Rigid reinforced automobile bottom protection plate and production method thereof

A technology of rigidity enhancement and production method, applied in the direction of vehicle components, superstructure, superstructure sub-assembly, etc., can solve the problems of poor rigidity and poor load-bearing capacity, and achieve the effect of reducing weight, high rigidity and high strength

Active Publication Date: 2014-11-19
WUXI GISSING AUTO PARTS CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the disadvantage of poor rigidity and poor load-bearing capacity of the car bottom guard plate in the prior art, and to provide a rigidity-enhanced car bottom guard plate with good rigidity and simple method steps and its production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Example 1: Production of Dongfeng Yueda Kia car K4 bottom guard plate, with a five-layer structure, from top to bottom: polypropylene resin layer, glass fiber mat layer, polypropylene resin layer, glass fiber mat layer and polypropylene resin layer, specifications and sizes For: 1320×580mm.

[0013] The production method of the rigidity-enhanced automobile bottom guard plate comprises the following steps:

[0014] (1) Put the polypropylene resin layer and the glass fiber felt layer of the base material of the automobile base cloth protection plate into the oven for heating between the upper oven heating plate and the lower oven heating plate. When heating, the temperature of the upper oven heating plate is controlled at 380°C , the temperature of the heating plate of the lower oven is controlled at 410°C, and the heating time is controlled at 420s;

[0015] (2) Put the heated base material of the car bottom guard plate into the closed forming mold, and place and posit...

Embodiment 2

[0019] Example 2: Production of Fiat car K4L car bottom guard plate, with a five-layer structure, from top to bottom: polypropylene resin layer, glass fiber mat layer, polypropylene resin layer, glass fiber mat layer and polypropylene resin layer, the specifications are: 1180×520mm.

[0020] The production method of the rigidity-enhanced automobile bottom guard plate comprises the following steps:

[0021] (1) Put the polypropylene resin layer and the glass fiber felt layer of the base material of the automobile base cloth protection plate into the oven for heating between the upper oven heating plate and the lower oven heating plate. When heating, the temperature of the upper oven heating plate is controlled at 350 ℃, the temperature of the heating plate of the lower oven is controlled at 380 ℃, and the heating time is controlled at 360s;

[0022] (2) Put the heated base material of the car bottom guard plate into the closed forming mold, and complete the positioning and l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a rigid reinforced automobile bottom protection plate and a production method thereof. The rigid reinforced automobile bottom protection plate is of a structure with five layers, namely, the polypropylene resin layer, the glass fiber mat layer, the polypropylene resin layer, the glass fiber mat layer and the polypropylene resin layer from top to bottom in sequence. The production method comprises the steps of heating the polypropylene resin layers and the glass fiber mat layers in a drying oven, laying and locating the polypropylene resin layers and the glass fiber mat layers in a closed forming mold, starting a forming press and carrying out pressing formation. The production steps of the rigid reinforced automobile bottom protection plate are simple, the produced automobile bottom protection plate is light in weight and high in strength, the weight of finished automobile equipment is greatly lowered, the rigidity of the automobile bottom protection plate is high, the automobile bottom protection plate will not be broken or droop, and the whole production process is free of hazardous substances and is friendly to environment.

Description

technical field [0001] The invention relates to a production method of a rigidity-enhanced automobile bottom guard plate, which belongs to the technical field of production of automobile exterior trim parts. Background technique [0002] The car bottom guard plate assembly is generally installed under the car chassis and directly faces the road surface; it is mainly used to protect the car chassis and related accessories during driving, and prevent the sewage, stone splashing on the road surface, and uneven road surface from dragging the bottom of the car chassis and other related problems. The influence of accessories; and through its good state stability and weather aging resistance, it can effectively protect and reduce the corrosion and impact of the chassis and related accessories, and play a role in blocking the influence of climate and geographical environment. In the era of increasingly pursuing high safety, environmental protection, energy saving, lightweight, and p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B62D25/20
Inventor 惠柯杰
Owner WUXI GISSING AUTO PARTS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap