Candy packaging bag and preparation method thereof

A technology for packaging bags and candies, which is applied in the field of candy packaging bags and its preparation, can solve the problems of low light transmittance, tensile strength, elongation at break, and low tear strength of candy packaging bags, and achieve excellent anti-fog effects and long-lasting The effect of excellent shrinkage

Inactive Publication Date: 2014-12-10
周佳瑜
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the above technical problems, the present application provides a candy packaging bag and its preparation method, which solves the technical problems of the existing candy packaging bags such as low light transmittance, tensile strength, elongation at break and low tear strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Weigh 100 parts of LDPE; 25 parts of DOP; 10 parts of PP; 10 parts of 4,5-epoxy tetrahydrophthalate di-isooctyl; 5 parts of PS; 0.1 part of zinc stearate; ; 1 part of calcium stearate; 5 parts of tricresyl phosphate; 6 parts of silicon dioxide; 20 parts of polyisobutylene; 5 parts of CPE; 5 parts of triphenyl phosphite; 15 parts of MBS; share.

[0022] Put LDPE, DOP, PP, 4,5-diisooctyl 4,5-epoxytetrahydrophthalate and PS into the reactor, heat to 80°C, stir for 10 minutes, then add the remaining raw materials, heat up to 110°C, stir for 20 minutes, cool to 40°C.

[0023] Put the mixed material into the extruder for extrusion, the barrel temperature is 150°C, 160°C, 170°C, 180°C, 185°C, 190°C and 200°C, the head temperature is 185°C, 180°C, and the screw speed is 70r / Min, the temperature of the connecting body is 190°C, the longitudinal stretching ratio is 3 times, and the stretching temperature is 70°C. After stretching, it can be rolled up, inspected and put into st...

Embodiment 2

[0026] Weigh 100 parts of LDPE; 35 parts of DOP; 30 parts of PP; 20 parts of 4,5-epoxy tetrahydrophthalate di-isooctyl; 25 parts of PS; 0.5 parts of zinc stearate; 35 parts of rosin resin ; 5 parts of calcium stearate; 15 parts of tricresyl phosphate; 10 parts of silicon dioxide; 40 parts of polyisobutylene; 25 parts of CPE; 15 parts of triphenyl phosphite; 25 parts of MBS; share.

[0027] Put LDPE, DOP, PP, 4,5-diisooctyl 4,5-epoxytetrahydrophthalate and PS into the reactor, heat to 100°C, stir for 20 minutes, then add the remaining raw materials, heat up to 130°C, stir for 50 minutes, cool to 50°C.

[0028] Put the mixed material into the extruder for extrusion, the barrel temperature is 150°C, 160°C, 170°C, 180°C, 185°C, 190°C and 200°C, the head temperature is 185°C, 180°C, the screw speed is 80r / min, the connecting body temperature is 190°C, the longitudinal stretching ratio is 5 times, and the stretching temperature is 80°C. After stretching, it can be rolled up, insp...

Embodiment 3

[0031] Weigh 100 parts of LDPE according to the ratio of parts by weight; 27 parts of DOP; 15 parts of PP; 2 parts of calcium fatty acid; 8 parts of tricresyl phosphate; 7 parts of silicon dioxide; 25 parts of polyisobutylene; 10 parts of CPE; 6 parts of triphenyl phosphite; 18 parts of MBS;

[0032] Put LDPE, DOP, PP, 4,5-diisooctyl 4,5-epoxytetrahydrophthalate and PS into the reactor, heat to 85°C, stir for 12min, then add the remaining raw materials, heat up to 115°C, stir for 30min, cool to 43°C.

[0033] Put the mixed material into the extruder for extrusion, the barrel temperature is 150°C, 160°C, 170°C, 180°C, 185°C, 190°C and 200°C, the head temperature is 185°C, 180°C, and the screw speed is 72r / min, the temperature of the connecting body is 190°C, the longitudinal stretching ratio is 3 times, and the stretching temperature is 73°C. After stretching, it can be rolled up, inspected and put into storage.

[0034] The light transmittance of the product is 96%, the lon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a candy packaging bag and a preparation method thereof. The candy packaging bag is prepared by weighting the following components in parts by weight: LDPE (Low-Density Polyethylene), DOP (Dioctyl-Phthalate), PP (Propene Polymer), 4,5-epoxytetrahydroisooctyl phthalate, PS (Poly Styrene), zinc stearate, a thickening agent, calcium stearate, tricresyl phosphate, silicon oxide, a toughening agent, CPE (Chlorinated Polyethylene), triphenyl phosphite, MBS (Methyl Methacrylate) and epoxy soybean oil octyl ester, evenly mixing, extruding, granulating and then drawing, winding, inspecting and warehousing. The light transmittance of the product is 95-98%, the longitudinal tensile strength is 45-55MPa, the transverse tensile strength is 20-30MPa, the longitudinal elongation at break is 450-550%, the transverse elongation at break is 850-950%, the longitudinal tear strength is 120-130N / mm and the transverse tear strength is 140-150N / mm.

Description

technical field [0001] The application belongs to the field of packaging bag preparation technology, and in particular relates to a candy packaging bag and a preparation method thereof. Background technique [0002] Packaging bags refer to bags used to pack various supplies, making the goods convenient to transport and store during the production and distribution process. Widely used in daily life and industrial production. The development of packaging bags has gone through four distinct stages: the original packaging bag stage, the large packaging bag stage, the small packaging bag stage, and now gradually entering a new stage of environmentally friendly (green) packaging bags. With the development of the commodity economy, the commodity nature of the packaging itself is becoming more and more obvious. It has become a special product that is no longer attached to commodity production, and a widely used product that all commodities cannot do without. With the rapid develop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L23/12C08L23/18C08L25/06C08L93/04C08L23/22C08K13/02C08K3/36C08K5/098C08K5/12C08K5/521C08K5/524B65D85/60
CPCC08L23/06B65D85/60C08K2201/014C08L2205/025C08L2205/035C08L2207/066
Inventor 周佳瑜
Owner 周佳瑜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com