High-gloss, high-fluidity and high-content glass fiber reinforced nylon material and preparation method thereof
A technology with high content of glass fiber and high fluidity, which is applied in the field of polymer materials, can solve the problems of nylon infiltration, serious floating fibers on the surface, and difficulty in effectively improving the overall performance, and achieve the effect of high fluidity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] Example 1
[0025] First dry the branched nylon 6 resin at 80°C to control the moisture content below 0.1%; weigh 43 kg of the branched nylon 6 resin, 0.5 kg each of the antioxidants Irganox 168 and Irganox 1098, and 1 kg of the bright lubricant, and mix at room temperature After uniformity, add it to the twin-screw extruder; take 55kg of glass fiber and add it from the glass fiber port in the fifth zone, cool, dry, and pellet after extrusion to prepare high gloss, high fluidity, and high content glass fiber reinforced nylon material.
[0026] The processing conditions of the twin-screw extruder are: zone one temperature 245℃, zone two temperature 250℃, zone three temperature 255℃, zone four temperature 260℃, zone five temperature 265℃, zone six temperature 265℃, zone seven temperature 265 ℃, the temperature in the eight zones is 270℃, the temperature in the nine zones is 275℃, and the main engine rotates at 250 rpm.
Example Embodiment
[0027] Example 2
[0028] First dry the branched nylon 6 resin at 80°C to control the moisture content below 0.1%; weigh 37.7 kg of the branched nylon 6 resin, 0.4 kg of the antioxidants Irganox 168 and Irganox 1098, 1.5 kg of the bright lubricant, room temperature After mixing uniformly, add to the twin-screw extruder; take 60kg of glass fiber and add it from the glass fiber port of the fifth zone, cool, dry, and pellet after extrusion to prepare high gloss, high fluidity, and high content glass fiber reinforced nylon material.
[0029] The processing conditions of the twin-screw extruder are: zone one temperature 255℃, zone two temperature 260℃, zone three temperature 265℃, zone four temperature 270℃, zone five temperature 275℃, zone six temperature 275℃, zone seven temperature 275 ℃, the temperature in the eight zones is 280℃, the temperature in the nine zones is 285℃, and the main engine rotates at 350 rpm.
Example Embodiment
[0030] Example 3
[0031] First dry the branched nylon 6 resin at 80°C to control the moisture content below 0.1%; weigh 32.5 kg of the branched nylon 6 resin, 0.25 kg each of the antioxidants Irganox 168 and Irganox 1098, and 2 kg of the bright lubricant, at room temperature After mixing uniformly, add it into the twin-screw extruder; take 65kg of glass fiber and add it from the glass fiber port of the fifth zone, cool, dry, and pellet after extrusion to prepare high gloss, high fluidity, and high content glass fiber reinforced nylon material.
[0032] The processing conditions of the twin-screw extruder are: zone one temperature 250℃, zone two temperature 255℃, zone three temperature 260℃, zone four temperature 265℃, zone five temperature 270℃, zone six temperature 270℃, zone seven temperature 270 ℃, the temperature in the eight zones is 270℃, the temperature in the nine zones is 280℃, and the main engine rotates at 250 rpm.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap