Thermosetting composition, lamination body, substrate, film, display device, and window material

A composition, thermosetting technology, applied in the direction of synthetic resin layered products, coatings, layered products, etc., can solve problems such as reduced reflectivity

Inactive Publication Date: 2014-09-03
JNC CORP
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the effect of reducing the reflectance is small only in the antireflection film of one layer, and it is necessary to increase the effect of reducing the reflectance by using a laminate of two or more layers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermosetting composition, lamination body, substrate, film, display device, and window material
  • Thermosetting composition, lamination body, substrate, film, display device, and window material
  • Thermosetting composition, lamination body, substrate, film, display device, and window material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0211] Hereinafter, although an Example demonstrates this invention further, this invention is not limited to these Examples.

[0212] Compounds used in synthesis examples, comparative synthesis examples, reference examples, examples, and comparative examples are described in advance for each component.

[0213] Fluorine-containing radically polymerizable monomer (a1):

[0214] a1-1: 2,2,2-trifluoroethyl methacrylate

[0215] a1-2: 2-(perfluorohexyl)ethyl methacrylate

[0216] a1-3: 1,1,1,3,3,3-hexafluoroisopropyl methacrylate

[0217] Radical polymerizable monomer (a1') used for comparative example:

[0218] a1′-4: methyl methacrylate

[0219] Radical polymerizable monomer (a2) containing alkoxysilane:

[0220] a2-1: 3-(trimethoxysilyl)propyl methacrylate

[0221] Solvent (a3) ​​used in the polymerization reaction:

[0222] a3-1: Propylene glycol monomethyl ether (hereinafter abbreviated as "PGME")

[0223] Polymerization initiator (a4):

[0224] a4-1: 2,2'-azobis(2,...

Synthetic example 1

[0269] [Synthesis Example 1] Synthesis of Fluorinated Copolymer (A-1)

[0270] Into a 500 mL 4-neck flask equipped with a thermometer, a stirrer, a raw material inlet, and a nitrogen inlet, methacrylic acid-2,2,2-methacrylic acid-2,2,2- Trifluoroethyl ester (a1-1), 3-(trimethoxysilyl)propyl methacrylate (a2-1) as a radically polymerizable monomer (a2) containing alkoxysilane, as a polymer PGME (a3-1) as the solvent (a3) ​​used in the reaction, and 2,2'-azobis(2,4-dimethylvaleronitrile) (a4-1) as the polymerization initiator (a4) , and polymerized by heating at a polymerization temperature of 90° C. for 4 hours.

[0271] a1: a1-1 (90.00g)

[0272] a2: a2-1 (10.00g)

[0273] a3: a3-1 (150.00g)

[0274] a4: a4-1 (5.00g)

[0275] The reaction liquid was cooled to room temperature to obtain a 40% by weight solution of the fluorinated copolymer (A-1). A portion of the solution was sampled and analyzed by GPC to determine the weight average molecular weight. As a result, the w...

Synthetic example 2

[0276] [Synthesis Example 2] Synthesis of Fluorinated Copolymer (A-2)

[0277] In the same manner as in Synthesis Example 1, the following components were charged and polymerized by the following weights.

[0278] a1: a1-1 (80.00g)

[0279] a2: a2-1 (20.00g)

[0280] a3: a3-1 (150.OO g)

[0281] a4: a4-1 (5.00g)

[0282] The same treatment as in Synthesis Example 1 was performed, and the weight average molecular weight determined by GPC analysis of a 40% by weight solution of the obtained fluorinated copolymer (A-2) was 5,500.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a thermosetting composition, a lamination body, a substrate, film, a display device, and a window material. The thermosetting composition which can manufacture the two-layer lamination body through one-step film formation is provided, and the thermosetting composition is used to obtain the lamination body whose haze value is low. The thermosetting composition is characterized by comprising fluorine-containing copolymer (A),a carboxyl compound (B) containing aromatic nucleus, a cyclic ether compound (C) containing aromatic nucleus, and a solvent (D), the fluorine-containing copolymer (A) is obtained by polymerizing fluorine-containing free radical polymerizcable monomer (a1) and free radical polymerizcable monomer (a2) containing alkoxy silane, and the composition contains each ingredient by specific quantity.

Description

technical field [0001] The present invention relates to a cured film obtained by forming a thermosetting composition and a film. This cured film is a laminate having two layers formed by one film formation, and this laminate can be used as an antireflection substrate or an antireflection film, and can be used as various display devices. and anti-reflection films used in window materials. Background technique [0002] Now, with the development of multimedia, various developments occur in various display devices. In addition, in various display devices, especially in display devices used outdoors mainly in portable display devices, it is increasingly important to improve the visibility. Watch, this matter goes straight to a technical subject. [0003] Moreover, in various window materials, especially in window materials used under lighting and outdoors, centering on display window materials such as shops and vending machines, it is possible to reduce the reflection of light...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D179/08C09D133/16C08F220/22C08F230/08C08G73/16
CPCG02B1/11C08F230/08C08G73/16C08J5/18C08L33/16C08L43/04C08L79/08B32B27/308C08F220/24C08F220/325C08F220/1807C08F222/402
Inventor 堀田佑策
Owner JNC CORP