Recyclable coating material and preparation method thereof

A film covering and corn starch technology, which is applied in the field of recyclable film covering materials and their preparation, can solve the problems of difficult degradation of film covering materials, achieve the effects of protecting the environment, realizing recycling, and saving resources

Inactive Publication Date: 2015-01-14
ANHUI ZHONGCAI PRINTING
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a recyclable coating material and its preparation method for the defects of the above-mentioned prior art. The coating material can solve the problem that the coating material is difficult to degrade in the prior art, and realize The recycling of membranes protects the environment and saves resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A method for preparing a recyclable film covering material, the specific steps are as follows: first, 100 parts of cornstarch is mixed with 70°C-85°C water to make a paste, and then mixed with 8 parts of carboxyethyl cellulose and 3 parts of alkyd resin 12 parts of low-density polyethylene resin, 3 parts of glycerin, 4 parts of calcium stearate, 1 part of liquid paraffin, 1.0 part of calcium propionate, 1.2 parts of titanium dioxide, 0.5 parts of reinforcing modifier, 0.1 part of stabilizer , and 0.2 parts of the initiator were added to the high-speed mixer and mixed for 20 minutes to mix evenly, then put into the twin-screw extruder, extruded and granulated through the head die, the extrusion granulation temperature was 180°C, and then extruded with a single screw The blow molding machine blows into the film material at 180°C.

[0018] The reinforcing modifier in the recyclable coating material is selected from nylon fiber, the stabilizer is selected from stabilizer 73...

Embodiment 2

[0020] A method for preparing a recyclable coating material, the specific steps are as follows: first, 100 parts of cornstarch is mixed with water at 70°C-85°C to make a paste, and then mixed with 16 parts of carboxyethyl cellulose and 8 parts of alkyd resin 20 parts of low-density polyethylene resin, 8 parts of glycerin, 10 parts of calcium stearate, 5 parts of liquid paraffin, 1.6 parts of calcium propionate, 1.8 parts of titanium dioxide, 0.8 parts of reinforcing modifier, and 0.5 parts of stabilizer , and 0.6 parts of the initiator were added to the high-speed mixer and mixed for 30 minutes to mix evenly, then put into the twin-screw extruder, extruded and granulated through the head die, the extrusion granulation temperature was 210°C, and then extruded with a single screw The blow molding machine blows into the film material at 195°C.

[0021] The reinforcing modifier in the recyclable coating material is selected from nylon fiber, the stabilizer is selected from stabili...

Embodiment 3

[0023] A method for preparing a recyclable coating material, the specific steps are as follows: first, 100 parts of corn starch is mixed with 70°C-85°C water to make a paste, and then mixed with 12 parts of carboxyethyl cellulose and 5 parts of alkyd resin 16 parts of low-density polyethylene resin, 6 parts of glycerol, 6 parts of calcium stearate, 3 parts of liquid paraffin, 0.8 parts of calcium propionate, 1.6 parts of titanium dioxide, 0.6 parts of reinforcing modifier, 0.3 parts of stabilizer , and 0.4 parts of the initiator were added to the high-speed mixer and mixed for 25 minutes to mix evenly, then put into the twin-screw extruder, extruded and granulated through the head die, the extrusion granulation temperature was 200 ° C, and then extruded with a single screw The blow molding machine blows into the film material at 185°C.

[0024] The reinforcing modifier in the recyclable coating material is selected from nylon fiber, the stabilizer is selected from stabilizer 7...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a coating material and a preparation method thereof, particularly a recyclable coating material and a preparation method thereof. The coating material is composed of the following components in parts by weight: 100 parts of corn starch, 8-16 parts of carboxyethyl cellulose, 3-8 parts of alkyd resin, 12-20 parts of low density polyethylene resin, 3-8 parts of glycerol, 4-10 parts of calcium stearate, 1-5 parts of liquid paraffin, 1.0-1.6 parts of calcium propionate, 1.2-1.8 parts of titanium white, 0.5-0.8 part of reinforced modifier, 0.1-0.5 part of stabilizer and 0.2-0.6 part of initiator. The coating material solves the problem of low degradability of the coating material in the prior art, implements recycling, protects the environment and saves the resources.

Description

technical field [0001] The invention relates to a coating material and a preparation method thereof, in particular to a recyclable coating material and a preparation method thereof. Background technique [0002] Laminating, also known as "overplastic", "mounting glue", "film sticking", etc., refers to the use of transparent plastic film to apply heat and pressure to the surface of printed matter to protect and increase gloss. Laminating film has been widely used for surface binding and protection of book covers, picture albums, commemorative albums, postcards, product brochures, calendars and maps. At present, common film-coated packaging products include cartons, cartons, handbags, fertilizer bags, seed bags, self-adhesive labels, etc. [0003] Lamination is to put a layer of film on the outer packaging of the product to make the appearance of the product more beautiful, shiny, and dirt-resistant. There are many products that need this process, such as the outer packaging ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L3/02C08L1/28C08L67/08C08L23/06C08L91/06C08K13/02C08K5/053C08K5/098C08K3/22B29C55/28
Inventor 付云
Owner ANHUI ZHONGCAI PRINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap