magnesium oxide and other compounds together evenly, and finally pour the magnesium chloride solution into it and stir evenly;

[0016] 2) Pour the stirred and mixed raw materials into the licking brick mould, using 25kg / cm 2 It is molded with micro-pressure, and then dried naturally at 15-35°C for 30 days to complete the production of the product. It is suitable for sheep and goats to lick. Cows need to be supplemented with copper f...

Embodiment 3

[0018] 1) Taking 100 kilograms as an example, the licking brick includes the following raw materials in weight percentage: 10 kilograms of magnesium chloride, 30 kilograms of magnesium oxide, 10 kilograms of calcium carbonate, 8 kilograms of calcium hydrogen phosphate, and 42 kilograms of sodium chloride. First, dissolve 10 kilograms of magnesium chloride In 7 kg of water, then mix other compounds such as magnesium oxide together evenly, and finally pour the magnesium chloride solution into it, and stir evenly;

[0019] 2) Pour the stirred and mixed raw materials into the licking brick mold, using 17kg / cm 2 It is molded with micro-pressure, and then dried naturally at 25-35°C for 10 days to complete the production of the product. It is suitable for grazing cattle and sheep before the pasture turns green in spring. The amount of sheep licking is controlled within 60 grams per day. Licking is controlled within 140 grams.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparing method for a mineral lick brick for cattle and sheep. The preparing method comprises the following steps that: firstly, magnesium chloride is dissolved in water; then, magnesium oxide, calcium carbonate, calcium hydrophosphate and inorganic mineral elements required by cattle and sheep are uniformly mixed; the magnesium chloride solution is poured into the uniformly mixed mineral elements; the mixture is uniformly stirred; then, the mixed raw materials are poured into a lick block mold; micro-pressure compression molding is carried out; finally, natural drying is carried out at a temperature of 15 to 35 DEG C to obtain the mineral lick block for cattle and sheep. The preparing method has the advantages that the production cost is low; the hardness of the lick block reaches 25 to 35kg / cm<2>; and the mineral lick brick do not get loose after being soaked in water for 10 to 30 days, thereby being suitable for cattle and sheep to lick.

Description

technical field [0001] The invention relates to a preparation method of mineral element lick bricks for cattle and sheep. Background technique [0002] At present, the production of livestock mineral elements licking bricks generally adopts binders (lime, cement, bentonite, etc.) and mineral elements to be mixed in proportion and then pressed and formed by high-strength presses. The forming mainly relies on high-strength presses to provide pressure molding. So as to achieve the appropriate hardness. As described in Chinese patents 200610037867.X, 201210190334.0, 200610037868.4, 200610037866.5 and 201010551578.8, they are all produced by strong pressure mechanical pressing. Because the high-strength mechanical pressing machine is expensive, and the maintenance and repair costs of the machine are relatively high, the production cost of mineral elements licking bricks is increased. Contents of the invention [0003] The purpose of the present invention is to avoid the disad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A23K1/20A23K1/175A23K10/40A23K20/20A23K20/24A23K20/26A23K40/20A23K50/10
Inventor 高强
Owner 高强