Paint vehicle with anticorrosion and antimould effects and preparation method thereof
An anti-corrosion, mildew-proof and paint technology, which is applied in the paint field, can solve problems such as short shelf life, poor wear resistance, poor anti-corrosion and mildew resistance, and achieve the effect of extending shelf life, prolonging service life, and ensuring health
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1:
[0020] A paint with anti-corrosion and anti-mildew effect, prepared from the following parts by weight: 180 parts of acrylic resin emulsion, 20 parts of nano-mixture, 15 parts of seaweed mud, 14 parts of talc, 10 parts of sepiolite, nano 9 parts of titanium dioxide, 6.3 parts of preservatives, 6.1 parts of surfactants, 4.6 parts of emulsified silicone oil, 4.2 parts of polyvinylpyrrolidone, 2.8 parts of film forming aids, 74 parts of deionized water, appropriate amount of heptane and appropriate amount of oleic acid.
[0021] A paint with anti-corrosion and anti-mildew effect, its preparation method includes the following steps:
[0022] a. Pretreatment of the nano-mixture: soak the nano-mixture in heptane with 5 times its mass, add 35% oleic acid in the volume of the nano-mixture, and ultrasonically disperse for 25 minutes to obtain the mixed component A, and then mix it Add the nano-mixture to component A, ultrasonically disperse for 50 minutes, place the dispe...
Example Embodiment
[0028] Example 2:
[0029] A paint with anti-corrosion and anti-mildew effect, prepared from the following parts by weight: 195 parts of acrylic resin emulsion, 18 parts of nano-mixture, 17 parts of seaweed mud, 12 parts of talc, 13 parts of sepiolite, nano 8 parts of titanium dioxide, 6.8 parts of preservatives, 5.4 parts of surfactants, 5.3 parts of emulsified silicone oil, 3.6 parts of polyvinylpyrrolidone, 3.4 parts of film forming aids, 70 parts of deionized water, appropriate amount of heptane and appropriate amount of oleic acid.
[0030] A paint with anti-corrosion and anti-mildew effect, its preparation method includes the following steps:
[0031] a. Pretreatment of nano-mixture: immerse the nano-mixture in heptane 6 times its mass, add 40% oleic acid in volume of the nano-mixture, and disperse it ultrasonically for 32 minutes to obtain mixed component A, and then mix it Add the nano-mixture to component A, disperse ultrasonically for 57 minutes, place the dispersion in a ...
Example Embodiment
[0037] Example 3:
[0038] A paint with anticorrosive and antifungal effects, prepared from the following parts by weight of raw materials: 206 parts of acrylic resin emulsion, 25 parts of nano-mixture, 19 parts of seaweed mud, 18 parts of talc, 14 parts of sepiolite, nano 12 parts of titanium dioxide, 7.3 parts of preservatives, 7.5 parts of surfactants, 5.9 parts of emulsified silicone oil, 5.3 parts of polyvinylpyrrolidone, 3.9 parts of film forming aids, 80 parts of deionized water, appropriate amount of heptane and appropriate amount of oleic acid.
[0039] A paint with anti-corrosion and anti-mildew effect, its preparation method includes the following steps:
[0040] a. Pretreatment of nano-mixture: immerse the nano-mixture in heptane 5-8 times its mass, add 44% oleic acid in the volume of the nano-mixture, and ultrasonically disperse for 37 minutes to obtain mixed component A, then Add the nano-mixture to the mixed component A, ultrasonically disperse for 65 minutes, place t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap