Communication station high hardness coating material

A technology for coating materials and communication sites, applied in the direction of coating, etc., can solve the problems of high hardness and easy cracking of materials, poor thermal insulation, etc., and achieve the effects of stable physical and chemical properties, excellent thermal insulation materials, and low thermal conductivity

Inactive Publication Date: 2014-09-24
QINGDAO XIANGHAI ELECTRONICS
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Various thermal insulation materials in the prior art, because various thermal insulation raw materials have their own shortcomings, thus affecting the improvement of their comprehensive performance, there are various defects, such as high hardness, easy cracking, poor thermal insulation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] A high-hardness coating material for communication sites, characterized in that it comprises the following parts by weight: 35-52 parts of plastic base material, 11-26 parts of glass fiber, 1-9 parts of brominated flame retardant, clam shell powder 3-8 parts, white clam shell powder 2-6 parts, aqueous dispersant 1-3 parts, eucalyptus wood chips 4-8 parts, cypress wood chips 3-8 parts, firs wood chips 2-6 parts, orange wood chips 1-6 parts parts, 9-13 parts of stearic acid, 30-50 parts of cement, 12-16 parts of acrylate, 3-5 parts of isoprene rubber, 9-11 parts of alcohol-soluble resin, and 10-18 parts of gypsum.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a communication station high hardness coating material, which is characterized by including the following substances by weight: 35-52 parts of a plastic base material, 11-26 parts of glass fiber, 1-9 parts of a brominated flame retardant, 3-8 parts of clam shell powder, 2-6 parts of Mactra veneriformis shell powder, 1-3 parts of a water-based dispersing agent, 4-8 parts of Eucalyptus sawdust, 3-8 parts of cypress sawdust, 2-6 parts of oaklet sawdust, 1-6 parts of orange tree sawdust, 9-13 parts of stearic acid, 30-50 parts of cement, 12-16 parts of acrylic ester, 3-5 parts of isoprene rubber, 9-11 parts of alcohol soluble resin, and 10-18 parts of gypsum. The material provided by the invention is an excellent thermal insulation material, has the advantages of low thermal conductivity coefficient, stable physical and chemical properties, no aging, high temperature resistance and no cracking, can be used as a coating, and also can be placed into a mould to be strickled, heated and baked into a sheet material.

Description

technical field [0001] The invention relates to a high-hardness coating material for communication stations. Background technique [0002] Most of the existing mobile base stations are set up in the open air. Since various devices in the mobile base station need to work under a certain temperature and humidity, and the temperature difference between the inside and outside of the base station is large, it is necessary to apply a thermal insulation material on the surface to prevent Reduce energy loss caused by heat exchange with the outside world. Various heat preservation materials in the prior art have their own shortcomings, which affect the improvement of their comprehensive performance, and have various defects, such as high hardness and easy cracking, and poor heat preservation. SUMMARY OF THE INVENTION [0003] The technical problem to be solved by the present invention is to provide a high-hardness coating material for a communication station. [0004] In order to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/02C09D7/12
Inventor 张昊亮
Owner QINGDAO XIANGHAI ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products