Wear-resistant aqueous aluminum pigment and preparation method thereof

An aluminum pigment, wear-resistant technology, applied in inorganic pigment treatment, chemical instruments and methods, fibrous fillers, etc., can solve the problems of poor dispersion and poor stability of metal pigments, and achieve easy storage, good weather resistance, and practicality. strong effect

Active Publication Date: 2015-01-14
HEFEI SUNRISE PIGMENTS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are also some problems with water-based metallic pigments, s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A wear-resistant water-based aluminum pigment prepared from the following components by weight (kg):

[0022] Flake aluminum powder 50, tetraethyl orthosilicate 9, silane coupling agent A-151 0.2, zircon powder 1.5, polytetrafluoroethylene micropowder 1.5, water-soluble lanolin 0.8, cellulose acetate butyrate 0.8, silicone acrylic emulsion 0.8, glyceryl triisocaprylate 0.8, polyethylene glycol 4, sodium lauryl sulfate 0.15, itaconic acid 0.08, compound additive 0.8;

[0023] Among them, the compound additives are made of raw materials with the following weight (kg):

[0024] Sisal residue 55, attapulgite 35, citric acid 6, sodium citrate 6, tetradecyltrimethylammonium chloride 1.5, sodium dodecylbenzenesulfonate 3, water 35;

[0025] The preparation method of compound auxiliary agent:

[0026] Dry the sisal residue at 80°C overnight and crush it, add citric acid, sodium citrate, tetradecyltrimethylammonium chloride, sodium dodecylbenzenesulfonate and water and stir fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wear-resistant aqueous aluminum pigment which is prepared from the following raw materials in parts by weight: 40-60 parts of laminar aluminum powder, 8-10 parts of tetraethoxysilane, 0.1-0.3 part of a silane coupling agent A-151, 1-2 parts of zircon power, 1-2 parts of polytetrafluoroethylene micropowder, 0.5-1 part of water soluble wool fat, 0.5-1 part of cellulose acetate butyrate, 0.5-1 part of a silicone acrylic emulsion, 0.5-1 part of glyceryl trithylhexanoate, 3-5 parts of polyethylene glycol, 0.1-0.2 part of lauryl sodium sulfate, 0.05-0.1 part of itaconic acid and 0.5-1 part of compound auxiliaries. The aluminum pigment disclosed by the invention has good wear resistance, and is long in service life, high in dispersibility in aqueous media, stable in property and suitable for aqueous systems.

Description

technical field [0001] The invention relates to the field of metal pigments, in particular to a wear-resistant water-based aluminum pigment and a preparation method thereof. Background technique [0002] Nowadays, with the development of industrialization, the global environment is deteriorating, and environmental protection issues are getting more and more attention. Traditional metallic pigments have bright metallic luster and high hiding power, and have the advantages of high decoration and high protection. They are widely used and have a huge market. However, traditional solvent-based metallic pigments use a large amount of organic solvents in the application, which are discharged into the environment during the coating process, which is easy to cause pollution. Since most of the organic solvents of water-based metallic pigments are replaced by water, the pollution discharge during the coating process is greatly reduced. Therefore, the use of water-based metallic pigmen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D7/12C09C1/64C09C3/06C09C3/10
CPCC09C1/642C09C1/644C09C3/06C09C3/10C09D7/62
Inventor 董前年朱双单李国旺
Owner HEFEI SUNRISE PIGMENTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap