A kind of cold mix epoxy asphalt material and preparation method thereof

A technology of epoxy asphalt materials and cold-mixed epoxy asphalt, which is applied in building insulation materials, building components, buildings, etc., can solve the problems of harmful asphalt smoke, physical and environmental impact, and difficult transportation, and achieve excellent anti-corrosion Effects of rutting performance, improved compatibility, and improved overall performance

Active Publication Date: 2019-08-30
HUBEI UNIV +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, the epoxy asphalt aggregate that has been mixed must be transported from the mixing station to the construction site under the condition of heat preservation. Transportation is difficult. On the other hand, during the heating process of epoxy asphalt, asphalt fumes harmful to human body will be produced, which will have a great impact on the body of the constructor and the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cold mix epoxy asphalt material and preparation method thereof
  • A kind of cold mix epoxy asphalt material and preparation method thereof
  • A kind of cold mix epoxy asphalt material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0046] The present invention provides a kind of preparation method of a kind of cold mix epoxy asphalt material described in above-mentioned technical scheme, comprises the following steps:

[0047] a) Add asphalt, asphalt diluent, epoxy asphalt compatibilizer, and epoxy asphalt curing agent into a common reaction kettle and mix to obtain part A of epoxy asphalt material;

[0048] b) Add epoxy resin and epoxy diluent together into an ordinary reaction kettle and stir and mix to obtain part B of epoxy asphalt material;

[0049] c) Mix part A of the epoxy asphalt material obtained in step a) with part B of the epoxy asphalt material obtained in step b) to obtain an epoxy asphalt material, the weight ratio of the part A to the part B For (0.5~5): 1;

[0050] The step a) and the step b) are in no sequence.

[0051] According to the present invention, the parts A and B are the same as those described above, and will not be repeated here.

[0052] In the present invention, some s...

Embodiment 1

[0064] Accurately weigh 30g of asphalt (Shell asphalt No. 70, the same below), 10g of epoxy asphalt thinner styrene (purchased from Tianjin Bodi Chemical Co., Ltd., the same below), 17g of epoxy asphalt compatibilizer epoxy hard Octyl acetate (purchased from Wuhan Jinnuo Chemical Co., Ltd., the same below), 10g of epoxy curing agent polyamide 650 (purchased from Shanghai Resin Factory Co., Ltd., the same below), were added to a common reaction kettle at 80°C and stirred for 60 minutes, Obtain part A of the epoxy asphalt material; weigh 8g of epoxy resin diluent 632 (purchased from Yantai Yusheng Chemical Co., Ltd.), 20g of epoxy resin (brand E-51, purchased from Sinopec Baling Petrochemical Co., Ltd. Company, the same below), added to the reaction kettle at 80°C and stirred for 45 minutes to obtain part B of the epoxy asphalt material; After 20 minutes, after mixing evenly, cool the obtained mixed material to room temperature to obtain the epoxy asphalt material.

[0065] The p...

Embodiment 2

[0068] Accurately weigh 30g of asphalt, 12g of asphalt diluent styrene, 15g of epoxy asphalt compatibilizer epoxy octyl stearate, 12g of epoxy curing agent polyamide 650, and add them to an ordinary reaction kettle at 80°C and stir for 60min to obtain ring Part A of the epoxy asphalt material; Weigh 8g of epoxy resin diluent 632 and 20g of epoxy resin, add it to a reaction kettle at 80°C and stir for 45min to obtain part B of the epoxy asphalt material; then mix the A part of the epoxy asphalt material Part B and part B of the epoxy asphalt material were added to a normal temperature reactor and stirred for 20 minutes, and after mixing evenly, the resulting mixture was cooled to room temperature to obtain the epoxy asphalt material.

[0069] The performance of the epoxy asphalt material obtained in Example 2 was tested, and the test results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention provides a cold mixing epoxy asphalt material and a preparation method. The cold mixing epoxy asphalt material comprises a part A and a part B; the part A comprises the following components by weight: 100 parts of asphalt, 5-50 parts of epoxy asphalt diluents, 10-50 parts of epoxy asphalt compatibilizer and 5-50 parts of epoxy asphalt curing agent; the part B comprises the following components by weight: 40-100 parts of epoxy resin and 5-50 parts of epoxy resin diluents, wherein the weight ratio of the part A to part B is 0.5-5: 1. In the invention, the asphalt diluent and the epoxy diluent provide better construction fluidity to the epoxy asphalt material under room temperature, and easily penetrate into the pavement cracks for repairing; and can be stirred under normal temperature for usage without heating and insulation transportation.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a cold-mix epoxy asphalt material capable of stirring, mixing and construction at room temperature and a preparation method thereof. Background technique [0002] The epoxy asphalt material disclosed in the prior art is a semi-fluid paste at room temperature. When paving and using, it must be heated under strict high temperature control to make its viscosity reach about 200cp, such as the mixing temperature of ChemCo epoxy asphalt in the United States. The mixing temperature of TAF epoxy asphalt in Japan is 121°C, and the mixing temperature is 180°C. Moreover, the epoxy asphalt aggregate that has been mixed must be transported from the mixing station to the construction site under the condition of heat preservation. Transportation is difficult. On the other hand, during the heating process of epoxy asphalt, asphalt fumes harmful to human body will be produced, which w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L63/00C08L63/02C08K5/1515C04B26/26
Inventor 周威徐逢来蒋涛王东怡田科曹志龙敖成鸿
Owner HUBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap