A technology for veneering panels and rock slices, applied in covering/lining, construction, building construction, etc., can solve problems such as being easily affected by the external environment, complicated construction procedures, and difficult quality control, achieving good stone imitation effects and overcoming high costs , Fast construction effect

Active Publication Date: 2016-11-23
广西启利新材料科技股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a method of using rock chips to prepare veneers, which overcomes the shortcomings of the traditional preparation methods of veneers, such as complex construction procedures, difficult quality control, and easy to be affected by the external environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Mix 40kg425# cement, 60kg80 mesh quartz sand, 3 kg latex powder, 0.4 kg hydroxypropyl methylcellulose, 0.1 kg wood fiber, and 26 kg water and mix evenly to obtain cement adhesive, which is ready for use;

[0026] (2) Glue a layer of glass fiber mesh on a layer of mortar cloth with cement bonding glue, and scrape off the cement bonding glue on the glass fiber mesh. The amount of cement bonding glue is 0.5kg / ㎡;

[0027] (3) Sprinkle colored rock flakes with matching colors on the cement adhesive glue on the glass fiber mesh surface that has been scraped;

[0028] (4) After the cement adhesive is cured, sand the colored rock flakes to make them smooth;

[0029] (5) Apply a layer of overlay resin, and after drying, it can be cut into finished products as required.

Embodiment 2

[0031] (1) Mix 50kg of 325# cement, 45kg of 100 mesh quartz sand, 8kg of VAE emulsion, 1kg of hydroxypropyl methylcellulose, 0.5kg of 0.5cmPP fiber, and 28kg of water, and mix evenly to obtain a cement adhesive for use;

[0032] (2) Glue a layer of glass fiber mesh on a layer of glass fiber mesh sheet with cement bonding glue, and scrape off the cement bonding glue on the glass fiber mesh. The amount of cement bonding glue is 1kg / ㎡;

[0033] (3) Sprinkle colored rock flakes with matching colors on the cement adhesive glue on the glass fiber mesh surface that has been scraped;

[0034] (4) After the cement adhesive is cured, sand the colored rock flakes to make them smooth;

[0035] (5) Apply two layers of overlay resin, and after drying, it can be cut into finished products as required.

Embodiment 3

[0037] (1) Mix and stir 50kg425# cement, 50kg150 mesh quartz sand, 15kg latex powder, 0.8kg hydroxypropyl methylcellulose, 0.3kg1cmPP fiber, and 30kg water evenly to obtain cement adhesive, which is ready for use;

[0038] (2) Glue two layers of glass fiber mesh with cement bonding glue on a layer of mortar cloth, and scrape off the cement bonding glue on the glass fiber mesh. The amount of cement bonding glue is 2kg / ㎡;

[0039] (3) Sprinkle colored rock flakes with matching colors on the cement adhesive glue on the glass fiber mesh surface that has been scraped;

[0040] (4) After the cement adhesive is cured, sand the colored rock flakes to make them smooth;

[0041] (5) Apply two layers of overlay resin, and after drying, it can be cut into finished products as required.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing veneers by using rock slices. Rock flakes are widely used in building materials. The use of rock flakes as decorative materials is mainly to incorporate rock flakes into paint, but this method is costly, difficult to control quality, and complicated construction procedures. In the present invention, the cement bonding glue is firstly prepared for use; one layer or two layers of glass fiber mesh are glued on a layer of mortar cloth or a glass fiber mesh thin plate with cement bonding glue, and scraped off. The amount of cement bonding glue is 0.5 to 2.5 kg / ㎡; Sprinkle with colored rock flakes with matching colors; after the cement adhesive is cured, sand the colored rock flakes to make them smooth; apply one or two coats of overcoat resin and dry. The present invention directly manufactures the rock slice veneer, and only needs to operate the veneer during construction. The invention has the advantages of smooth surface, strong crack resistance, good stone imitation effect, simple pasting, fast construction, low cost, and is not affected by cloudy, light rainy weather and low temperature weather above -5°C.

Description

technical field [0001] The invention relates to a method for preparing veneers by using rock slices, which belongs to the field of new building materials. Background technique [0002] Rock slices have the advantages of color retention, water resistance, crack resistance, weather resistance, and strong simulation, and are widely used in building materials. At present, there are mainly two kinds of colored rock flakes as building decoration materials in the market: one is to mix colored rock flakes into the stone paint, but the cost of materials for this method is as high as 52 yuan / square meter, and the construction labor cost is 20 yuan / square meter. The material cost is 32 yuan / square meter; the second is to mix colored rock flakes and acrylic emulsion into rock flake paint, and the cost of materials for this method is also as high as 52 yuan / square meter. The biggest defects of these two imitation stone building decoration materials are: the process of on-site spraying c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/09
Inventor 王新巢启钟勤刘齐程峰周绍文
Owner 广西启利新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap