Moisture-retaining paint

A technology for coatings and film-forming aids, which is applied in the field of materials to achieve the effects of improving performance, reducing the time of health preservation, and improving moisturizing performance.

Inactive Publication Date: 2014-12-17
徐玲玲
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are no reports of such products at home and abroad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A moisturizing paint, comprising Xanthium powder 12g, film-forming aid 14g, dibutyl benzoate 7g, pentaerythritol 13g, tetrafluoroethylene resin 6g, resin 7g, fluorocarbon polymer 6g, graphene 13g and graphite 7g.

[0012] The coalescent is methyl 2-hydroxy-3-methylbutyrate.

Embodiment 2

[0014] A moisturizing paint, comprising Xanthium powder 16g, film-forming aid 21g, dibutyl benzoate 18g, pentaerythritol 18g, tetrafluoroethylene resin 8g, resin 11g, fluorocarbon polymer 10g, graphene 23g and graphite 9g.

[0015] The coalescent is methyl 2-hydroxy-3-methylbutyrate.

Embodiment 3

[0017] A moisture-retaining paint, comprising cocklebur powder 15g, film-forming aid 17g, dibutyl benzoate 11g, pentaerythritol 15g, tetrafluoroethylene resin 7g, resin 10g, fluorocarbon polymer 8g, graphene 15g and graphite 8g.

[0018] The coalescent is methyl 2-hydroxy-3-methylbutyrate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Moisture-retaining paint comprises 12-16 g of cocklebur powder, 14-21 g of a film-forming auxiliary agent, 7-18 g of dibutyl benzoate, 13-18 g of pentaerythritol, 6-8 g of tetrafluoroethylene resin, 7-11 g of resin, 6-10 g of fluorine carbon polymer, 13-23 g of graphene and 7-9 g of graphite. The film-forming auxiliary agent is methyl 2-hydroxyl-3-methylbutanoate. When being used to coat the surface of cement being cured, the paint is capable of improving the moisture retaining performance and reducing curing time, and also becomes a part of cement and helps to improve performances of cement.

Description

technical field [0001] The invention belongs to the field of materials, in particular to a moisturizing paint. Background technique [0002] During the curing process of cement, it is necessary to keep the surface of the cement moist. At present, the covering is used for moisturizing, and the moisturizing effect is not good. Therefore, a moisturizing coating is provided, which can be applied on the surface of the cement and can improve the performance of the cement after drying. . [0003] There is no report of this type of product both at home and abroad at present. Contents of the invention [0004] The purpose of the present invention is to provide a moisture-retaining coating, which can improve the moisture-retention performance and reduce the curing time when applied on the surface of the curing cement, and at the same time, it will become a part of the cement to improve the performance of the cement. [0005] The technical solutions adopted are: [0006] A moistur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D127/18C09D127/12C09D7/12
Inventor 徐玲玲
Owner 徐玲玲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com