Glass-solder microwave-welded planar tempered vacuum glass edge-sealed by using bar frames
A vacuum glass and glass solder technology, applied in glass forming, glass remolding, glass production and other directions, can solve the problems of difficulty, unbearable for users, high production cost, improve the qualification rate and life, good heat insulation and sound insulation performance, the effect of eliminating the effect of flatness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0044] Example 1: see figure 1 , Tempered vacuum glass is composed of two pieces of tempered glass or semi-tempered glass, one of which is low-emissivity glass, and its production method is as follows: First, cut a flat glass and a piece of low-emission The glass is edged, chamfered, and film removed. After cleaning and drying, the tempered glass ink is used to make an edge banding frame on two pieces of glass by screen printing. The upper glass has an edge banding frame and the lower glass has an edge banding frame. Two edge seal frames, the size of the upper glass edge seal frame is between the two edge seal frames of the lower glass. After the upper and lower glass are combined, the edge seal frame of the upper glass can be embedded in the two Between the edge banding strips; secondly, send the two pieces of glass into the tempering furnace and carry out tempering treatment under the same conditions. Under the action of high temperature, the tempered glass ink and glass are...
Embodiment 2
[0045] Example 2: see figure 2 , the upper and lower glass of the double vacuum layer tempered vacuum glass is tempered glass or semi-tempered glass, and the middle glass is low-emissivity glass. The production method is as follows: first cut two pieces of flat glass of the required size according to the shape and size of the vacuum glass to be produced and A piece of low-emissivity glass is edged, chamfered, film removed, cleaned and dried, and the tempered glass ink is printed on the joint surface of the three pieces of glass to form an edge band frame by printing technology, and printed on the upper and lower glass at the same time The support, wherein the upper glass has one edge banding frame, the upper surface of the middle glass has two edge banding frames, the lower surface has one edge banding frame, the lower glass has two edge banding frames, and the upper edge banding frame The size is between the two lower edge-seal frames. After the upper, middle and lower glass...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com